超级黄铜与磷铜比较表

磷青銅-黄铜等材料性能规格磷青銅(Phosphor Bronze) 特性及規格一覽表：(1)化學成份(Chemical Composition)(2)物理特性(Physical Properties)(3)機械性質(Mechanical Properties)Mechanical Properties (continuous)黃銅(Brass) 特性及規格一覽表：(1)化學成份(Chemical Composition)(2)物理特性(Physical Properties)(3)機械性質(Mechanical Properties)合編號Alloy No.質別Temper符號Symbol抗拉試驗Tensile test硬度試驗Hardness test厚度Thickness(mm)抗拉強度Tensilestrength(kgf/mm2)延伸率(50mm)Elongation(in2”)(%)HvThickness>0.15mmC2600O C2600R-O > 0.2 > 28 > 40 70~90 H/2 C2600R-H/2> 0.2 36~45 > 28 110~130H C2600R-H > 0.2 42~55 - 140~160 EH C2600R-EH> 0.2 53~60 - 160~180SH C2600R-SH> 0.2 > 58 - > 180C2680O C2680R-O > 0.2 > 28 > 40 70~90 H/2 C2680R-H/2> 0.2 36~46 > 28 110~130H C2680R-H > 0.2 42~55 - 140~160 EH C2680R-EH> 0.2 53~60 - 160~180SH C2680R-SH> 0.2 > 58 - > 180C2801O C2801R-O > 0.2 > 33 > 35 -H/4 C2801R-H/4> 0.2 36~45 > 25 95~115H/2 C2801R-H/2> 0.2 42~50 > 15 115~140 H C2801R-H > 0.2 > 48 - > 140C194合(HSM Copper)特性及規格一覽表：(1)化學成份(Chemical Composition)合編號化學成份(wt.%)Material Designation Cu Fe P Zn Pb JIS C194 Rem. 2.10~2.60 0.015~0.15 0.05~0.20 <0.03(2)物理特性(Physical Properties)(3)機械性質(Mechanical Properties)合編號Alloy 質別Temper符號Symbol抗拉試驗Tensile test硬度試驗Hardness testNo.厚度Thickness(mm)抗拉強度Tensilestrength(kgf/mm2)延伸率(50mm)Elongation(in2”)(%)HvThickness>0.15mmC194O C194R-O > 0.2 31~38 > 25 90~115H/2 C194R-H/2 > 0.2 37~44 > 6 115~135 H C194R-H > 0.2 42~49 > 3 125~145 EH C194R-EH > 0.2 47~51 > 2 135~150 SH C194R-SH > 0.2 49~53 - 140~155ESH C194R-ESH> 0.2 51~56 - 145~160紅銅(Copper) 特性及規格一覽表：(1)化學成份(Chemical Composition)合編號化學成份(wt.%) Material Designation Cu PJIS C1100(ETP)C1200(DLP)C1220(DHP)99.9(min)99.9(min)99.9(min)-0.004~0.0120.015~0.040(2)物理特性(Physical Properties)合編號(Alloy No. )密度(Density)g/cm3彈性係數(Modulus ofElasticity)(Young’sModulus)GPa熱膨脹係數(Coefficient ofThermalExpansion at 20 o C to300 o C)m/m．K熱傳導係數(ThermalConductivityat 20 o C)W/m．K導電率(ElectricalConductivity at20 o C)%IACSC1100 C1200 C1220 8.948.948.9411711711716.916.917.1391.1386.0339.21019885(3)機械性質(Mechanical Properties)合編號Alloy No.質別Temper抗拉試驗Tensile test硬度試驗Hardness test 厚度Thickness(mm)抗拉強度Tensile strength(kgf/mm2)延伸率(50mm)Elongation(in2”)(%)HvThickness>0.15mmC1100 C1200 C1220O > 0.2 < 27 > 30 < 65 H/4 > 0.2 24~30 > 13 60~80 H/2 > 0.2 26~33 > 10 70~90 3/4H > 0.2 29~35 > 5 80~100 H > 0.2 30~37 > 4 90~110 EH > 0.2 33~40 > 3 95~110 SH > 0.2 35~41 > 2 100~125磷青銅(Phosphor Bronze)合各規格對照表規格名稱SPEC 合 編號 Alloy No.化 學 成 分 Chemical Composition (wt.%)規格號Speno.Cu Sn P Fe Ni Pb Zn OthersISO CuSn 4Rem. 3.5~4.50.01~0.40 ≦0.1 ≦0.3 ≦0.05 ≦0.3 ----427CuSn 5 4.5~5.5CuSn 6 5.5~7.5CuSn 8 7.5~9.0 CNS C5101Rem. 3.0~5.50.03~0.35 ---- ---- ---- ---- Cu ＋Sn ＋P≧99.5950H311C5191 5.5~7.0C5212 7.0~9.0JISC5111 Rem. 3.5~4.5 0.03~0.35---- ---- ---- ----Cu ＋Sn ＋P≧99.5H311C51024.5~5.5C5191 5.5~7.0C5212 7.0~9.0 C5210 7.0~9.0 ≦0.1 ----≦0.05≦0.2 Cu ＋Sn ＋P≧99.7 H313ASTM C51100Rem. 3.5~4.90.03~0.35 ≦0.1 ----≦0.05 ≦0.3 ---- B10C51000 4.2~5.8C51900 5.0~7.0C52100 7.0~9.0 ≦0.2DIN CuSn 4Rem. 3.5~4.50.01~0.35 ≦0.1 ≦0.3 ≦0.05≦0.3 ≦0.2 1766CuSn 6 5.5~7.5CuSn 8 7.5~8.5BS PB101 Rem. 3.5~4.5 0.02~0.40 ---- ---- ≦0.02 ≦0.3---- 287PB102 4.5~5.5PB1035.5~7.5銅合 板材厚度公差 (Thickness tolerances for strip):紅銅 (C1100、C1200、C1220) 黃銅 (C2600、C2680、C2801)磷青銅(C2600、C2680、C2801) 特殊銅合(C194)銅合板材寬度公差(Width tolerances for strip):銅合板材蛇彎度公差(Permissible max. value on camber):* Dimensional tolerances shall be in accordance with JIS H3100。

