硬度换算表 (以HRC硬度为基准) 1—前桥教育Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似Rockwell C(洛氏C)150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile(拉伸)150 kgfDiamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)Diamond(钻石)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)HRC 68 940 --- 85.6 --- 76.9 93.2 84.4 75.4 --- 68 67 900 --- 85.0 --- 76.1 92.9 83.6 74.2 --- 67 66 865 --- 84.5 --- 75.4 92.5 82.8 73.3 --- 66 65 832 739 83.9 --- 74.5 92.2 81.9 72.0 --- 65 64 800 722 83.4 --- 73.8 91.8 81.1 71.0 --- 6463 772 705 82.8 --- 73.0 91.4 80.1 69.9 --- 63 62 746 688 82.3 --- 72.2 91.1 79.3 68.8 --- 62 61 720 670 81.8 --- 71.5 90.7 78.4 67.7 --- 61 60 697 654 81.2 --- 70.7 90.2 77.5 66.6 --- 60 59 674 634 80.7 --- 69.9 89.8 76.6 65.5 --- 5958 653 615 80.1 --- 69.2 89.3 75.7 64.3 --- 58 57 633 595 79.6 --- 68.5 88.9 74.8 63.2 --- 57 56 613 577 79.0 --- 67.7 88.3 73.9 62.0 --- 56 55 595 560 78.5 --- 66.9 87.9 73.0 60.9 2075 55 54 577 543 78.0 --- 66.1 87.4 72.0 59.8 2015 5453 560 525 77.4 --- 65.4 86.9 71.2 58.6 1950 53 52 544 512 76.8 --- 64.6 86.4 70.2 57.4 1880 52 51 528 496 76.3 --- 63.8 85.9 69.4 56.1 1820 51 50 513 481 75.9 --- 63.1 85.5 68.5 55.0 1760 50 49 498 469 75.2 --- 62.1 85.0 67.6 53.8 1695 49硬度换算表 (以HRC硬度为基准) 2前桥教育Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似Rockwell C(洛氏C)150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile(拉伸)150 kgfDiamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)Diamond(钻石)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)HRC 48 484 455 74.7 --- 61.4 84.5 66.7 52.5 1635 48 47 471 443 74.1 --- 60.8 83.9 65.8 51.4 1580 47 46 458 432 73.6 --- 60.0 83.5 64.8 50.3 1530 46 45 446 421 73.1 --- 59.2 83.0 64.0 49.0 1480 45 44 434 409 72.5 --- 58.5 82.5 63.1 47.8 1435 4443 423 400 72.0 --- 57.7 82.0 62.2 46.7 1385 43 42 412 390 71.5 --- 56.9 81.5 61.3 45.5 1340 42 41 402 381 70.9 --- 56.2 80.9 60.4 44.3 1295 41 40 392 371 70.4 --- 55.4 80.4 59.5 43.1 1250 40 39 382 362 69.9 --- 54.6 79.9 58.6 41.9 1215 3938 372 353 69.4 --- 53.8 79.4 57.7 40.8 1180 38 37 363 344 68.9 --- 53.1 78.8 56.8 39.6 1160 37 36 354 336 68.4 (109.0) 52.3 78.3 55.9 38.4 1115 36 35 345 327 67.9 (108.5) 51,5 77.7 55.0 37.2 1080 35 34 336 319 67.4 (108.0) 50.8 77.2 54.2 36.1 1055 3433 327 311 66.8 (107.5) 50.0 76.6 53.3 34.9 1025 33 32 318 301 66.3 (107.0) 49.2 76.1 52.1 33.7 1000 32 31 310 294 65.8 (106.0) 48.4 75.6 51.3 32.5 980 31 30 302 286 65.3 (105.5) 47.7 75.0 50.4 31.3 950 30 29 294 279 64.7 (104.5) 47.0 74.5 49.5 30.1 930 29硬度换算表 (以HRC硬度为基准) 3Brinell (布氏)Rockwell Hardness(洛氏硬度)Rockwell Superficial Hardness(罗克韦尔表面硬度)Rockwell C (洛氏C)3000 kgfRockwell A(洛氏A)Rockwell B(洛氏B)Rockwell D(洛氏D)Approximate近似150 kgf Vickers10 mm 60 kgf100 kgf100 kgf15 kgf30 kgf45 kgf Tensile (拉伸)Diamond (钻石)Hardness(硬度)Ball(球)Diamond(钻石)1//16" ball(1//16球)Diamond(钻石)1/16" ball(1/16球)1/16" ball(1/16球)1/16" ball(1/16球)Strength(强度)HRC