强度硬度换算表

洛⽒硬度HRB、HRA与其它硬度、强度换算关系表1返回⽬录附录⼆洛⽒硬度与其它硬度、强度换算表-1(摘⾃GB/T1172-1999)洛⽒硬度布⽒硬度F/D2=30HRC HRA HBS HBW 维⽒硬度HV强度（近似值）MPab/σ20 60.2 225 226 77421 60.7 229 230 79322 61.2 234 235 81323 61.7 240 241 83324 62.2 245 247 85425 62.8 251 253 87526 63.3 257 259 89727 63.8 263 266 91928 64.3 269 273 94229 64.8 276 280 96530 65.3 283 288 98931 65.8 291 296 101432 66.4 298 304 103933 66.9 306 313 106534 67.4 314 321 109235 67.9 323 331 111936 68.4 332 340 114737 69.0 341 350 117738 69.5 350 360 120739 70.0 360 371 123840 70.5 370 370 381 127141 71.1 380 381 393 130542 71.6 391 392 404 134043 72.1 401 403 416 137844 72.6 413 415 428 141745 73.2 424 428 441 145946 73.7 436 441 454 150347 74.2 449 455 468 155048 74.7 470 482 160049 75.3 486 497 165350 75.8 502 512 171051 76.3 518 52752 76.9 535 54453 77.4 552 56154 77.9 569 57855 78.5 585 59656 79.0 601 615 57 79.5 616 635 58 80.1 628 655 59 80.6 639 676 60 81.2647698 61 81.7 721 62 82.2 745 63 82.8 770 64 83.3 795 65 83.9 822 66 84.4 850 67 85.0 879 68 85.5 909注：1. 本表适⽤于包括碳钢、合⾦钢（铬钢、铬钒钢、铬镍钢、铬钼钢、铬镍钼钢、铬锰硅钢、超⾼强度钢、不锈钢等）系列中含炭量由低到⾼的主要钢种。

一、硬度与抗拉强度的关系
当钢的硬度在500HB以下时，其抗拉强度与硬度成正比，kg/m㎡（óB）=1/3 X HB=3.2 X HRC=2.1 X HS,但上述关系式也并非在什么场合都成立，从热处理方面说，回火温度低时，kg/m㎡与HRC时的相关关系便可能被破坏，钢的回火温度，硬度和抗拉强度的关系如图所示。

由此图可见硬度随回火温度的升高而下降，但在淬火状态以及300℃以下低温回火时，硬度与抗拉强度的关系难以成立。

当回火温度在300℃左右时，kg/m ㎡与HRC具有相关关系，即硬度高，抗拉强度就高；硬度低，抗拉强度就低。

在低温回火状态欲求出kg/m㎡值是很困难的，因为此时抗拉强度值分布很离散。

由于低温回火件的kg/m㎡不稳定而不能确定，故在日本工业标准（JIS）中也是通试验来测定400℃以上温度回火件的拉伸特性（也有300℃回火工件）。

换言之是只对调质件（淬火+400℃回火）进行拉伸试验。

在工业上只是在要求抗旋转弯曲疲劳和抗磨损时才使用低温回火件。

高频淬火和渗碳淬火即为此适用例。

受拉应力的零件不采用低温回火。

不过在低碳钢中，但淬火M能发生自回火(故Ms点高)时，亦有在淬火状态下使用者。

低碳钢的板条马氏体组织结构自回火，正可在工业上应用，但此时必须考虑淬透性和质量效应（必要时应添加B、Cr、Mn等金属元素）。

二、钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表
如果您要查的抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC，请查本表。

1２Cr1MoV合金结构钢力学性能：抗拉强度》490屈服强度》245伸长率》22%断面收缩率》50%冲击功》71（均为标准单位）热处理规范：淬火970度，空冷，回火750度，空冷，。