磷青铜-黄铜等材料性能规格磷青铜(Phosphor Bronze) 特性及规格一览表：(1)化学成份(Chemical Composition)(2)物理特性(Physical Properties)(3)机械性质(Mechanical Properties)固溶热处理, 冷加工至1/8 硬(1/8H)；固溶热处理, 冷加工至硬态(H)；沉淀硬化(AT)；1/4 硬和沉淀热处理(1/4HT)；半硬和沉淀热处理(1/2HT)O：退火（软）状态；H：加工硬状态；EH：特硬状态；SH：抗拉强度最大的加工制品；Mechanical Properties (continuous)SH C5191R-SH> 0.2> 75> 5230~270C5212O CC5210R-O> 0.2> 35> 45-H/4C5210R-H/4> 0.240~52> 40120~150 H/2C5210R-H/2> 0.250~60> 30150~170 3/4H C5210R-3/4H> 0.252~62> 20170~190 H C5210R-H> 0.260~72> 12190~210 EH C5210R-EH> 0.270~80> 8210~230 SH C5210R-SH> 0.2> 75> 5230~270黄铜(Brass) 特性及规格一览表：(1)化学成份(Chemical Composition)合金编号化学成份(wt.%)Material Designation Cu Zn Fe PbJIS C2600C2680C280168.5~71.564.0~68.559.0~63.0Rem.Rem.Rem.0.05(max)0.05(max)0.05(max)0.07(max)0.15(max)0.30(max)(2)物理特性(Physical Properties)合金编号(Alloy No. ) 密度(Density)g/cm3弹性系数(Modulus ofElasticity)(Young’s Modulus)GPa热膨胀系数(Coefficient of ThermalExpansion at 20 o C to 300o C)m/m．K热传导系数(ThermalConductivityat 20 o C)W/m．K导电率(ElectricalConductivity at 20o C)%IACS(3)机械性质(Mechanical Properties)C194合金(HSM Copper)特性及规格一览表：(1)化学成份(Chemical Composition)合金编号化学成份(wt.%)Material Designation Cu Fe P Zn PbJIS C194Rem. 2.10~2.600.015~0.150.05~0.20<0.03 (2)物理特性(Physical Properties)合金编号(Alloy No. ) 密度(Density)g/cm3弹性系数(Modulus ofElasticity)(Young’sModulus)GPa热膨胀系数(Coefficient of ThermalExpansion at 20 o C to300 o C)m/m．K热传导系数(ThermalConductivityat 20 o C)W/m．K导电率(ElectricalConductivity at20o C)%IACSC1948.8312116.326265 (3)机械性质(Mechanical Properties)合金编号质别Temper符号Symbol抗拉试验Tensile test硬度试验Hardness testAlloyNo.厚度Thickness(mm)抗拉强度Tensilestrength(kgf/mm2)延伸率(50mm)Elongation(in 2”)(%)HvThickness>0.15mmC194O C194R-O> 0.231~38> 2590~115 H/2C194R-H/2> 0.237~44> 6115~135 H C194R-H> 0.242~49> 3125~145 EH C194R-EH> 0.247~51> 2135~150 SH C194R-SH> 0.249~53-140~155 ESH C194R-ESH> 0.251~56-145~160红铜(Copper) 特性及规格一览表：(1)化学成份(Chemical Composition)合金编号化学成份(wt.