HV HB HRA HRB HRD HR15N HR30N HR45N ksi (MPa)28 286 271 64.3 (104.0) 46.1 73.9 48.6 28.9 910 28 27 279 264 63.8 (103.0) 45.2 73.3 47.7 27.8 880 27 26 272 258 63.3 (102.5) 44.6 72.8 46.8 26.7 860 26 25 266 253 62.8 (101.5) 43.8 72.2 45.9 25.5 840 25 24 260 247 62.4 (101.0) 43.1 71.6 45.0 24.3 825 2423 254 243 62.0 100.0 42.1 71.0 44.0 23.1 805 23 22 248 237 61.5 99.0 41.6 70.5 43.2 22.0 785 22 21 243 231 61.0 98.5 40.9 69.9 42.3 20.7 770 21 20 238 226 60.5 97.8 40.1 69.4 41.5 19.6 760 20 (18) 230 219 --- 96.7 --- --- --- --- 730 (18)(16) 222 212 --- 95.5 --- --- --- --- 705 (16) (14) 213 203 --- 93.9 --- --- --- --- 675 (14) (12) 204 194 --- 92.3 --- --- --- --- 650 (12) (10) 196 187 --- 90.7 --- --- --- --- 620 (10) (8) 188 179 --- 89.5 --- --- --- --- 600 (8)---(6) 180 171 --- 87.1 --- --- --- --- 580 (6) (4) 173 165 --- 85.5 --- --- --- --- 550 (4) (2) 166 158 --- 83.5 --- --- --- --- 530 (2) (0) 160 152 --- 81.7 --- --- --- --- 510 (0)42CrMo：材料采用调质工艺一般840淬火，620～680之间回火，硬度控制在261～304HB。
硬度知识介绍及硬度对照表硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度（HB）、洛氏硬度（HRA，HRB，HRC）、维氏硬度（HV），橡胶塑料邵氏硬度（HA,HD）等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度（HS）则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度（Hardness）的代号为H。
按硬度试验方法的不同，常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
HV-适用于显微镜分析。
维氏硬度（HV）以120kg以内的载荷和顶角为136的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值（HV）。
HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000VB（回弹速度）/V A（冲击速度）。
目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
布氏硬度（HB）一般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。
洛氏硬度（HRC）一般用于硬度较高的材料，如热处理后的硬度等等。
1、HB-布氏硬度:布氏硬度（HB）是以一定大小的试验载荷，将一定直径的淬硬钢球或硬质合金球压入被测金属表面，保持规定时间，然后卸荷，测量被测表面压痕直径。
常见材料硬度对照表硬度高于20HRC ，1HRC≈10HB，硬度低于20HRC，1HRC≈11.5HB。
备注：对于切削加工，基本可统一换算1HRC≈10HB（工件材料硬度有波动范围）金属材料的硬度硬度是指材料抵抗局部变形，特别是塑性变形、压痕或划痕的能力。
它是衡量材料软硬的指标。
按测试方法的不同，硬度分为三种类型。
①划痕硬度。
主要用于比较不同矿物的软硬程度，方法是选一根一端硬一端软的棒，将被测材料沿棒划过，根据出现划痕的位置确定被测材料的软硬。
定性地说，硬物体划出的划痕长，软物体划出的划痕短。
②压入硬度。
主要用于金属材料，方法是用一定的载荷将规定的压头压入被测材料，以材料表面局部塑性变形的大小比较被测材料的软硬。
由于压头、载荷以及载荷持续时间的不同，压入硬度有多种，主要是布氏硬度、洛氏硬度、维氏硬度和显微硬度等几种。
③回跳硬度。
主要用于金属材料，方法是使一特制的小锤从一定高度自由下落冲击被测材料的试样，并以试样在冲击过程中储存（继而释放）应变能的多少（通过小锤的回跳高度测定）确定材料的硬度。
金属材料最常见到的布氏硬度、洛氏硬度和维氏硬度属于压入硬度，硬度值表示材料表面抵抗另一物体压入时所引起的塑性变形的能力；回跳法（肖氏、里氏）测量硬度，硬度值代表金属弹性变形功能的大小。
布氏硬度 Brinell Hardness用直径D的淬火钢球或硬质合金球作压头，以相应的试验力F压入试件表面，经规定的保持时间后，卸除试验力，得到一直径为d的压痕。
用试验力除以压痕表面积，所得值即为布氏硬度值，符号用HBS或HBW表示。
HBS和HBW的区别是压头的不同。
HBS表示压头为淬硬钢球，用于测定布氏硬度值在450以下的材料，如软钢、灰铸铁和有色金属等。
HBW表示压头为硬质合金，用于测定布氏硬度值在650以下的材料。
同样的试块，当其它试验条件完全相同的情况下，两种试验结果不同，HBW值往往大于HBS值，而且并无定量的规律所循。
【知识】常用硬度对照表，一目了然！热处理书籍专业书店金相热处理综合实训 Mini Program今天的【知识】篇，我们一起看看各种硬度的换算：硬度是指材料抵抗局部变形，特别是塑性变形、压痕或划痕的能力。
它是衡量材料软硬的指标。