金相组织：铁素体+贝氏体用途：是高压及超高压、亚临界电站锅炉过热器、集箱和主蒸气导管广泛应用的钢种。

580度仍具有高强度和高的抗氧化性，有较高的持久塑性。

生产工艺简单，焊接性能良好，但对正火冷却速度较敏感，580度长期使用会造成珠光体球化。

牌号：15CrMo标准：GB/T3077-1988●特性及适用范围：有良好的工艺性能和焊接性能，在500～550℃下有较高的持久强度。

温度超过550℃时，抗氧化性能变差，蠕变强度显着降低。

长期处在500～550℃时，钢的热强性降低，强度降低。

用于制造510℃的高、中压蒸气导管、集箱以及管壁温度为550℃的过热器及锻件。

●化学成份：碳C：0.12～0.18硅Si：0.17～0.37锰Mn：0.40～0.70硫S：允许残余含量≤0.035磷P：允许残余含量≤0.035铬Cr：0.80～1.10镍Ni：允许残余含量≤0.030铜Cu：允许残余含量≤0.030钼Mo：0.40～0.55●力学性能：抗拉强度σb(MPa)：≥440(45)屈服强度σs(MPa)：≥295(30)伸长率δ5(％)：≥22断面收缩率ψ(％)：≥60冲击功Akv(J)：≥94冲击韧性值αkv(J/cm2)：≥118(12)硬度：≤179HB试样尺寸：试样毛坯尺寸为30mm●热处理规范及金相组织：热处理规范：淬火900℃,空冷;回火650℃,空冷。

金相组织：铁素体+珠光体+少量贝氏体●交货状态：以热处理（正火、退火或高温回火）或不热处理状态交货，交货状态应在合同中注明。

材质（锻件）热处理抗拉强度（MPa）屈服强度(MPa)35CrMo调质（纵向）73554035CrMo调质（切向）63044045调质（纵向）630370Q235-A(纵向)330230材质（非锻件）热处理抗拉强度（MPa）屈服强度（MPa）35CrMo980835 45600355Q235-A375-500205金属硬密封的[wiki]阀门[/wiki]都会考虑到密封面硬度值，而阀门硬度值现在基本上是以洛氏硬度（HRA/HRC)来表示的，最近碰到很多人都说进口阀门的密封面硬度可以超过HRC70，还有些卖进口阀门的说自己卖的阀门硬度值可以达到HRC71,HRC72的，更有甚者连设计院的人都替进口阀门吹嘘说进口阀门的密封面硬度值可以达到HRC72。

各种硬度及强度的换算1.努氏硬度与维氏硬度的换算(1)以相同硬度的物体对努氏维氏两种压头具有相等的抗力为依据，分别对维氏努氏两种压头在加载荷下的应力进行推导，再根据σHK=σHV得出：HV=0.968HK本公式是在低载荷下测得，误差比较大。

此外在硬度值大于HV900时此公式误差很大，失去参考价值。

(2)经过推导与修正提出努氏硬度与维氏硬度的换算公式为经实际数据验证，该公式的最大相对换算误差为0.75%，具有较高的参考价值。

2.洛氏硬度与维氏硬度的换算(1)对Hans·Qvarnstorm提出的The Qvarnstorm换算公式：进行修正后得出洛氏硬度与维氏硬度的换算公式为：此公式用我国公布的黑色金属硬度标准数据进行换算，其HRC误差基本上在±0.4 HRC 范围内，其最大误差也仅士0.9HRC，计算的HV误差最大为±15HV。

(2)根据不同压头所受应力σHRC=σHV，通过对洛氏硬度与维氏硬度压痕深度关系曲线的分析得出公式本公式与国家标准实验换算值对照,换算式计算结果与标准实验值之误差为±0.1HRC。

(3)根据实际的实验数据利用线性回归的方法对洛氏硬度与维氏硬度的换算进行探讨，得出公式：本公式使用范围小，误差较大，但计算简便，在对精度要求不高时可以使用。

3.洛氏硬度与布氏硬度的换算(1)对布氏压痕和洛氏压痕深度关系进行分析，根据压头的应力σHRC =σHB得出换算公式计算结果与国家标准实验值对照，换算式计算结果与标准实验值之误差为±0.1HRC。

