聚合物稳定与降解（Polymer stability and degradation）The first chapter, introduction1. the concept of aging (degradation)The storage, processing and use of polymer materials in the process of chemical properties, physical and mechanical properties will gradually become worse, known as aging or degradation. P1Characteristic：The inevitable, irreversible process.The relatively short time scale.2. factors that lead to the degradation of the polymer(a) internalThe composition and structure of A. polymer chain.(1) different composition and degradation of different(2) the activity may be the main cause of the degradation of the matrix(3) the active hydrogen is more likely to be seized(4) head to head (tail tail) structure of polyolefin are more likely to become active points.(5) the effect of molecular weight change: changes in the structure of the molecular weight of the internal rules increases, causing stability. On the contrary, if the irregular structure is reduced, increased stability.(6) effects of the molecular weight distribution: down a wide molecular weight distribution and stability.(7) the degree of branching effect: the degree of branching increases, the weak link in the molecular chain also increased, more prone to degradation.The aggregation state of B. polymersThe stability of amorphous polymer material less than crystalline polymer materialsThe reason: amorphous materials (low density polymer chain irregular arrangement), easy to be oxygen, water, chemical infiltration, degradation.3. impurities in polymersIn the two kinds of polymer impurity:(1) a small amount of impurities mixed in the process of the inevitable;(2) additive.Most of the impurities will accelerate the degradation of polymers.(two) external causes:Effects of A. heat, temperature and heat and oxygen: heat the polymer chain scission, the formation of free radicals (reversible, bidirectional) hot oxygen polymer crosslinking or degradation of the material performance decline.Effect of B. lightEffect of C. oxygen and ozone oxygen to polymer degradation in heat and light effect. The ozone of unsaturated bond (such as rubber) the damage is very serious.Effect of D. water and damp of water dissolving and extraction of components; hydrolysis and chain scission.Effect of E. and other factors: the effect of microorganism; other organisms; effects of various process factors. Often a variety of external synergy.The second chapter, the basic principle of polymer degradation and stability.(a) the type of thermal degradationDepolymerization; random chain scission reaction; small molecular chain breaking elimination reaction;Features: simple caused by heat, no oxygen in.1. the depolymerization reaction (zipper degradation)The depolymerization began or weak molecular chain end point. Only product: monomer.Characteristic：(1) the early change of molecular weight polymer small, great mass loss;(2) to the degradation of polymer quality almost completely lost when the polymer relative molecular weight decreased dramatically.2. random chain scission reaction -- almost all polycondensate and add substantial degradation of polymersIrregular polymer chain scission reaction; the main product is low molecular weight polymer.Characteristic：(1) the initial molecular weight decreased rapidly and the quality of the polymer basically unchanged;(2) degradation to later stage, a large number of low molecular volatile polymer mass quickly disappeared.3. small molecular backbone fracture elimination reactionPolymer degradation caused by the elimination of side groups; and finally caused the main chain scission and comprehensive degradation.Features: from any part of the molecular chain of random elimination(two), the mechanism of degradationThe thermal oxidative degradation of the polymer at a certain temperature and oxygen in the air and the degradation reaction.Auto oxidation is the main feature of thermal oxidative degradation, but also the core of degradation.[heat: Auto oxidation reaction at room temperature to 150 DEG C, thermal oxidation is auto catalytic characteristics in the typical free radical chain mechanism, the. ]Schematic diagram of the polymer thermal oxygen cycleThe polymer thermal oxygen cycle, which represents the thermal oxidation process automatically. Seen from the figure, with each cycle, an initial alkyl radical R - at least 3 into a R, alkyl radical concentration is more and more high, the reaction speed is more and more fast, the formation of auto oxidation reaction.The rate of oxidation1. when the concentration of oxygen concentration in the air reaches or higher, with the rate of R and oxygen is very fast, [R -] < [ROO.Therefore, ROO double dominant coupling termination. The initiation rate is equal to the suspension rate (to reach steady state), available at steady state concentration of ROO.The oxygen concentration is greater than or equal to the oxygen concentration in the air, the oxidation reaction rate and the concentration of oxygen;2. oxygen concentration is very low, [R]>>[ROO, the reaction rate of the oxidation reaction rate depends on R and oxygen.In R, the termination reaction coupling termination dominant base,The oxygen concentration is very low, the oxidation rate of oxygen concentration.