维氏硬度、布氏硬度、洛氏硬度对照表分享给你，快收藏起来吧！常用HV=HB=HRC硬度对照表抗拉强度（N/mm2）维氏硬度HV布氏硬度HB洛氏硬度HRC2558076.0—2708580.7—2859085.2—3059590.2—32010095.0—33510599.8—350110105—370115109—380120114—400125119—415130124—430135128—450140133—465145138—480150143—490155147—510160152—530165156—545170162—560175166—575180171—595185176—610190181—625195185—640200190—660205195—675210199—690215204—705220209—720225214—740230219—755235223—77024022820.3 78524523321.3 80025023822.2 82025524223.1 83526024724.0 85026525224.8 86527025725.6 88027526126.4 90028026627.1 91528527127.8 93029027628.5 95029528029.2 96530028529.8 99531029531.0 103032030432.2 106033031433.3 109534032334.4 112535033335.5 111536034236.6 119037035237.7 122038036138.8122038036138.8 125539037139.8 129040038040.8 132041039041.8 135042039942.7 138543040943.6 142044041844.5 145545042845.3 148546043746.1 152047044746.91555480(456)47.71595490(466)48.41630500(475)49.11665510(485)49.81700520(494)50.51740530(504)51.11775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.988066.490067.092067.594068.0本表数据来自德国标准DIN50150。
硬度HRC，HV，HB-硬度换算硬度換算公式:1.肖氏硬度(HS)=勃式硬度(BHN)/10+122.肖式硬度(HS)=洛式硬度(HRC)+153.勃式硬度(BHN)= 洛克式硬度(HV)4.洛式硬度(HRC)= 勃式硬度(BHN)/10-3硬度測定範圍:HS<100HB<500HRC<70HV<1300(80~88)HRA, (85~95)HRB, (20~70)HRC洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。
洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。
标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。
因此标尺B适用相对较软的材料，而标尺C适用较硬的材料。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
但各种材料的换算关系并不一致。
本站《硬度对照表》一文对钢的不同硬度值的换算给出了表格，请查阅。
硬度表示材料抵抗硬物体压入其表面的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。
2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间,硬度值与强度值之间具有近似的相应关系.因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高,硬度值也就越高。
三、硬度換算公式
1. 肖氏硬度(HS)=勃式硬度(BHN）/10+12
2。
肖式硬度（HS)=洛式硬度（HRC)+15
3。
勃式硬度(BHN）= 洛克式硬度(HV)
4. 洛式硬度(HRC)= 勃式硬度(BHN）/10-3
硬度測定範圍：
HS〈100
HB〈500
HRC<70
HV<1300。
常见硬度对照表常用HV=HB=HRC硬度对照表金属材料的硬度：硬度是指材料抵抗局部变形，特别是塑性变形、压痕或划痕的能力。
它是衡量材料硬度的一个指标。
根据测试方法的不同，硬度可分为三种。
①划痕硬度。
主要用于比较不同矿物的软硬程度，方法是选一根一端硬一端软的棒，将被测材料沿棒划过，根据出现划痕的位置确定被测材料的软硬。
定性地说，硬物体划出的划痕长，软物体划出的划痕短。
②压入硬度。
主要用于金属材料，方法是用一定的载荷将规定的压头压入被测材料，以材料表面局部塑性变形的大小比较被测材料的软硬。
由于压头、载荷以及载荷持续时间的不同，压入硬度有多种，主要是布氏硬度、洛氏硬度、维氏硬度和显微硬度等几种。
③回跳硬度。
主要用于金属材料，方法是使一特制的小锤从一定高度自由下落冲击被测材料的试样，并以试样在冲击过程中储存（继而释放）应变能的多少（通过小锤的回跳高度测定）确定材料的硬度。
金属材料中最常见的布氏硬度、洛氏硬度、维氏硬度都属于压痕硬度，硬度值表示材料表面抵抗另一物体压痕引起的塑性变形的能力。
用回弹法(肖氏和里氏)测量硬度，硬度值代表金属的弹性变形函数。
布氏硬度 Brinell Hardness用直径D的淬火钢球或硬质合金球作压头，以相应的试验力F 压入试件表面，经规定的保持时间后，卸除试验力，得到一直径为d的压痕。
用试验力除以压痕表面积，所得值即为布氏硬度值，符号用HBS或HBW表示。
HBS和HBW的区别是压头的不同。
HBS表示压头为淬硬钢球，用于测定布氏硬度值在450以下的材料，如软钢、灰铸铁和有色金属等。
HBW表示压头为硬质合金，用于测定布氏硬度值在650以下的材料。
同样的试块，当其它试验条件完全相同的情况下，两种试验结果不同，HBW值往往大于HBS值，而且并无定量的规律所循。
2003年以后，我国已经等效采用国际标准，取消了钢球压头，全部采用硬质合金球头。
因此HBS停止使用，全部用HBW 表示布氏硬度符号。
硬度简介：
硬度表示材料抵抗硬物体压入其表面的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1.布氏硬度(HB)
以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。
2.洛氏硬度(HR)
当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表示：
HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
HRC（一般使用）：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
3 维氏硬度(HV)
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。
硬度对照表：
根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。
洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算硬度是衡量材料软硬程度的一个性能指标。
硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度(HB)、洛氏硬度(HRA，HRB，HRC)、维氏硬度(HV)，橡胶塑料邵氏硬度(HA,HD)等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度(Hardness)的代号为H。
按硬度试验方法的不同，●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
●HV-适用于显微镜分析。
维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)。
●HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/ VA（冲击速度）。
●目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列》）。
硬度介绍及对照表
一、硬度简介：
硬度表示材料抵抗硬物体压入其表面的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1. 布氏硬度（HB）
以一定的载荷（一般3000kg）把一定大小（直径一般为10mm的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值（HB），单位为公斤力/mm2（N/mm2。
）
2. 洛氏硬度（HR）
当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表示：
HRA是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料（如硬质合金等）。
HRB是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料（如退火钢、铸铁等）。
HRC是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料（如淬火钢等）。
3 维氏硬度（HV）
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值（kgf/mm2）。
注：
洛氏硬度中HRAHRB HRC等中的A、B C为三种不同的标准，称为标尺A 标尺B、标尺C。
洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N（合10kgf），最后根据压痕深度计算硬度值。
标尺A使用的是球锥菱形压头，然后加压至588.4N（合60kgf）；标尺B使用的是直径为 1.588mm（1/16英
寸）的钢球作为压头，然后加压至980.7N（合100kgf）;而标尺C 使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N（合150kgf）。
因此标尺B适用相对较软的材料，而标尺C适用较硬的材料。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相
应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
但各种材料的换算关系并不一致。
本站《硬度对照表》一文对钢的不同硬度值的换算给出了表格，请查阅。
二、硬度对照表：
根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验
代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
下面是本站根据由实验得到的经验公式制作的快速计算器，有一定的实用价值，但在要求数据比较精确时，仍需要通过试验测得
三、硬度换算公式
1. 肖氏硬度(HS)=勃式硬度(BHN)/10+12
2. 肖式硬度(HS)=洛式硬度(HRC)+15
3. 勃式硬度(BHN)=M克式硬度(HV)
4. 洛式硬度(HRC)=a式硬度(BHN)/10-3
硬度测定范围:
HS<100
HB<500
HRC<70
HV<1300
洛氏硬度布氏硬度HB10/3000维氏硬度HV HRCHRA
59.580.7676
59.080.5666
58.580.2655
58.080.0645
57.579.7635
57.079.5625
56.579.2615
56.078.9605
55.578.6596
55.078.4538587
54.578.1532578
54.077.9526569
53.576.6520560
53.076.3515551
52.576.1509543
52.076
込503535
5
」
0176 b497527
5」076
3492520
附录G钢的硬度值换算（续）
表1钢的维氏硬度（HV与其他硬度和强度的近似换算值 a （续）
a)在本表中用黑体字表示的值与按ASTW E140表1的硬度转换值一致，由
相应的SAE- ASMk ASTM联合会列出的。
b)括号里的数值是超出范围的，只是提供参考。
在生产现场，由于受检测仪器的限制，经常使用布氏硬度计测量大型淬火件的硬度。
如果想知道该工件的洛氏硬度值，通常的方法是，先测量出布氏硬度值，然后根据换算表，查出相对应的洛氏硬度值，这种方式显然有些繁琐。
那么，能否根据布氏硬度计的压痕直径，直接计算出工件的洛氏硬度值呢？答案当然是肯定的。
根据布氏硬度和洛氏硬度换算表，可归纳出一个计算简单且容易记住的经验公式：HRC(479-100D) /4，其中D为①10m准冈球压头在30KN压力下压在工件上的压痕直径测量值。
该公式计算出的值与换算值的误差在0.5〜-1范围内,
该公式在现场用起来十分方便，您不妨试一试。