(2)根据实际实验数据用线性回归法得到公式公式误差偏大，使用范围偏小，但计算简便，在对精度要求不高的情况下可以使用。

4.布氏硬度与维氏硬度的换算布氏硬度与维氏硬度的关系，同样根据σHB=σHV得出公式此公式换算结果与国家标准换算值对照，换算误差为±2HV。

5.努氏硬度与洛氏硬度的换算因为努氏硬度与洛氏硬度的对应曲线类似于抛物线[7]，故由曲线得出近似的换算公式为此公式比较精确，可以作为使用参考。

硬度表示材料抵抗硬物体压入其表面的能力。

它是金属材料的重要性能指标之一。

一般硬度越高，耐磨性越好。

常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。

1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。

2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。

它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。

根据试验材料硬度的不同，分三种不同的标度来表示：∙HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。

∙HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。

∙HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。

3 维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。

邵氏硬度（HA）邵氏硬度专用在橡胶方面的硬度测试做橡胶的应该知道怎么测邵氏硬度（HA）用于橡胶、塑料等材料的硬度测定，将一定形状的钢制压针，在试验力作用下压入试样表面，当压足平面与试样表面紧密贴合时，测量压针相对压足平面的伸出长度。

通过公式计算出邵氏硬度值。

具有结构简单、使用方便、型小体轻、读数直观等特点。

A型参数：刻度盘值：0-100HA；压针行程范围：0—2.5mm；压针端部压力：0.055N-8.05N；压针顶端直径：Φ0.79mm+\-0.03m m。

黑色金属硬度及强度换算表硬度抗拉强度（公斤/毫米2）洛氏表面洛氏维氏 布氏碳钢 铬钢 铬钒钢 铬镍钢 铬钼钢 铬镍 钼钢 铬锰硅钢 超高强度钢不锈钢 不分 钢种 HRC HRA H R15N H R30N H R45N HV HB30D 2(70.0) 86.6 1037 本栏适用二换算精度要求不高的一般钢种(69.5) 86.3 1017 (69.0) 86.1 997 (68.5) 85.8 978 (68.0) 85.5 959 (67.5) 85.2 941 67.0 85.0 923 66.5 84.7 90666.0 84.4 889 65.5 84.1 872 65.0 83.9 92.2 81.3 71.7 856 64.5 83.6 92.1 81.0 71.2 840 64.0 83.3 91.9 80.6 70.6 825 63.5 83.1 91.8 80.2 70.1 810 63.0 82.8 91.7 79.8 69.5 795 62.5 82.5 91.5 79.4 69.0 780 62.0 82.2 91.4 79.0 68.4 766 61.5 82.0 91.2 78.6 67.9 752 61.0 81.7 91.0 78.1 67.3 739 60.5 81.4 90.8 77.7 66.8 726 60.0 81.2 90.6 77.3 66.2 713 269.1 260.7 59.5 80.9 90.4 76.9 65.6 700 262.3 255.1 59.0 80.6 90.2 76.5 65.1 688 255.8 249.6 58.5 80.3 90.0 76.1 64.5 676 249.6 244.3 58.0 80.1 89.8 75.6 63.9 664 243.7 239.1 57.5 79.8 89.6 75.2 63.4 653 238. 234.1 57.0 79.5 89.4 74.8 62.8 642 232.6 229.3 56.5 79.3 89.1 74.4 62.2 631 227.4 224.6 56.0 79.0 88.9 73.9 61.7 620 222.4 220.1 55.5 78.7 88.6 73.5 61.1 609217.7215.7 55.0 78.5 88.4 73.1 60.5 599 206.6 209.8 208.6 213.1 211.5 54.5 78.2 88.1 72.6 59.9 589 203.3 206.1 204.8 208.7 207.4 54.0 77.9 87.9 72.2 59.4 579 200.0 202.5 201.0 204.5 203.4 53.5 77.7 87.671.858.8570196.8 199.0197.4 200.5199.553.0 77.4 87.4 71.3 58.2 561 193.7 195.5 192.5 198.5 193.8 196.7 195.7 52.5 77.1 87.1 70.9 57.6 551 190.6 192.0 189.3 195.1 190.3 193.0 192.1 52.0 76.9 86.8 70.4 57.1 543 188.1 187.5 188.7 186.1 191.8 187.0 189.4 188.5 51.5 76.6 86.6 70.0 56.5 534 184.1 184.5 185.4 183.0 188.6 183.6 186.0 185.1 51.0 76.3 86.3 69.5 55.9 