煤炭合成尼龙66工艺流程英文回答：The process of coal to nylon 66 synthesis involves several steps. First, coal is converted into coal gas through a process called gasification. This involves heating the coal in the absence of oxygen to produce a mixture of carbon monoxide and hydrogen gases.Next, the coal gas is purified to remove impurities such as sulfur and nitrogen compounds. This is important to prevent these impurities from affecting the subsequent steps of the synthesis process.After purification, the carbon monoxide and hydrogen gases are reacted together in the presence of a catalyst to produce a mixture of organic compounds known as synthesis gas. This synthesis gas contains a variety of molecules, including those that can be used to produce nylon 66.The synthesis gas is then further processed to separate and purify the desired molecules for nylon 66 production. This involves a series of chemical reactions and separation techniques, such as distillation and crystallization.Once the desired molecules are obtained, they are polymerized to form nylon 66. Polymerization is a processin which small molecules, called monomers, are chemically bonded together to form a large, chain-like structure. In the case of nylon 66, the monomers are adipic acid and hexamethylenediamine. These monomers react together to form the repeating units of nylon 66.The polymerization process can be carried out using various methods, such as melt polymerization or solution polymerization. In melt polymerization, the monomers are melted and reacted together, while in solution polymerization, the monomers are dissolved in a solvent and reacted.Once the nylon 66 is formed, it can be further processed into various products, such as fibers, films, andplastics. These products have a wide range of applications, including in the textile, automotive, and electronics industries.中文回答：煤炭合成尼龙66的工艺流程包括几个步骤。

尼龙66工艺流程讲解英文回答：Nylon 66 Manufacturing Process.Polymerization.Nylon 66 is produced through the condensation polymerization of hexamethylene diamine (HMD) and adipic acid (AA). The reaction takes place in two stages:Amidation: HMD and AA are heated in the presence of water to form nylon salt, which is a high-viscosity liquid.Polymerization: The nylon salt is further heated to remove water and form the nylon 66 polymer. This process is typically carried out in a continuous reactor under high pressure and temperature.Spinning.The molten nylon 66 polymer is extruded through spinnerets into a fiber form. The fibers are cooled and solidified in a spinning bath. The spinning process can be classified into two main methods:Melt spinning: The molten polymer is extruded through a spinneret with small holes to form fine fibers.Solution spinning: The polymer is dissolved in a solvent and extruded through a spinneret to form fibers. The solvent is then removed through evaporation.Drawing.The spun fibers are subsequently drawn to align the molecules and improve their strength and toughness. Drawing involves stretching the fibers under controlled conditions of temperature and tension.Heat Treatment.Drawn fibers are heat treated to further enhance their properties. Heat treatment can be carried out in different ways, including:Annealing: Heating the fibers above their glass transition temperature and then cooling them slowly.Quenching: Rapidly cooling the fibers from an elevated temperature.Extrusion.Heat-treated fibers are extruded into various shapes and sizes, such as yarns, filaments, and film. Extrusion involves melting the polymer and forcing it through a die.Properties of Nylon 66。

尼龙-66的连续聚合生产工艺流程课程设计高分子合成工艺设计说明书年产60万吨尼龙66连续聚合生产工艺设计院、部：材料与化学工程学院学生姓名：指导教师：职称专业：高分子材料与工程班级：1001班完成时间：2013年06月03日摘要本文主要阐述了尼龙-66的国内外发展现状以及研究其连续聚合生产工艺流程设计过程。

设计尼龙-66连续聚合的工艺流程，选择正确的工艺条件和设备，并进行合理的设备配置，以便按我们的要求进行生产。

关键词：尼龙-66；连续聚合ABSTRACTThi sarticle expounded the development situation from domestic and overseas of nylon-66 and also studied it’s process of continuous polymerization. In order to meet our request, we designed process of continuous polymerization of nylon-66, chose suitable processing condition and device arrange the devices appropriately.Key words： nylon-66；continuous polymerization目录1 绪论 (1)1.2 国外生产现状 (1)1.3 国内生产现状 (2)1.3 进出口情况 (3)2 工艺流程和方案的说明及论证 (5)2.1 工艺路线的选择 (5)2.2 工艺流程设计 (5)2.2.1尼龙66的生产原料及原料制备 (5)2.2.2尼龙66的生产工艺 (9)2.3 工艺参数的选择 (10)2.3.1 工艺关键点控制 (10)2.3.2工艺说明 (12)3 物料衡算 (13)3.1 年产量60万吨尼龙-66的物料衡算过程 (13)4 热量衡算 (18)4.1 尼龙66生产中的能耗分析 (18)4.2 尼龙66生产设备的能量衡算 (18)4.2.1 蒸发器 (18)4.2.2 反应器 (20)4.2.3 闪蒸器 (21)4.2.4 聚合器 (23)5 聚合釜及各设备选型 (25)5.1对设备的要求 (25)5.2溶解过程 (25)5.3预缩聚过程 (25)5.4闪蒸过程 (25)5.5后缩聚过程 (26)参考文献 (27)致谢 (29)附录 (30)1 绪论引言+生产能力数据+聚合方法（连续缩聚+间歇缩聚）+主要（连续聚合）尼龙66是最早研制成功的尼龙品种,于1939年由美国杜邦公司实现工业化生产,是目前最主要的尼龙品种之一。

