硬度与强度还是有⼀定的关系的，附硬度对照表
硬度与强度的关系：
硬度试验是机械性能试验中最简单易⾏的⼀种试验⽅法。
为了能⽤硬度试验代替某些机械性能
试验，⽣产上需要⼀个⽐较准确的硬度和强度的换算关系。
实践证明，⾦属材料的各种硬度值
之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗⼒和继续塑
性变形抗⼒决定的，材料的强度越⾼，塑性变形抗⼒越⾼，硬度值也就越⾼。
根据德国标准DIN50150,以下是常⽤范围的钢材抗拉强度与维⽒硬度、布⽒硬度、洛⽒硬度、肖
⽒硬度的对照表：
欢迎⼤家在评论处补充你认为⽂章中有解释不对或⽋缺的部分，这样下⼀个阅读的⼈就会学到更多，你知道的正是⼤家需要的。
强度\硬度换算表序号洛氏硬度HRC洛氏硬度HRA表面洛氏硬度HR15N表面洛氏硬度HR30N表面洛氏硬度HR45N维氏硬度HV布氏硬度HB30D2布氏硬度d10、2d5、4d2.5mm抗拉强度σbMPa碳钢抗拉强度σbMPa铬钢抗拉强度σbMPa铬钒钢抗拉强度σbMPa铬镍钢抗拉强度σbMPa铬钼钢抗拉强度σbMPa铬镍钼钢抗拉强度σbMPa铬锰硅钢抗拉强度σbMPa超高强度钢抗拉强度σbMPa不锈钢抗拉强度σbMPa不分钢种117.67.337.915.62112114.1573.6706705772726757703724217.567.638.416.22142144.1374.4714712775731763711731318.67.838.916.82162164.11753723719779737769719737418.568.39.317.42182184.09762731727783743776728744519.68.339.818.221224.07771739735788749782737752619.568.540.318.62232224.0578748743792755789745759720.68.840.719.22262254.0379757751797761796754767820.569.41.219.82292274.02799766759802768803764774921.69.341.720.42312274.0809775767807775817737821 021.69.542.221.232323.97819785776813782817782791541 122.69.842.621.52372343.958297947858197898257927991 222.570.43.122.1242373.938398047948257978328028081 323.70.343.622.7243243.91849814803831805848128161 423.570.644.23.32462423.89868248138388138488228251 524.70.844.523.92492453.87878348238458218568328351 624.571.145.24.52522483.85881844833852838658438441 725.71.445.525.12552513.83892855843868388748538541 825.571.645.925.72582543.89038658538688478668828648641 926.71.946.426.32612573.789148768648768578768928758742 026.572.246.926.9264263.769268878758848678869018858842 127.72.447.327.52682633.74937898886893877897918978952 227.572.747.828.12712663.72949909897902887907929089062 328.73.48.328.72742693.796192909912897918939199172 428.573.348.729.32782733.67972932921922908939419319282273.49.29.227 3.698949393919495949459.052981654332911202 629.573.849.730.5285283.639979559469429319539629549512 730.74.150.231.12982833.6110099679599539439669739669642 830.574.450.631.72922873.5910219799729649559789859789762 931.74.751.132.32962913.561034991985976967991996999893 031.574.951.632.932943.54104710049999889810051008100310013 132.75.252.33.5342983.52106010161013100199310181020101510153 232.575.552.534.1383023.51073102910271013100710321033102810283 333.75.853.34.73123063.481086104210421027102010471046104110423 433.576.153.435.3316313.461100105510571040103510621059105410563 534.76.453.935.9323143.431113106810721054104910771073106710703 634.576.754.436.53243183.411127108210881069106410921086108110853 735.77.54.837.3293233.391141109511041084107911081101109511003 835.577.255.337.63333273.371156110911201099109511251115110911153 936.77.555.838.23383323.341170112411361115111111411130112311314 036.577.856.238.83423363.32118511381153113111281158114611381147序号洛氏硬度HRC洛氏硬度HRA表面洛氏硬度HR15N表面洛氏硬度HR30N表面洛氏硬度HR45N维氏硬度HV布氏硬度HB30D2布氏硬度d10、2d5、4d2.5mm抗拉强度σbMPa碳钢抗拉强度σbMPa铬钢抗拉强度σbMPa铬钒钢抗拉强度σbMPa铬镍钢抗拉强度σbMPa铬钼钢抗拉强度σbMPa铬镍钼钢抗拉强度σbMPa铬锰硅钢抗拉强度σbMPa超高强度钢抗拉强度σbMPa不锈钢抗拉强度σbMPa不分钢种4 137.78.156.739.43473413.31200115311711148114411761161115311634 237.578.457.240.3523453.281215116811881165116211941177116811804 338.78.757.640.6357353.261231118412061182117912121194118411974 438.579.58.141.23623553.2412461199122512001197123112111193120012144 539.70.79.358.641.8367363.2112631216124312191216125012281218121612324 639.570.379.659.42.43723653.1912791232126212381235127012461243123312504 740.70.579.959.543.377373.1712961249128212571254129012641267125012684 840.570.880.260.43.63823753.1512131267130212771274131012831291126812874 941.71.80.560.444.238383.1313311284132212981294133113021315128613070185 041.571.380.860.944.83933853.1113481303134313191315135313221339130513275 142.71.681.161.345.43993913.0913671322136413401336137513421362132513475 242.571.881.461.845.9453963.0713861341138513621357139713621385134513685 343.72.181.762.346.54114013.0514051361140713851379142013841409136613895 443.572.482.62.747.14174073.0314251382142914081402144314051432138714115 