525 (501) 180.3 181.6 182.1 179.9 185.4 180.4 182.7 181.7 50.5 76.1 86.0 69.1 55.3 517 (494) 176.7 178.7 179.0 176.9 182.3 177.3 179.5 178.5硬度抗拉强度（公斤/毫米2）洛氏表面洛氏维氏布氏碳钢铬钢铬钒钢铬镍钢铬钼钢铬镍钼钢铬锰硅钢超高强度钢不锈钢不分钢种HRC H RA H R15N H R30N H R45N HV HB30D250.0 75.8 85.7 68.6 54.7 509 (488) 174.4 173.1 175.8 175.8 173.9 179.3 174.2 176.5 175.9 175.3 49.5 75.5 85.5 68.2 54.2 501 (481) 171.4 169.8 173.0 172.8 171.0 176.2 171.2 173.5 172.3 172.2 49.0 75.3 85.2 67.7 53.6 493 (474) 168.6 166.6 170.2 169.8 168.2 173.3 168.3 170.7 168.8 169.2 48.5 75.0 84.9 67.3 53.0 485 (468) 165.8 163.5 167.5 166.9 165.4 170.4 165.4 167.9 165.5 166.3 48.0 74.7 84.6 66.8 52.4 478 (461) 163.1 160.5 164.9 164.0 162.6 167.6 162.7 165.2 162.3 163.5 47.5 74.5 84.3 66.4 51.8 470 (455) 160.6 157.6 162.3 161.2 159.9 164.8 160.0 162.5 159.2 160.8 47.0 74.2 84.0 65.9 51.2 463 449 158.1 154.9 159.7 158.4 157.3 162.0 157.3 160.0 156.3 158.1 46.5 73.9 83.7 65.5 50.7 456 442 155.6 152.2 157.2 155.7 154.7 159.3 154.7 157.5 153.5 155.5 46.0 73.7 83.5 65.0 50.1 449 436 153.3 149.7 154.7 153.1 152.2 156.7 152.2 155.0 150.8 152.9 45.5 73.4 83.2 64.6 49.5 443 430 151.0 147.2 152.2 150.5 149.7 154.1 149.8 152.6 148.2 150.4 45.0 73.2 82.9 64.1 48.9 436 424 148.8 144.8 149.8 148.0 147.2 151.6 147.4 150.2 145.7 148.0 44.5 72.9 82.6 63.6 48.3 429 418 146.6 142.6 147.5 145.5 144.8 149.1 145.0 147.8 143.3 145.7 44.0 72.6 82.3 63.2 47.7 423 413 144.5 140.3 145.2 143.1 142.5 146.7 142.7 145.5 141.0 143.4 43.5 72.4 82.0 62.7 47.1 417 407 142.5 138.2 142.9 140.8 140.2 144.3 140.5 143.2 138.7 141.1 43.0 72.1 81.7 62.3 46.5 411 401 140.5 136.1 140.7 138.5 137.9 142.0 138.4 140.9 136.6 138.9 42.5 71.8 81.4 61.8 45.9 405 396 138.6 134.1 138.5 136.2 135.7 139.7 136.2 138.5 134.5 136.8 42.0 71.6 81.1 61.3 45.4 399 391 136.7 132.2 136.4 134.0 133.6 137.5 134.2 136.2 132.5 134.7 41.5 71.3 80.8 60.9 44.8 393 385 134.8 130.3 134.3 131.9 131.5 135.3 132.2 133.9 130.5 132.7 41.0 71.1 80.5 60.4 44.2 388 380 133.1 128.4 132.2 129.8 129.4 133.1 130.2 131.5 128.6 130.7 40.5 70.8 80.2 60.0 43.6 382 375 131.3 126.7 130.2 127.7 127.4 131.0 128.3 129.1 126.8 128.7硬度抗拉强度（公斤/毫米2）洛氏表面洛氏维氏布氏碳钢铬钢铬钒钢铬镍钢铬钼钢铬镍钼钢铬锰硅钢超高强度钢不锈钢不分钢种HRC H RA H R15N H R30N H R45N HV HB30D240.0 70.5 79.9 59.5 43.0 377 370 129.6 124.9 128.2 125.7 125.4 129.0 126.4 126.7 125.0 126.8 39.5 70.3 79.6 59.0 42.4 372 365 127.9 123.2 126.2 123.8 123.5 127.0 124.6 124.3 123.3 125.0 39.0 70.0 79.3 58.6 41.8 367 360 126.3 121.6 124.3 121.9 121.6 125.0 122.8 121.8 121.6 123.238.5 79.0 58.1 41.2 362 355 124.6 119.9 