Abstract: Nano-silver has become a substitute for traditional conductive materials because of its high conductivity, high transparency, high flexibility and flexibility. Exploring more convenient and environmentally friendly methods to prepare silver nanowires with different specifications and high quality as conductive materials has become a research trend. In this paper, silver nanowires were prepared by polyol reduction method. Silver ions in silver nitrate were reduced to silver by ethylene glycol. Polyvinylpyrrolidone (PVP) was used as structure-oriented and protective agent to promote the growth of silver nanowires. The morphology of nano-silver was characterized by field emission scanning electron microscopy (FESEM). It was found that when the PVP solution was 0.4 mol/L, most of the nano-silver was granular; when the PVP solution was 0.6 mol/L, nano-silver could grow into a line normally; but when the PVP solution was 0.8 mol/L, the surface coordination of the nucleus would be too strong to obtain the desired morphology.Keywords: silver nanowires; polyol; reduction method; conductive materia常子贡，吴若梅，武帅，陈振钊，周雨松，王丽萍(湖南工业大学 包装与材料工程学院，湖南 株洲 412000)多元醇法制备纳米银线及其性能研究Preparation and Properties of SilverNanowires by Polyol MethodCHANG Zi-gong, WU Ruo-mei, WU Shuai, CHEN Zhen-zhao, ZHOU Yu-song, WANG Li-ping(Institute of Packaging and Materials Engineering, Hunan University of Technology Zhuzhou Hunan 412007, China)摘要：纳米银因具有高导电性、高透光性、高耐弯曲性以及良好的柔性，成为了传统导电材料的替代品。

图18可以观察到随着反应时间的延长 ，溴化 银的衍 射峰逐 渐减弱 ，银的 衍射峰 逐渐增 强。反 应持续24h后， 溴化银 衍射峰 消失； 说明反 应结束 ，溴化 银全部 被还原 为银。 因为(111)晶 面和(200)晶面 衍射峰 的比值 较大， 可以得 出该银 纳米线 具有较 大的长 径比。
第18页/共20页
第7页/共20页
从图9(a)-(d)中的SEM图片中可以看出 在140 ℃温度 下，随 着反应 时间的 增长， 产物由 尺寸不 均匀的 银纳米 棒和形 貌不规 则的银 纳米颗 粒的混 合物生 长为纯 度教好 、均匀 性好的 银纳米 线。从 图9(d) 中的TE M可以 观察到 银纳米 线的直 径为80nm，长 度分部 在40~10 0um
图9 140 ℃不同反应时间下所得产物的SEM 和TEM 照片 第8页/共20页
图10 140℃反应24h银纳米线的XRD 谱图
该XRD谱图与银的衍射峰完全一致， 表明制 备的银 纳米线 具有面 心立方 结构， 且结晶 度很高 。
第9页/共20页
图11 反应时间为24 h, 不同反应温度下所得产物的SEM 照片 从图中SEM图中可以看出反应温度较 低是无 法得到 银纳米 线，产 物为形 貌不规 则的纳 米颗粒 ，这是 因为反 应温度 较低， 体系活 性低， 开始生 成的纳 米颗粒 无法在 溶解组 装成纳 米线； 反应温 度过高 时所得 产物为 尺寸较 大的不 规则纳 米颗粒 ，因为 反应温 度高， 体系活 性大分 子运动 也比较 剧烈, 使得PVB 难以稳定吸附在晶体(100)晶面上。
1.功能性纳米粒子的制备与分析(一维结构纳米银的合成研究)
图2 纳米银合成的操作流程图
图1 高分子-多元醇合成法制备纳米银装置实验图 第1页/共20页

2. Introduction to synthesis of silver nanowires
3. Synthesis of silver nanowires based on the polyol method
• 3.1 Introduction to the polyol method • 3.2 Mechanism • 3.3 Improvements of the polyol method • 3.4 Further research
3.3 Improvements
Several key factors
Formation of MTPs :
Requiring a low concentration of AgNO3
Etching of MTPs:
Requiring reducing the effct of oxygen on the activity of MTPs
Biomdeidcal and chemical sensor
Catalysts
……
Silver nanowires rafts for trace analysis
Optical negative refraction
ppt课件
5
Jie Yao, et al.Science,2008,321,930
2.Introduction to synthesis of silver nanowires
Approaches for synthesis of silver nanowires generally fall into one of two categories:
Template-directed
PVP

银纳米线的制备和应用研究银纳米线是一种高效的导电材料，已经得到了广泛的应用和研究。

本文将介绍银纳米线的制备方法和应用研究，并探讨其未来发展方向。

一、银纳米线的制备方法1. 溶液法溶液法是一种常见的制备银纳米线的方法。

该方法主要包括两个步骤：先制备出含有银离子的溶液，然后在溶液中添加适当的还原剂，如氢气或维生素C，使银离子还原成银微粒，再在微粒表面形成银纳米线。

2. 气相法气相法是另一种制备银纳米线的方法。

该方法主要借助于物理气相沉积技术，将金属银蒸发到高温下的气态条件下，经过淀积和延展作用，得到产品。

3. 电化学法电化学法是在电解质溶液中将金属银氧化成离子，并在电位调节的作用下，使其还原成银微粒，形成银纳米线。

以上方法各有特点，银纳米线的制备过程也会不同。

二、银纳米线的应用研究1. 透明电极透明电极是一种重要的电子器件，适用于触摸屏、太阳能电池和发光二极管等领域。

银纳米线因其高导电性、透明性和柔性，成为透明电极材料的首选。

2. 柔性电子器件随着电子器件的发展，柔性电子器件成为越来越受关注的领域。

银纳米线因其柔性优良，成为制备柔性电子器件的重要材料。

例如，可以用银纳米线作为导电垫层，制备出柔性的显示器、传感器和照明设备等。

3. 可穿戴设备可穿戴设备已经成为人们日常生活中不可或缺的一部分，但是传统电子器件的刚性限制了设备的发展。

银纳米线材料的柔性和透明性，使得可穿戴设备具有了更多的发展空间。

例如，可以用银纳米线制备出具有温度感应功能的可穿戴衣物，以及弹性好、舒适度高的运动手环、智能手表等。

三、银纳米线的未来发展随着人们对可穿戴设备、智能家居等生活科技产品的需求越来越多，银纳米线等类似的高性能材料将会得到更多的应用。

此外，科学家也在不断探索使用银纳米线和其他材料制备新型电子器件的方法。

例如，可以将银纳米线与石墨烯相结合，用于传感器、透明发光二极管等领域。

总之，银纳米线是一种具有广阔应用前景的高性能材料，其制备方法和应用领域也在不断发展和拓展。