%)Material Designation Cu PJIS C1100(ETP)C1200(DLP)C1220(DHP)99.9(min)99.9(min)99.9(min)-0.004~0.0120.015~0.040(2)物理特性(Physical Properties)(3)机械性质(Mechanical Properties)磷青铜(Phosphor Bronze)合金各规格对照表规格名称SPEC 合金编号Alloy No.化学成分Chemical Composition (wt.%)规格编号Spec no.Cu Sn P Fe Ni Pb Zn OthersISO CuSn 4Rem.3.5~4.50.01~0.40≦0.1≦0.3≦0.05≦0.3----427 CuSn 5 4.5~5.5CuSn 6 5.5~7.5CuSn 87.5~9.0CNS C5101Rem.3.0~5.50.03~0.35----------------Cu＋Sn＋P≧99.59503H3112 C5191 5.5~7.0C52127.0~9.0JIS C5111Rem.3.5~4.50.03~0.35----------------Cu＋Sn＋P≧99.5H3110 C5102 4.5~5.5C5191 5.5~7.0C52127.0~9.0C52107.0~9.0≦0.1----≦0.05≦0.2Cu＋Sn＋P≧99.7H3130ASTM C51100Rem.3.5~4.90.03~0.35≦0.1----≦0.05≦0.3----B103 C51000 4.2~5.8C51900 5.0~7.0C521007.0~9.0≦0.2DIN CuSn 4Rem.3.5~4.50.01~0.35≦0.1≦0.3≦0.05≦0.3≦0.217662 CuSn 6 5.5~7.5CuSn 87.5~8.5BS PB101Rem.3.5~4.50.02~0.40--------≦0.02≦0.3----2870 PB102 4.5~5.5PB103 5.5~7.5铜合金板材厚度公差(Thickness tolerances for strip):红铜(C1100、C1200、C1220)黄铜(C2600、C2680、C2801)磷青铜(C2600、C2680、C2801)特殊铜合金(C194)over 0.70 mm to 0.90 mm incl.±0.035 mm±0.060 mm±0.015 mmover 0.90 mm to 1.20 mm incl.±0.040 mm±0.070 mm±0.020 mmover 1.20 mm to 1.50 mm incl.±0.045 mm±0.080 mm±0.025 mmover 1.50 mm to 2.00 mm incl.±0.050 mm±0.090 mm±0.025 mm 铜合金板材宽度公差(Width tolerances for strip):宽度Width厚度Thickness 厚度公差ToleranceJIS Standard (H3100)S&T≦100 mm≦200 mm≦100 mm≦200 mm0.10 ~ 0.55 mm.±0.10 mm±0.20 mm±0.05 mm±0.10 mm0.55 ~ 2.00mm.±0.20 mm±0.30 mm±0.10 mm±0.20 mm 铜合金板材蛇弯度公差(Permissible max. value on camber):宽度Width公差Tolerance (per 1000 mm)over 6 mm to 9 mm inc9 mm max.over 9 mm to 13 mm incl. 6 mm max.over 13 mm to 25 mm incl. 4 mm max.over 25 mm to 50 mm incl. 3 mm max.over 50 mm to 100 mm incl. 2 mm max.over 100 mm 1 mm max.* Dimensional tolerances shall be in accordance with JIS H3100。