544.72.682.363.247.74234133.0114451403145214311425146714271455141014345 644.572.982.663.648.34294182.9914661426147514551448149114501478143314575 745.73.282.964.148.94364242.9714881448149814801472151614741502145714805 845.573.483.264.649.5443432.9515101472152215051497154114981526148215045 946.73.783.565.50.14494362.9315331497154715311522156715221550150815296 046.573.983.765.550.74564422.9115561522157215571547159315471575153515556 147.74.284.65.951.24634492.8915811549159715841573162015731600156315816 247.574.584.366.451.8474552.8716061576162316121599164816001625159216086 348.74.784.666.852.44784612.85163116051649164016261676162716521623163564784.67.53.446 2.81616161616171616161648.55.9308583583575695404547955636 549.75.385.267.753.64934742.8116861666170216981682173316831707168816926 649.575.585.568.254.2514812.7917141698173017281710176217121735172317226 750.75.885.768.654.7594882.7717441731175817581739179317421765175917536 850.576.186.69.155.34174942.75176717871790176918231773179517856 951.76.386.369.555.95255012.73180318161821179918541804182718177 051.576.686.670.56.5534184118451854183018861836186018517 152.76.986.870.457.1543188118751887186119181870189418857 252.577.187.170.957.655119061920189319511903193019217 353.77.487.471.358.256119371955192519851938196719577 453.577.787.671.858.857196819901974200519957 554.77.987.972.259.4579200020252010204520347 654.578.287.672.659.9589203320612048208720747 755.78.588.473.160.5599206620982086213121157 855.578.788.673.561.169217721577 956.79.88.973.961.762222422018 056.579.389.174.462.263122742246序号洛氏硬度HRC洛氏硬度HRA表面洛氏硬度HR15N表面洛氏硬度HR30N表面洛氏硬度HR45N维氏硬度HV布氏硬度HB30D2布氏硬度d10、2d5、4d2.5mm抗拉强度σbMPa碳钢抗拉强度σbMPa铬钢抗拉强度σbMPa铬钒钢抗拉强度σbMPa铬镍钢抗拉强度σbMPa铬钼钢抗拉强度σbMPa铬镍钼钢抗拉强度σbMPa铬锰硅钢抗拉强度σbMPa超高强度钢抗拉强度σbMPa不锈钢抗拉强度σbMPa不分钢种8 157.79.589.474.862.8642232622938 257.579.889.675.263.4653238023418 358.80.189.875.663.9664243723918 458.580.390.76.164.5676249624438 559.80.690.276.565.1688255824968 659.580.990.476.965.67262325518 760.81.290.677.366.2713269126078 860.81.90.877.766.8725468 961.81.791.78.167.37399 061.582.91.278.667.97529 162.82.291.479.68.47669 262.582.591.579.469.789 363.82.891.779.869.57959 463.583.191.880.270.1819 564.83.391.980.670.68259 664.583.692.181.71.2849 765.83.992.281.371.78569 865.584.18729 966.84.48891 0 066.584.7961 0 167.85.9231 0 267.585.294116890 38.5.5591 0 468.585.89781 0 569.86.19971 0 669.586.31171 0 770.86.6137。
一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。
由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。
当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。
在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。
由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。
换言之是只对调质件（淬火+400℃回火）进行拉伸试验。
在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。
高频淬火和渗碳淬火即为此适用例。
受拉应力的零件不采用低温回火。
不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。
低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。
二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。
硬度表示材料抵抗硬物体压入其外表的能力。
它是金属材料的重要性能指标之一。
一般硬度越高，耐磨性越好。
常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。
1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料外表，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm 2 (N/mm 2)。
2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm 的钢球，在一定载荷下压入被测材料外表，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表示：• HRA ：是采用60kg 载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
• HRB ：是采用100kg 载荷和直径1.58mm 淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
• HRC ：是采用150kg 载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
3 维氏硬度(HV)以120kg 以内的载荷和顶角为136°的金刚石方形锥压入器压入材料外表，用材料压痕凹坑的外表积除以载荷值，即为维氏硬度HV 值(kgf/mm 2)。
邵氏硬度〔HA 〕 邵氏硬度专用在橡胶方面的硬度测试 做橡胶的应该知道怎么测邵氏硬度〔HA 〕 用于橡胶、塑料等材料的硬度测定，将一定形状的钢制压针，在试验力作用下压入试样外表，当压足平面与试样外表严密贴合时，测量压针相对压足平面的伸出长度。
通过公式计算出邵氏硬度值。
具有构造简单、使用方便、型小体轻、读数直观等特点。
A 型参数：刻度盘值：0-100HA ；压针行程范围：0—2.5mm ；压针端部压力：0.055N-8.05N ；压针顶 端直径：Φ0.79mm+\-0.03m m 。