Special Feature本期特稿功能性针织面料的开发与应用随着针织服装向高档化和多功能化方向发展，功能性针织面料的开发越来越重要。
文章介绍了功能性针织面料的生产开发方法，并以纬编和经编两种不同的织造方法为线索，从原料、织造和整理等方面分别介绍了吸湿排汗、抗菌、保暖、塑身等多种功能性针织面料的开发方法及应用场合，最后还对功能性针织面料的市场情况进行了介绍，提出功能性针织面料将会向多元化、功能复合、时尚化的方向发展。
Knitted garments development is shifting to the higher end with multi-functions which pronounced the increasing importance for the R&D of functional knitted fabrics. The speci fi c manufacturing process of functional warp-knitted and weft-knitted fabrics was introduced in this paper. Development and the application of multi-functional knitted fabrics viz. quick-dry, antibacterial, thermo-keeping, body-shaping were investigated from different stages as in raw material, knitting and fi nishing. The marketplace situation of functional knitted fabrics was also studied concluding that knitted fabrics shall be diversi fi ed, functionally compounded and more fashionable.R&D and Application of Functional Knitted Fabrics文 / 丛洪莲 李秀丽随着生活质量的不断提高，人们对服装面料的功能要求有了本质的变化，过去往往注重经济实用，而现在则关注舒适性、功能性和保健性。
改性涤纶的发展【转载】发布者：日期：2011-04-031941年英国Whenfield和Dikson以对苯二甲酸和乙二醇为原料合成了聚对苯二甲酸乙二酯，并制成了纤维，在我国商品名为涤纶。
涤纶于1946年在英国工业化生产，1953年开始在世界范围内大规模工业化生产，1971年开始在数量上超过尼龙，成为第一大合成纤维。
由于涤纶具有强度高、弹性好、保型性好、尺寸稳定性高等优异性能，由其织成的衣物经久耐穿，电绝缘性好，易洗快干，具有“洗可穿”的美称，因而被广泛应用于服装、装饰、产业等领域。
但是涤纶由于内部分子排列紧密，分子间缺少亲水结构，因此回潮率很小，吸湿性能差。
在相对湿度为95％的条件下，其最高吸湿率为0.7％，由于其吸湿性差，抗静电性不好，涤纶织物透气性不好，染色性差，抗起毛起球性差。
针对涤纶使用性能的缺陷，其改性研究主要有：一是物理改性方法，主要在涤纶的生产过程中进行物理共混改性；二是化学改性方法，运用化学接枝或嵌段的方法改变涤纶的分子链结构，改善涤纶的服用性能。
1 涤纶的染色改性涤纶纤维是疏水性的合成纤维，缺乏能与直接染料、酸性染料、碱性染料等结合的官能团。
虽然具有能与分散染料形成氢键的酯基，但是涤纶分子链结构紧密，染料分子不易进入纤维内部，致使染色困难，色泽单调，直接影响到涤纶面料花色品种的开发。
由于涤纶的结晶度高，纤维中只存在较小的空隙，当温度较低时，分子热运动改变其位置的幅度较小，在潮湿条件下，涤纶纤维又不会象棉纤维那样能通过剧烈溶胀而使空隙增大，染料分子难以渗透到纤维内部。
涤纶染色时通常只能用分散染料进行染色，并且必须在高温高压下或借助载体进行染色。
为了提高涤纶的染色性能，从分子结构上考虑，提高分子链的疏松程度，将有助于染料分子的进入。
改善染色性能主要采用的方法有：(1)与分子体积庞大的化台物共聚；(2)与具有可塑化效应的化合物混合纺丝；(3)导入具有醚键那样的和分散性染料亲和性好的基团。