黄铜跟磷铜有什么区别？哪个比较贵？相关性能和了解更多加工性能可以百度绿兴金属找到我们。

1.组成不同:黄铜是由铜和锌所组成的合金,黄铜分为普通黄铜和特殊黄铜两种，如果只是由铜、锌组成的黄铜就叫作普通黄铜。

如果是由二种以上的元素组成的多种合金就称为特殊黄铜,特殊黄铜又叫特种黄铜。

它强度高、硬度大、耐化学腐蚀性强，还有切削加工的机械性能也较突出。

磷铜又叫青铜，是铜锡合金，在铜里边加3~5%的锡和0.03~0.3的磷，可以大大改善铜的强度和韧性。

2.颜色不同:黄铜是金黄色的、磷铜是褐色的、铍铜是幻白色、紫铜是有带点紫色的。

3.硬度不同：磷铜弹性好硬度强点，黄铜韧性好，特种黄铜。

它强度高、硬度大、耐化学腐蚀性强，还有切削加工的机械性能也较突出。

4.用途不同:（1）由黄铜所拉成的无缝铜管，质软、耐磨性能强。

黄铜无缝管可用于热交换器和冷凝器、低温管路、海底运输管。

制造板料、条材、棒材、管材，铸造零件等。

含铜在62%～68%，塑性强，制造耐压设备等。

在工业和民用上，根据不同的使用特点来选用不同的材料。

如做电线,要求较柔软，用紫铜，如做联接件，上螺丝的地方多选用黄铜，多数黄铜具有良好色泽、加工性、延展性，易于电镀或涂装。

（2）锡青铜的铸造性能、减摩性能好和机械性能好，适合於制造轴承、蜗轮、齿轮。

铅青铜是现代发动机和磨床广泛使用的轴承材料。

铝青铜强度高，耐磨性和耐蚀性好，用於铸造高载荷的齿轮、轴套、船用螺旋桨等。

铍青铜和磷青铜的弹性极限高，导电性好，适於制造精密弹簧和电接触元件，铍青铜还用来制造煤矿、油库等使用的无火花工具。

5.性质不同，生产方法不同，自然界含量不同，需求量不同。

磷青铜和黄铜的价格也不同，一般磷铜还会比黄铜贵。

黄铜是由铜和锌所组成的合金，黄铜有较强的耐磨性能。

黄铜分为普通黄铜和特殊黄铜两种，如果只是由铜、锌组成的黄铜就叫作普通黄铜。

如果是由二种以上的元素组成的多种合金就称为特殊黄铜。

特殊黄铜又叫特种黄铜，它强度高、硬度大、耐化学腐蚀性强。

如何用肉眼或简易工具识别黄铜与磷青铜材料的技术方法？
当今时代市面上大家都有使用到科技产品(例如:手机或平板电脑);然而使用的科技产品必须要用到关键材料传输信号用的端子导体金属材料(例如手机用到充电数据线中的连接器);而金属导体材料种类多样，功能作用形式不一;通常消费型电子产品中用传输信号或传输电流用到的上黄铜和磷青铜的材料，在没有检测设备的情况下怎么用肉眼方法识别判断用的是黄铜与磷青铜材料呢？今天小编就给大家带来如何一项如何识别判别黄铜与磷青铜的首创简便技术供大家参考借鉴:
1.黄铜是由铜与锌成分组成的，其最大的特点外观颜色是黄色，而磷青铜是由铜与锡和磷(P)组成的，我们学过化学都知道磷(P)元素是呈红颜色的，因此磷青铜的最大外观特点是呈红颜色。