(three) the classification and method of adding antioxidant.Two kinds of antioxidants:The main antioxidant (radical scavenger): free radical reaction and auto oxidation process, interrupt the chain reaction.Features: automatic change of oxidation process.The auxiliary antioxidant (preventive antioxidant): can produce automatic decomposition of the oxidation process of ROOH without generating free radicals.Features: only reduce the oxidation rate, does not change the auto oxidation process.Principle: the sooner the better polymer added antioxidants.The type and mechanism of A. primary antioxidantThe main antioxidant can be divided into: hydrogen donor; electron donor; free radical trapping; benzofuran ketones.Hydrogen donor: is the most common secondary aromatic amines and hindered phenolic antioxidant.2,6-di-tert-butyl-4-methylphenolThe electron donor of tertiary amine containing reactive functional group of N-HGenerally, they can be given, generating onium cation.Radical trapping body can capture free radicals, and the product will no longer trigger free radical chain reaction.Benzofuran ketone - dilute oxygen conditions, alkyl radical captureWith B. antioxidantUse a variety of antioxidants, there will be synergistic effect, additive effect and antagonistic effect.Synergy: 1+1>2Two (or more) with antioxidant effect, the sum of more than separately use effect. Can be divided into both synergistic effect and hybrid Association effect.[cases] are synergistic effects of two kinds of hindered phenol.Antagonistic effect: 1+1<2Two (or more) with antioxidant effect, to separately use effect.Additive effect: 1+1 = 2Antioxidants used alone or in conjunction with other antioxidant,The effect of the same.(four) initiation of carbonylThe Norrish type I reaction between carbonyl and alpha carbon atoms bond cleavage.The Norrish type II reaction: only occurred in the gamma ketocarbonyl carbon atoms, at least one hydrogen atom under the condition can occur at room temperature.The Norrish type III reaction: through transfer of beta hydrogen atoms and C - C bond cleavage near the carbonyl side, the formation of aldehydes and alkenes.(five) stabilized light degradation and light degradation of oxygenA commonly used type of light stabilizer: light shielding agent; UV absorber; quenching agent; hindered amine light stabilizerThe 1. light shielding agentThe reflection or absorption of light at the polymer surface, or reduce the amount of transmission to the polymer, the main physical stabilization method.(1) surface protection agent: on the surface of polymer materials for coating or plating metal film protection.(2): carbon black pigment is the most effective light shielding agent.2. UV absorbersA kind of light stabilizer and most strongly and selectively absorb ultraviolet light, with low-energy radiation heat or harmless way to release energy.(1) two o-hydroxyl benzophenone UV absorber is the most importantCarbonyl ortho must contain a hydroxyl group to form hydrogen bonds through the chelate ring, keto enol tautomerism and to absorb and release energy. The intramolecular hydrogen bond strength is greater, more conducive to the process of tautomerism.No ortho hydroxy carbonyl when the compounds become photosensitizer.Six. The reaction of ozone with rubber- double bond addition reactionOzone cracking: the destruction of the ozone stress on the rubber, causing cracking in the direction perpendicular to the stress direction.Crack: rubber cracking caused by oxidative degradation.Seven. Biodegradable polymersNatural polymers are biodegradable, relatively natural polymer, synthetic polymer is difficult to be biodegraded.The third chapterA polyolefin.The structure of the polyolefin and polymer degradation and stability.The thermal stability of various key and group respectively:The thermal stability of order polyolefin as follows: polyethylene polypropylene polyisobutylene > >Main order: Polyolefin oxidation stability of high density polyethylene and low density polyethylene polypropylene > >Two PVC.The thermal stability of PVC is poor, without the stabilizer, cannot be processed into products by melting method.The thermal degradation of PVC 1.