M. M. Rashad Æ Z. I. Zaki Æ H. El-Shall
Received: 23 October 2008 / Accepted: 16 March 2009 / Published online: 2 April 2009 Ó Springer Science+Business Media, LLC 2009
123
J Mater Sci (2009) 44:2992–2998
2993
The method is also called combustion method, polymeric precursor method, acids gel method (oxalate precursor, tartaric acid, lactic acid, etc.), and also Pechini-type process (Citrate precursor method). The organic precursor was not only used to form stable complexes with starting metallic ions but also used as organic rich fuel [20–23]. This study aims to synthezise the spinel magnesium aluminate nanopowders using 8-hydroxyquinoline (HQ) and tetraethyl ammonium hydroxide (TEAOH). The changes in phase formation, crystallite size, density, specific surface area, particle size distribution, and powder morphology were systematically studied.
Thus, it is important to obtain the spinel of high purity using an easy preparation method. The solid-state synthesis of MgAl2O4 spinel, as conventional synthesis technique,
J Mater Sci (2009) 44:2992–2998 DOI 10.1007/s10853-009-3397-8
LETTER
A novel approach for synthesis of nanocrystalline MgAl2O4 powders by co-precipitation method
To the best of our knowledge, no published study in the literature on synthesis of MgAl2O4 has so far used the co-precipitation method with organic reagents. Most publications about organic precursor technique, which involves the preparation of aqueous solution, required cation, the chelation of cations in solution by addition of carboxylic acid then, raising the temperature of the solution until formation of the precursor. The precursor is calcined at low temperature compared with other methods to form the powder, where the quasi-atomic dispersion of constituent components in liquid precursors facilitates synthesis of the crystallized powder.
requires higher temperature and longer reaction time so that the synthesized powder suffers from agglomeration and low sinter activity. Thus, the preparation of magnesium aluminate powders with high purity, chemical homogeneity, control of stoichiometry, fine particle size, narrow particle size distribution, and minimum particle agglomeration with high sinter activity has received considerable attention in order to improve the material properties [10]. Numerous wet chemical methods have been employed to synthesize magnesium aluminate fine particles including sol–gel [11, 12], co-precipitation [13–15], hydrothermal [16, 17], microwave-assisted combustion processing [18], microemulsion [19], metal-organic processing [20–23], spray drying [24], freeze drying [25], and mechanochemical synthesis [26, 27] techniques. The chemical co-precipitation method [28–31] ensures proper distribution of various metals ions resulting into stoichiometric and smaller particle sized product compared to some of the others. Moreover, the process is a lowcost technique suitable for the mass production compared to the other mentioned methods. The main drawback is that the particle size is not small and monodispersed enough for specific applications.
Experimental
Materials and processing
All the chemicals and reagents used were of high purity. The materials used were anhydrous aluminum chloride AlCl3, anhydrous magnesium chloride MgCl2, TEAOH (C2H5)4NOH, and 8-HQ C9H7NOH.
ቤተ መጻሕፍቲ ባይዱ
Introduction
Magnesium aluminate spinel (MgAl2O4) posseses a unique combination of desirable properties such as high melting point (2,135 °C), good mechanical strength at room and evaluated temperatures, high chemical inertness, low dielectric constant and electrical losses, good shock resistance, and excellent optical properties [1]. Due to these desirable properties, it has a wide range of applications in structural, chemical, optical, and electrical industries. MgAl2O4 has mainly been used as refractory in heavy industry and as substrate for solid-state electronic devices. Nowadays, new potential applications have been reported including; ceramic ultra-filtration membranes, electroinsulators, and optical materials such as optically transparent, fiber-optic temperature sensors, tunable solid-state lasers, matrix for fabrication of optical nanodevices, highbrightness phosphor screen, catalysis, and humidity sensor applications. Furthermore, the MgAl2O4 spinel has been employed as excellent transparent ceramic materials for high temperature arc-enclosing envelopes and alkali-metal vapor discharge devices [2–9].