尼龙66盐工艺流程
《尼龙66盐工艺流程》
尼龙66是一种重要的合成纤维，它具有优异的强度和耐热性能，被广泛应用于纺织品、工业材料等领域。

而尼龙66的生产过程中，盐工艺流程是其中关键的一环。

尼龙66的盐工艺流程主要包括以下几个步骤：
1. 原料准备：将己内酰胺和六亚胺混合，在加入盐酸，使其形成盐酸盐。

2. 合成反应：将盐酸盐与水、溶剂等混合物加热至一定温度，进行聚合反应，生成尼龙66。

3. 混合和过滤：将合成反应产物进行混合、过滤，去除杂质和未反应的原料。

4. 溶剂回收：从混合和过滤后的溶剂中回收并重复利用。

5. 干燥和成形：将溶剂回收后的产物进行干燥，再经过成形工艺，最终得到尼龙66的成品。

尼龙66盐工艺流程是一个比较成熟和稳定的生产工艺，通过优化每一个步骤，可以实现高效、高质量的尼龙66生产。

与此同时，尼龙66的生产还需要严格控制工艺条件，确保产物的品质和稳定性。

总的来说，尼龙66盐工艺流程是尼龙66生产过程中至关重要的一环，其优化和稳定对于尼龙66的生产和品质有着重要的影响。

通过不断的技术创新和工艺改进，可以进一步提升尼龙66的生产效率和产品质量。

中文名称聚己二酰己二胺俗名尼龙66英文名称Nylon 66结构式 [-NH (CH2)6NHCO(CH2)4CO-]n(一)发展简史尼龙66足最早开发成功的尼龙品种。

1935年美目Du Pont公司采用己二胺和己二酸缩聚制得，并于1939年实现工业化生产。

此后，德国BASF公司，日本东丽公司也先后实现了工业化生产。

尼龙66是目前聚酰胺系列产品中产量最大的品种。

1997年美国聚酰胺消费量为575kt，其中尼龙66的消费量占50％以上。

国内黑龙汀省尼龙厂、上海塑料制品十八厂用作塑料，上海天原化工厂、山西太原合成纤维厂用作纤维。

（二）生产方法尼龙66由己二酸和己二胺缩聚而成。

它的生产工艺主要有单体合成、尼龙66盐的制备和缩聚三个工序。

1.单体合成1)己二酸的制备主要有苯酚法、环己烷法和丙烯腈二聚法。

苯酚法是以苯酚为原料，用雷尼镍作催化剂，在140～l50℃和2～3MPa压力下，加氢生成环己醇，然后用60％～65％浓度的硝酸，在铜或钒催化剂存在下，在55～60℃氧化成己二酸。

反应式如下：环己烷法是以环己烷为原料，在环烷酸钴或硼酸催化剂存在下，通入空气加压液相氧化，生成环己酮和环己醇的混合物，再用60％浓度的硝酸在45～60℃氧化成己二酸。

反应式如下：丙烯腈二聚法是以丙烯腈为原料，用电解还原法二聚生成己二腈，然后在稀硫酸水溶液中加热水解得到己二酸。

反应式如下：2)己二胺的制备主要有己二酸法和丁二烯法。

己二酸法是以己二酸为原料，在磷酸二丁酯等脱水催化剂存在下，于280～300℃温度下氨化脱水，得到己二腈，再在雷尼镍催化剂存住下，在90℃和2．8MPa压力下，于乙酸中加氢得到己二胺。

反应式如下：丁二烯法是先使丁二烯氯化生成二氯丁烯异构体混合物，再与氢氰酸或氰化钠在酸性水溶液中氰化成丁烯二氰异构体，然后用氧氧化钠处理，使异构体全部转化成l，4-二氰基丁烯-2，精制后用钯炭作催化剂，在300℃下氢化成己二胺。

反应式如下：2．尼龙66盐的制备由二元酸和二元胺制取尼龙时，需要严格控制原料配比为等摩尔比，才能得到分子量较高的聚合物，因此，住生产中必须先把己二酸和己二胺混合制成尼龙66盐。