因此我们就可以利用其特性进行识别:
2.我们使用到的科技产品(如手机要用到的充电数据线传信号及电流的连接器端子导体金属材料识别其用的是黄铜还是磷青铜)，因手机用到的充电器数据线中的导体金属有经过电镀表面处理，这时我们将充电器数据线解剖把传输信号或电流的连接器端子金属件解剖开来，然后用刀片将其端子的金属表面的镀层刮掉，如果刮掉镀层后显示黄色的话就是黄铜，如果是呈红色就是磷青铜。

因手机充电器的数据线的连接器端子结构很小，如果用肉眼看到不是很明显的话可以用手机拍照功能放大一下看就很明显了，如果放在显微镜的看就更清楚了。

以下是黄铜的解剖端子(红色圈起部位将端子金属上镀层刮掉后呈黄颜色)示意图举例:
以下为磷青铜的解剖端子(红色圈起部位将端子金属的镀层刮掉后呈红颜色)示意图举例。

黄铜、磷铜、紫铜的使用区别是什么？
黄铜，比较耐腐蚀，有一定的塑形变形能力而不会毁损，我们常见的有黄铜做的水龙头，它耐腐蚀嘛。

还有，很多轴套也由黄铜制成，因为有少量塑性变形，不影响使用。

磷铜，耐腐蚀，冲击时候无火花，弹性非常好。

所以，我们用的插座，如果是质量好的插座，里面的弹片，多半是磷铜啦。

方便多次，成千上万次拔出插入插头啊。

紫铜，相当于纯铜（不完全是），延展性和导电性都相当不错，所以，经常被作为电缆的芯。

延展性方面也有应用，就是比较软，而且又重，用铜棒敲击东西能不损坏东西的表面，而又能传递过力量，在安装的时候，我们经常会用紫铜垫在大锤和要打击的物体之间，确保物体不被打坏外部轮廓。

