文档下载后可定制修改，请根据实际需要进行调整和使用，谢谢！本店铺为大家提供各种类型的实用资料，如教育随笔、日记赏析、句子摘抄、古诗大全、经典美文、话题作文、工作总结、词语解析、文案摘录、其他资料等等，想了解不同资料格式和写法，敬请关注！Download tips: This document is carefully compiled by this editor. I hope that after you download it, it can help you solve practical problems. The document can be customized and modified after downloading, please adjust and use it according to actual needs, thank you! In addition, this shop provides you with various types of practical materials, such as educational essays, diary appreciation, sentence excerpts, ancient poems, classic articles, topic composition, work summary, word parsing, copy excerpts, other materials and so on, want to know different data formats and writing methods, please pay attention!磷石膏是磷肥生产过程中产生的副产品,其处理和利用是一项复杂的工艺流程。

磷石膏组成特性及处理方法磷石膏主要有灰黑色和灰白色两种，颗粒直径一般为5～50μm，结晶水含量20%~25%。

磷石膏是湿法磷酸工艺中产生的固体废弃物，其组分主要是二水硫酸钙。

磷石膏的组成比较复杂，除硫酸钙以外，还有未完全分解的磷矿、残余的磷酸、氟化物、酸不溶物、有机质等，其中氟和有机质的存在对磷石膏的资源化利用影响最大。

磷石膏的随意排放堆积严重破坏了生态环境，不仅污染地下水资源，还造成土地资源的浪费。

组成磷石膏多呈板状，根据生产工艺的不同，磷石膏中二水硫酸钙和半水硫酸钙的比例也不相同，但主要组成以二水硫酸钙为主，还含有少量的磷酸、氟、有机物等杂质，另外还含有一些放射性元素。