122.5 120.0 119.7 123.1 121.1 119.3 120.0 121.4 38.0 78.7 57.6 40.6 357 350 123.1 118.4 120.6 118.2 117.9 121.2 119.4 118.4 119.7 37.5 78.4 57.2 40.0 352 345 121.5 116.8 118.8 116.5 116.2 119.4 117.7 116.8 118.0 37.0 78.1 56.7 39.4 347 341 120.0 115.3 117.1 114.8 114.4 117.6 116.1 115.3 116.3 36.5 77.8 56.2 38.8 342 336 118.5 113.8 115.3 113.1 112.8 115.8 114.6 113.8 114.7 36.0 77.5 55.8 38.2 338 332 117.0 112.4 113.6 111.5 111.1 114.1 113.0 112.3 113.1 35.5 77.2 55.3 37.6 333 327 115.6 110.9 112.0 109.9 109.5 112.5 111.5 110.9 111.5 35.0 77.0 54.8 37.0 329 323 114.1 109.5 110.4 108.4 107.9 110.8 110.1 109.5 110.0 34.5 76.7 54.4 36.5 324 318 112.7 108.2 108.8 106.9 106.4 109.2 108.6 108.1 108.5 34.0 76.4 53.9 35.9 320 314 111.3 106.8 107.2 105.4 104.9 107.7 107.3 106.7 107.0 33.5 76.1 53.4 35.3 316 310 110.0 105.5 105.7 104.0 103.5 106.2 105.9 105.4 105.6 33.0 75.8 53.0 34.7 312 306 108.6 104.2 104.2 102.7 102.0 104.7 104.6 104.1 104.2 32.5 75.5 52.5 34.1 308 302 107.3 102.9 102.7 101.3 100.7 103.2 103.3 102.8 102.8 32.0 75.2 52.0 33.5 304 298 106.0 101.6 101.3 100.1 99.3 101.8 102.0 101.5 101.5 31.5 74.9 51.6 32.9 300 294 104.7 100.4 99.9 8.8 98.0 100.5 100.8 100.3 100.1 31.0 74.7 51.1 32.3 296 291 103.4 99.1 98.5 97.6 96.7 99.1 99.6 99.0 98.9 30.5 74.4 50.6 31.7 292 287 102.1 97.9 97.2 96.4 95.5 97.8 98.5 97.8 97.6硬度抗拉强度（公斤/毫米2）洛氏表面洛氏维氏布氏碳钢铬钢铬钒钢铬镍钢铬钼钢铬镍钼钢铬锰硅钢超高强度钢不锈钢不分钢种HRC HRA H R15N H R30N H R45N HV HB30D230.0 74.1 50.2 31.1 289 283 100.9 96.7 95.9 95.3 94.3 96.6 97.3 96.6 96.4 29.5 73.8 49.7 30.5 285 280 99.7 95.5 94.6 94.2 93.1 95.3 96.2 95.4 95.1 29.0 73.5 49.2 29.9 281 276 98.4 94.3 93.3 93.2 91.9 94.1 95.1 94.2 94.0 28.5 73.3 48.7 29.3 278 273 97.2 93.2 92.1 92.2 90.8 93.0 94.1 93.1 92.8 28.0 73.0 48.3 28.7 274 269 96.1 92.0 90.9 91.2 89.7 91.8 93.0 91.9 91.7 27.5 72.7 47.8 28.1 271 266 94.9 90.9 89.7 90.2 88.7 90.7 92.0 90.8 90.6 27.0 72.4 47.3 27.5 268 263 93.7 89.8 88.6 89.3 87.7 89.7 91.0 89.7 89.5 26.5 72.2 46.9 26.9 264 260 92.6 88.7 87.5 88.4 86.7 88.6 90.1 88.5 88.4 26.0 71.9 46.4 26.3 261 257 91.4 87.6 86.4 87.6 85.7 87.6 89.2 87.5 87.4 25.5 71.6 45.9 25.7 258 254 90.3 86.5 85.3 86.8 84.7 86.6 88.2 86.4 86.4 25.0 71.4 45.5 25.1 255 251 89.2 85.5 84.3 86.0 83.8 87.4 85.3 85.4 24.5 71.1 45.0 24.5 252 248 88.1 84.4 83.3 85.2 83.0 86.5 84.3 84.4 24.0 70.8 44.5 23.9 249 245 87.0 83.4 82.3 84.5 82.1 85.6 83.2 83.5 23.5 70.6 44.0 23.3 246 242 86.0 82.4 81.3 83.8 81.3 84.8 82.2 82.5 23.0 70.3 43.6 22.7 243 240 84.9 81.4 80.3 83.1 80.5 84.0 81.2 81.6注：1、带括号的硬盘值仅供参考。

