PAGE 071经验交流Experience Exchange色母对PBT 熔融结晶及力学性能的影响■ 柏志飞1 杜海涛1 李起龙1 王勇2（1.南京华信藤仓光通信有限公司 江苏 南京 210038）（2.扬州金森光电材料有限公司 江苏 扬州 225261）采用熔融共混法制备了不同色母比例的聚对苯二甲酸丁二醇酯（ＰＢＴ）试样，应用熔体速率流动仪、差示扫描量热仪（ＤＳＣ）、力学性能测试等方法研究色母添加量对ＰＢＴ熔融、结晶行为和力学性能的影响。
结果表明：作为异相成核剂，色母加入后可促进ＰＢＴ结晶，结晶度提高，结晶温度向高温移动，试样后收缩增大。
加入色母后可以提高ＰＢＴ的拉伸强度和弯曲模量，但是拉伸断裂伸长率及冲击强度却随着色母比例增加而降低。
Polybutylene terephthalate (PBT) samples of various color master batch (CMB) compositions were prepared via melt blending. The melting, crystallization, mechanical properties and after shrinkage were studied by means of melt flow rate measurer, differential scanning calorimeter (DSC) and mechanical tests. The results showed that the crystallization of PBT enhanced, crystallization peak shifted to higher temperature and after shrinkage enlarged, probably because the CMB acted as the nucleating agents. The tensile strength and flexural modulus increased, while the elongation at break and impact strength decreased with the increasing CMB content.聚对苯二甲酸丁二醇酯（ＰＢＴ） 色母 结晶 力学性能Polybutylene terephthalate (PBT); Color master batch; Crystallization; Mechanical propertiesDoi:10.3969/j.issn.1673-5137.2019.02.008摘 要Abstract关键词Key Words１． 前言聚对苯二甲酸丁二醇酯（PBT）是一种由对苯二甲酸和丁二醇单体脱水缩聚而成的热塑性聚酯。
PBT（聚对苯二甲酸丁二醇酯）是一种聚酯类的塑料，通常由对苯二甲酸和1,4-丁二醇合成。
在PBT中添加玻璃纤维（通常称为玻纤）可以改善其性能，增强其机械性能和热性能。
以下是玻纤在PBT中的作用：
机械性能提升：玻璃纤维是一种高强度、高模量的材料，将其添加到PBT中可以显著提升PBT的强度和刚度。
这对于需要高机械性能的应用非常有益，例如在汽车零部件、电子设备外壳等领域。
热性能改善：玻璃纤维的加入可以提高PBT的热变形温度，使其更适用于高温环境。
这对于一些需要耐高温性能的应用来说是很重要的，例如在发动机室内的汽车零部件。
维持尺寸稳定性：玻璃纤维的加入有助于减小PBT在温度变化时的尺寸变化，提高其尺寸稳定性。
这对于一些对尺寸精度要求较高的应用，如精密零部件，是非常重要的。
抗冲击性能提升：尽管PBT本身是一种相对刚硬的塑料，但添加玻璃纤维可以提高其抗冲击性能。
这对于一些需要同时具备强度和抗冲击性的应用非常有益。
耐化学性提升：玻璃纤维的加入也可以提高PBT的耐化学性，使其更能抵抗一些化学物质的侵蚀。
这对于在有腐蚀性环境中使用的应用来说是重要的。
总体而言，玻纤在PBT中的作用主要是为了改善其机械性能、热性能和其他一些特性，使其更适用于一些对材料性能要求较高的应用领域。