各种铜合金的硬度表铜合金作为一种常见的金属材料，具有较好的导电性和导热性，广泛用于工业制造、建筑装饰、航空航天等领域。

不同的铜合金具有不同的硬度，下面将介绍几种常见的铜合金及其硬度特点。

一、黄铜黄铜是由铜和锌组成的合金，具有良好的加工性能和机械性能。

黄铜的硬度一般在80-120HB之间，具有较好的可塑性和韧性，适用于制作各种零件和装饰品。

黄铜的硬度可根据不同的合金比例进行调整，如含锌量较高的锌黄铜硬度较低，含锌量较低的黄铜硬度较高。

二、磷青铜磷青铜是由铜、锡和磷组成的合金，具有较高的强度和耐磨性。

磷青铜的硬度一般在140-180HB之间，比黄铜稍硬。

磷青铜具有良好的耐腐蚀性和耐磨性，适用于制作轴承、齿轮等零件。

三、铝青铜铝青铜是由铜、铝和其他元素组成的合金，具有较高的强度和耐蚀性。

铝青铜的硬度一般在150-220HB之间，比黄铜和磷青铜都要硬。

铝青铜具有良好的耐热性和耐腐蚀性，适用于制作船舶零件、化工设备等。

四、铝硅青铜铝硅青铜是由铜、铝、硅和其他元素组成的合金，具有较高的强度和耐腐蚀性。

铝硅青铜的硬度一般在180-240HB之间，比铝青铜稍硬。

铝硅青铜具有良好的耐磨性和耐蚀性，适用于制作汽车零件、机械零件等。

五、铝锰青铜铝锰青铜是由铜、铝、锰和其他元素组成的合金，具有较高的强度和硬度。

铝锰青铜的硬度一般在200-260HB之间，比铝硅青铜稍硬。

铝锰青铜具有较好的耐磨性和耐蚀性，适用于制作摩擦片、齿轮等零件。

六、铝镍青铜铝镍青铜是由铜、铝、镍和其他元素组成的合金，具有较高的强度和硬度。

铝镍青铜的硬度一般在220-280HB之间，比铝锰青铜稍硬。

铝镍青铜具有较好的耐磨性和耐蚀性，适用于制作摩擦片、齿轮等零件。

总结：不同种类的铜合金具有不同的硬度特点，根据不同的应用需求选择合适的铜合金材料可以提高制品的质量和使用寿命。

在实际应用中，还需要考虑到铜合金的其他性能指标，如耐蚀性、导电性等，综合考虑选择最适合的材料。

磷铜和紫铜看起来是一样，价格却差几千
最近收了一批金球球-磷铜球，刚好在高价的时候收的，过了没几天，铜就开始掉价，那几天掉得很吓人，一天两千两千的掉。

放在仓库心惊胆战啊，现在终于开始涨价了，那啥是磷铜呢？磷铜是由青铜加了脱气剂磷、锡和其他微量元素，例如铁、锌等组成的金属原材料。

磷铜的延展性和耐疲劳性都比较好，可靠度高于一般铜合金，是一种很好的电气及机械材料。

随着电子技术的飞速发展，各种电路板的生产需求量迅速增大。

而铜作为电镀阳极的重要原料，需求量也随着增大，其中PCB精密电路板则需要用磷铜球作为阳极。

磷铜球适用于电子线路板，尤其是高精尖的多层线路板这种电子产品必不可少的重要组件，非常依赖优质PCB磷铜球阳极作为制造线路板的基础原材料。

因此磷铜阳极球的需求量颇为可观。

磷铜回收要怎么去辨别？这个磷铜球看起来是和紫铜一样的，颜色都是紫红色，外表没有明显区别。

紫铜：含铜量可达到99%又称纯铜，紫铜现在回收价格5万多左右。

磷铜，添加了磷的铜，磷铜价格6万左右。

因为两者外观一致，性质相似，只能通过光谱仪来检测。

以后遇到铜的老铁要分清啊，紫铜和磷铜一吨价格就差几千了。

铜的种类与区分有很多人都认为.铜.就是只有一种.它就是唯一.但其实还有其他不同种类的铜的.比如合金铜.下面就慢慢的介绍吧.一、纯铜纯铜是玫瑰红色金属，表面形成氧化铜膜后呈紫色，故工业纯铜常称紫铜或电解铜。

密度为8~9g/cm?，熔点1083℃.纯铜导电性很好，大量用于制造电线、电缆、电刷等；导热性好，常用来制造须防磁性干扰的磁学仪器、仪表，如罗盘、航空仪表等；塑性极好，易于热压和冷力加工，可制成管、棒、线、条、带、板、箔、等铜材。

纯铜产品有冶炼品及加工品两种。

二、铜合金1.黄铜黄铜是铜及锌的合金。

最简单的黄铜是铜、锌二元合金，称为简单黄铜或普通黄铜。

改变黄铜中锌的含量可以得到不同机械性能的黄铜。

黄铜中锌的含量越高，其强度也较高，塑性较低。

工业中采用的黄铜含锌量不超过45%，含锌量再高将会产生脆性，是合金性能变坏。

为了改善黄铜的某种性能，在一元黄铜的基础上加入其他合金元素的黄铜称为特殊黄铜。

常用的合金元素有硅、铝、锡、铅、锰、铁与镍等。

在黄铜中加铝能提高黄铜的屈服强度和抗腐蚀性，稍降低塑性。

含铝小于4%的黄铜具有良好的加工、铸造等综合性能。

在黄铜中加入1%的锡能显着改善黄铜的抗海水和海洋大气腐蚀的能力，因此成为“海军黄铜”。

锡还能改善黄铜的切削加工性能。

黄铜加铅的主要目的是改善切削加工性和提高耐磨性，铅对黄铜的强度影响不大。

锰黄铜具有良好的机械性能、热稳定性和抗蚀性；在锰黄铜中加铝，还可以改善它的性能，得到表面光洁的铸件。

黄铜可分为铸造和压力加工两类产品。

2.青铜青铜是历史上应用最早的一种合金，原指铜锡合金，因颜色呈青灰色，故称青铜。

为了改善合金的工艺性能和机械性能，大部分青铜内还加入其他合金元素，如铅、锌、磷等。

由于锡是一种稀缺元素，所以工业上还是用许多不含锡的无锡青铜，他们不仅价格便宜，还具有所需要的特殊性能。

无锡青铜主要有铝青铜、铍青铜、锰青铜、硅青铜等。

此外还有成分较为复杂的三元或四元青铜。