(1) the characteristics of degradation of PVC: the release of HCl -- the typical features; the presence of oxygen, accelerated degradation.The mechanism of HCl decomposition 2.PVC:(I) free radical mechanism: (II) ion molecule mechanism: (III) molecular mechanism:The photodegradation of PVC 3.PVC degradation and crosslinking during UV irradiation, the production of conjugated polyene and hydrogen chloride.The fourth chapterThe factors that cause a degradation in the processing andMechanical force, temperature, oxygen, water and other medium, such as trace metal impuritiesThe evaluation method of degradation and stabilization of polymer processing, twoAccording to the processing before and after processing (after different time or several times after processing) a performance test of polymer compared to make a judgment on the polymer degradation degree or stability.OneThe melt flow rate method. 2. the determination of relative molecular mass and its distribution. 3. rheological method. 4. yellow indexTwo. The degradation of PVC in the machining process1. the characteristics of degradation of PVCViscous flow temperature (160 to 212 DEG C) > the decomposition temperature (170 C)De HClThe dark - conjugated polymerThe molecular structure of polyene and intramolecular cyclization - polymer crosslinking and viscosity increase and the decrease of fluidityThe role of oxygen leads to removal of HCl increased;With polyene structure reaction, delay PVC color.Three. The influencing factors of the stability of PVC processingThe performance of the 1. polymer itself: molecular weight; particle morphology of resinInfluence of 2. factors on the degradation of PVC formula in the process ofCan reduce the viscosity of polymer melt.To improve the liquidity, reducing agent -- polymer degradation of PVC in the process of riskTo improve the processing of - PVCThe fifth chapterA polymer stabilizer.1. kinds of polymer stabilizersHeat stabilizer; light stabilizer; antioxidant capacity; chemical stabilizer; fungicideTwo. The mechanism of heat stabilizer1. preventive effect: to prevent the dehydrochlorination reaction, or at least can postpone the reaction.(1) the absorption of HCl, inhibit the auto catalytic role: metal carboxylate, organic tin mercaptide, epoxidized fatty acid esters(2) the replacement of labile chlorine atoms in the molecule of PVC, such as allylic chlorine or a chlorine atom of tertiary carbon, eliminate the trigger: metal soap, organic tin(3) to capture free radicals, prevent the auto oxidation of phenolic antioxidants:2. passivation effect: heat stabilizer can shorten the polyene sequence structure, and can form the PVC damage in the process of heating the carbon onium salt.Only organic tin stabilizer with thiol passivation and prevention functionThree types of heat stabilizers.1. lead heat stabilizer stabilizer2. organic tin stabilizer3. metal carboxylate stabilizer4. other metal stabilizer5.metal free 6. auxiliary stabilizerThe sixth chapterProcessing technology of waste plasticsThe establishment of waste plastics recycling system is feasible to eliminate environmental pollution and ensure waste plastic recycling.The main way of waste plastics recycling1. mechanical regenerationSimple regenerationAdvantages: economical and feasibleDisadvantages: requires relatively clean waste; high separation technology; end use markets products co.;Belongs to labor-intensive processing2. modified regenerationAdvantages: the mechanical property of the product is improved, can be recycled products of high gradeDisadvantages: process is complicated and some specific equipment3.: depolymerization is an advanced technology with the rapid development of recycling4. pyrolysis and gasificationAdvantages: pyrolysis can handle all can not be treated by other ways of waste plastics,Liquefaction condition can be selectedWithout the prior separation of plastic, also do not need to remove the impuritiesDisadvantages: gasification process General requirements for harsh conditionsThe pyrolysis liquid products need to be purified to more hydrocarbon components5. burningAdvantages: energy, fuelDisadvantages: exhaust pollution6. landfillAdvantages: simpleDisadvantages: loss of all available energy; space; exudate pollution; waste plastic refractory; huge investmentThe seventh chapterThe combustion characteristics of polymer materials.1. heat temperature of2.3. high flame burning speed of4. burning poisons released5. in the combustion will produce deformation, softening, melting and dropping phenomenon, which has a great influence on the combustion state, often cause the spread of fire, which makes it difficult to fire.Two. The combustion process of polymer materials3. fire by properties of materials are as follows 1. decomposition of the heating and melting heat: 2. flash temperature, autoignition temperature, limit oxygen index4. burningNet heat of combustion to combustion >0Net heat of combustion <0 stop burning5. flame propagationThree. Combustion process of polymers1. in the combustion of organic matter, the first thermal oxidation degradation reaction of polymer chain, long chain rapid collapse, liquid or solid organic materials into combustible gas (hydrocarbon),Combustion is a free radical chain reaction of 