硬度表示材料抵抗硬物体压入其表面的能力。

它是金属材料的重要性能指标之一。

一般硬度越高，耐磨性越好。

常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。

1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。

2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。

它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。

根据试验材料硬度的不同，分三种不同的标度来表示：∙HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。

∙HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。

∙HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。

3 维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。

邵氏硬度（HA）邵氏硬度专用在橡胶方面的硬度测试做橡胶的应该知道怎么测邵氏硬度（HA）用于橡胶、塑料等材料的硬度测定，将一定形状的钢制压针，在试验力作用下压入试样表面，当压足平面与试样表面紧密贴合时，测量压针相对压足平面的伸出长度。

通过公式计算出邵氏硬度值。

具有结构简单、使用方便、型小体轻、读数直观等特点。

A型参数：刻度盘值：0-100HA；压针行程范围：0—2.5mm；压针端部压力：0.055N-8.05N；压针顶端直径：Φ0.79mm+\-0.03m m。

黑色金属硬度及强度换算表注：1、带括号的硬盘值仅供参考。

根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。

抗拉强度<=1000N/mm2，或者维氏硬度<=310HV，或者布氏硬度<=300HB，或者洛氏硬度<=32HRC抗拉强度RmN/mm2维氏硬度HV布氏硬度HB洛氏硬度HRC250 80 76.0 - 270 85 80.7 - 285 90 85.2 - 305 95 90.2 - 320 100 95.0 - 335 105 99.8 - 350 110 105 - 370 115 109 - 380 120 114 - 400 125 119 - 415 130 124 - 430 135 128 - 450 140 133 - 465 145 138 - 480 150 143 - 490 155 147 - 510 160 152 - 530 165 156 - 545 170 162 - 560 175 166 - 575 180 171 - 595 185 176 - 610 190 181 - 625 195 185 - 640 200 190 - 660 205 195 - 675 210 199 - 690 215 204 - 705 220 209 - 720 225 214 - 740 230 219 - 755 235 223 - 770 240 228 20.3 785 245 233 21.3800 250 238 22.2820 255 242 23.1835 260 247 24.0850 265 252 24.8865 270 257 25.6880 275 261 26.4900 280 266 27.1915 285 271 27.8930 290 276 28.5950 295 280 29.2965 300 285 29.8995 310 295 31.0抗拉强度>1000N/mm2，或者维氏硬度>310HV，或者布氏硬度>300HB，或者洛氏硬度>32HRC抗拉强度Rm N/mm2维氏硬度HV布氏硬度HB洛氏硬度HRC103032030432.2 106033031433.3 109534032334.4 112535033335.5 111536034236.6 119037035237.7 122038036138.8 125539037139.8 129040038040.8 132041039041.8 135042039942.7 138543040943.6 142044041844.5 145545042845.3 148546043746.1 152047044746.9 1555480(456)47.7 1595490(466)48.4 1630500(475)49.1 1665510(485)49.8 1700520(494)50.5 1740530(504)51.1 1775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.988066.490067.092067.594068.0 硬度试验是机械性能试验中最简单易行的一种试验方法。