华侨大学课程名称：增强增韧尼龙66汽车专用料*****学号：9专业：08高分子二班任课教师：***前言：尼龙是结晶型塑料，品种颇多，已达到130多种，应用于注塑加工的有尼龙6、尼龙66、尼龙610、尼龙1010以及共聚性尼龙、超韧性尼龙、玻璃纤维增强尼龙、矿物增强尼龙等等。

世界市场中，应用量最大的是尼龙66。

尼龙最早在1889年首先由Gabriel和Maass 两人合成制得，但系统的研究并最终实现工业化实在1929年，由美国杜邦公司的Carothers着手进行的。

1931年Carothers申请了第一篇尼龙专利，1935年首先制得尼龙66，1939年实现工业化。

尼龙66的应用领域一般在汽车、电子电器、化工设备、机械设备等方面。

从最终用途看，汽车行业消耗的尼龙66占第一位，电子电器占第二位。

大约有88%的尼龙66通过注射成型加工成各种制件，约12%的尼龙66则通过挤出、吹塑等成型加工成相应的制品。

由于尼龙66优良的耐热性、耐化学药品性、强度和加工方便等，因而在汽车工业得到了大量应用，目前几乎已能用于汽车的所有部位，如发动机部位，电器部位和车体部位。

发动机部位包括进气系统和燃油系统，如发动机气缸盖罩、节气门、空气滤清器机器外壳，车用空气喇叭、车用空调软管、冷却风扇及其外壳、进水管、刹车油罐及灌盖，等等。

车体部位零部件有：汽车挡泥板、后视镜架、保险杠、仪表盘、行李架、车门手柄、雨刷支架、安全带扣搭、车内各种装饰件等等。

车内电器方面如电控门窗、连接器、保鲜盒、电缆扎线等。

工艺特点：⑴吸水性尼龙66较易吸湿，如果长时间暴露在空气下，会吸收大气中的水分。

吸水后会发生体积膨胀，影响制品的尺寸精度，如在注塑前吸收过量的水分时，其制作的外国外观和力学性质都会受损。

⑵结晶性尼龙66为结晶性高聚物，一般在20%~30%之间。

结晶度的高低与性能有关，结晶度高，拉伸强度、耐磨性、硬度、润滑性等性能有所提高，热膨胀系数和吸水性趋于下降。

尼龙66聚合过程与工艺己二酸和己二胺发生缩聚反应即可得到尼龙-66。

工业上为了己二酸和己二胺以等摩尔比进行反应，一般先制成尼龙-66盐后再进行缩聚反应。

在水的脱出的同时伴随着酰胺键的生成，形成线型高分子。

所以体系内水的扩散速度决定了反应速度，因此在短时间内高效率地将水排出反应体系是尼龙-66制备工艺的关键所在。

上述缩聚过程既可以连续进行也可以间歇进行。

在缩聚过程中，同时存在着大分子水解、胺解(胺过量时)、酸解(酸过量时)和高温裂解等使尼龙66的分子量降低的副反应。

尼龙-66盐的制备尼龙-66盐是己二酰己二胺盐的俗称，分子式:C12H26O4N2，分子量262.35,结构式:[+H3N(CH2)6NH3+-OOC(CH2)4COO-]。

尼龙-66盐是无臭、无腐蚀、略带氨味的白色或微黄色宝石状单斜晶系结晶。

室温下，干燥或溶液中的尼龙-66盐比较稳定，但温度高于200?时，会发生聚合反应。

尼龙-66盐在水中的溶解度很大，且随着温度上升而增大，其溶解度cs与温度的关系可描述为:cs=-376.3286+1.9224 T-0.001149T2尼龙-66盐在水中的溶解度温度，K 273.16 283.16 293.16 303.16 313.06 323.16 333.16 343.16 353.16溶解度，g/ml 37.00 43.00 47.00 50.50 52.50 54.00 56.00 58.5061.50(1)水溶液法以水为溶剂，以等当量的己二胺和己二酸在水溶液中进行中和反应，得到50%的尼龙-66盐溶液。

工艺流程:1-己二酸配制槽2-己二胺配制槽3-中和反应器4-脱色罐5-过滤器6、9、11、12-贮槽7-泵8-成品反应器10-鼓风机13-蒸发反应器将纯己二胺用软水配成约30%的水溶液，加入反应釜中，在40~50?、常压和搅拌下慢慢加入等当量的纯己二酸，控制pH值在7.7~7.9。

在反应结束后，用0.5%~1%的活性炭净化、过滤，即可得到50%的尼龙-66盐水溶液。