2. small molecule hydrocarbon, eventually forming carbon dioxide and water.3. polymer combustion, the main fuel is hydrogen, instead of carbon; in the polymer structure as the hydrogen molecule from substitutionThe key is to capture the 4. flame retardant free radical and free radical resistance and low energy. The combustion of PVC leaving the fire extinguish, because it generates hydrogen chloride can capture free radicals in the cleavage process.Four. Flame retardant agent and flame retardant mechanism1. basic options: (1) the polymer itself has a certain flame retardance (2) combustion velocity is relatively small(3) (4) good heat resistance and flame retardant filler, good compatibility2. flame retardant flame retardantThe endothermic effect covering effect of dilution effectThe inhibitory effect of enhancement effect3. as a flame retardant with four service conditions:(1) flame retardant is not flammable or low flammable material.(2) have good dispersion in polymer materials.(3) cannot be destroyed by the physical properties of flame retardant material. (4) flame retardant itself or under combustion conditions do not release toxic gases4. kinds of flame retardantsAdd type* easy to use, wide application range,* but there is a certain impact on the performance of polymer,* mainly used in polyethylene, polypropylene, polyvinyl chloride and polystyrene resin.* such as chlorinated paraffin, four Bromethyl, aluminium hydroxide and magnesium hydroxide etc..Reaction type* as a monomer in polymerization, the polymer with flame retardant properties.* operation and processing complex* four phthalic anhydride and two bromine chloride four bisphenol A is a reactive flame retardant.* for the polycondensation reaction, such as polyurethane, unsaturated polyester, epoxy resin, polycarbonate, etc..5. flame retardant mechanism of flame retardantDifferent flame retardant, the flame retardant mechanism is different, but the overall physical effect and chemical effect of.- physical effects of dilution of combustible materials, heat effect and air isolation effect;Chemical interaction in carbonation, eliminate free radicals and phosphorus acylation.The stability and degradation of the eighth chapter of medical polymer materialsOneBiomedical materials can be divided into three categories: medical metal materials, medical ceramic materials and medical polymer materials2.. Various factors in vivo degradation:* after a large number of studies show that the release of inflammatory cells (enzymes and enzyme hydrolase) and oxidant (O2 *, H2O2, OH), acidic substances (such as fatty acids) and substances in body fluids (Ca2+, phospholipid, cholesterol) constitute environmental degradation.* all non endothelialization surfaces of synthetic materialsstimulate certain levels of immune response in vivo, such as inflammatory reactions, and therefore all materials in the body are degraded.* the inflammatory response of the material depends on the interaction of the material surface with the protein in the body fluid. The adsorption and denaturation of the protein is the cause of the biological response to the cell and material interface.3. natural materials: gelatin, chitosan, cellulose, protein, natural coralDegradation of 4.PCL5. polylactic acid (PLA)direct methodThe relative molecular weight of polylactic acid produced by the method is less than 4000, and the strength is low, so the practicability is not strong.indirect method* first, DL- lactic acid was prepared by condensation polymerization with ZnO powder as catalyst* polylactic acid was synthesized by vacuum polymerization under the high temperature with ZnO as catalyst. The synthesized PLA has a molecular weight of 7.3 * 1046. tissue engineeringThe relationship between structure of mammalian tissues using the principle and method of engineering and life sciences to understand the normal and pathological features, biological tissue substitutes and development of live, used to repair, maintain and improve the function of human body.Three major elements of tissue engineering (1)Cell carrier materialThe separation of the cells themselves may not form the organization, they need temporary support material growth, the three-dimensional simulation of the natural counterpart, often in the extracellular matrix, which plays a physical support role, and adhesive substance cell loading in vitro and late implantationThree major elements of tissue engineering (two)Isolation and culture of cellsIndividual cells were collected from healthy parts of the donor tissue and isolated and then transplanted to the site needed by the patient.Three major elements of tissue engineering (three)Cell growth factorIn tissue and organ regeneration, various tissue inducing factors, growth factors and angiogenesis stimulating factors are beneficial to the formation of tissue, but it can not be implanted directly into the body.。