特性磷石膏通常是灰黑色或灰白色，只有少数对生产条件严格工厂的产生的磷石膏杂质少，颜色比较浅，有时呈白色。

磷石膏主要物相是二水硫酸钙，晶体的晶型有针状、单分散板状、多晶核和密实四种形态，其中以板状晶体为主。

磷石膏的胶凝性能低于天然石膏，胶结性能不如天然石膏，粘滞性、流动性也比天然石膏差，磷石膏浆体凝结时间长，并具有一定的腐蚀性。

磷石膏在水中的溶解度极小，随着温度的升高溶解度下降，层间的透水性能优于水平层内的透水性能，是一种应变软化材料。

磷石膏的粒径大小比例比较集中，杂质的含量与晶体的形貌与磷矿石有很大的关系，磷石膏的晶型越规则，磷石膏的粒径就越大，杂质含量相对就越少。

杂质磷石膏中的杂质是指除了硫酸钙以外的组分，包括少量未完全分解的磷矿、残留的磷酸以及氟化物、酸不溶物、铁铝化合物、有机质等。

根据磷石膏中杂质的物理特性，可以将杂质分为三类：第一类为可溶性杂质；第二类为难溶性杂质；第三类为放射性杂质。

其中可溶性杂质对环境的危害最大，随雨水渗透到土壤中污染环境；对于不溶杂质而言，影响相对比较弱。

难溶性杂质含量较高，种类不一。

磷磷石膏中磷的含量比较多，是对磷石膏的物理特性影响最大的杂质，磷石膏中因为磷的存在严重制约了其合理化利用。

根据磷在磷石膏中的存在形式可以将杂质磷分为三种，分别为可溶磷、难溶磷和共晶磷。

磷石膏综合利用的现状和研究进展磷石膏是湿法磷酸生产过程中排放的工业废渣。

其主要成分是二水硫酸钙，此外，还含有少量未分解的磷矿粉，未洗涤干净的磷酸、磷酸铁、磷酸铝和氟硅酸盐等杂质。

通常每生产1t磷酸约排放5t左右的磷石膏。

目前全世界磷石膏的年排放量非常可观，在150Mt以上。

我国磷石膏的年排放量也达到了20Mt。

这不仅占据了大量土地，而且还污染了环境。

磷石膏综合利用工艺研究，一直是国内外环保领域的重要课题。

长期来，人们都致力于研究磷石膏的有效利用。

1．作水泥缓凝剂水泥生产中需要大量的石膏作为延长凝固时间的缓凝剂。

目前我国水泥行业中所用的缓凝剂大部分为天然石膏，年耗量约20Mt/a。

磷石膏一般呈酸性，还含有水溶性五氧化二磷和氟，不能直接作水泥缓凝剂使用，需要经过预处理，去除杂质或改性。

磷石膏制水泥缓凝剂的工艺主要是洗涤去除杂质或经过改性处理。

预处理可采用水洗法，先将磷石膏加水调成含5%的固体浆料，再经真空过滤即可除去可溶性磷酸盐；也可采用中和法，用石灰（或消石灰）将可溶性磷酸盐转变为不溶性的磷酸钙，再进行干燥，焙烧碾磨后加水造粒，使之成为10-30mm粒度的产品。

杭州水泥厂、南京江南水泥厂、马鞍山水泥厂、上海水泥厂等企业都做过用磷石膏代替天然石膏作水泥缓凝剂的试验。

试验表明，用经过预处理的磷石膏代替天然石膏作水泥缓凝剂，不但不会降低水泥强度，而且使水泥的后期强度比天然石膏还高，且能降低生产水泥的成本。

据报道，1999年8月安徽省铜陵化学工业集团100t/a利用磷石膏生产水泥缓凝剂的工艺生产线建成投产，产品的初凝、终凝、抗折、抗压强度均达到了国家标准要求。

另外，陕西华县化工建材厂也建成了30t/a的水泥缓凝剂生产装置。

2.作石膏建筑材料磷石膏中的二水硫酸钙必须转变成半水磷酸钙才可用于作石膏建筑材料。

半水石膏有α和β2种。

前者称为高强石膏，后者称为熟石膏。

通常α-半水石膏结晶粗大、整齐、致密，有一定的结晶形状；β-半水石膏晶体细小，体积松大。

磷石膏预处理工艺研究磷石膏是一种常见的工业废渣，主要由磷酸、硫酸和水合硫酸钙组成。

磷石膏不仅含有大量的钙元素，也含有少量的磷元素，因此在农田改良和磷肥生产中有广泛的应用。

然而，直接利用磷石膏存在一些问题，如其结构不稳定、水溶性差，容易产生二次污染等。

为了充分利用磷石膏资源并减缓其对环境的影响，磷石膏预处理工艺被提出并得到广泛研究。

磷石膏预处理工艺主要包括碱激发处理、烧结预处理和酸处理等。

碱激发处理是利用碱性物质激发磷石膏中的活性成分，提高其稳定性和水溶性。

目前常用的碱激发剂包括氢氧化钙、氢氧化钠等。

通过与磷石膏反应生成磷酸钙等稳定物质，从而提高磷石膏的水溶性和可利用性。

烧结预处理是将磷石膏在高温条件下进行烧结，使其生成一种致密的烧结磷石膏砖。

烧结磷石膏砖具有较高的强度和稳定性，可用作建筑材料或道路基层材料。

同时，通过烧结预处理，还可以减少磷石膏的容积，降低对环境的占用。

酸处理是将磷石膏与酸性物质反应，将其转化为可溶性的磷酸盐化合物。

酸处理可以分为浸泡法和酸解法两种。

浸泡法是将磷石膏浸泡在酸性溶液中，使其与酸反应成可溶性的磷酸盐。

酸解法是将磷石膏与酸进行滚动反应，产生磷酸盐和硫酸。

酸处理可以提高磷石膏的溶解度和可利用性，方便其在肥料生产中的应用。

除了以上三种预处理工艺，还有一些其他的研究方法，如磷石膏石墨化处理、磷石膏氧化焙烧处理等。

这些方法在提高磷石膏的稳定性、水溶性和可利用性方面具有潜力。

总之，磷石膏作为常见的工业废渣，其预处理工艺研究具有重要意义。

通过合理的预处理工艺，既能充分利用磷石膏资源，又能减缓其对环境的影响，为环保产业的发展做出贡献。

第39卷第12期硅酸盐通扌艮Vol.39No.12 2020年12月BULLETIN OF THE CHINESE CERAMIC SOCIETY December,2020磷石膏激发预处理及其制备免烧建材的研究田佳瑜1,2,王海峰1,2,尤晓宇1,2,陈晓亮1,2,王家伟1,2(1.贵州大学材料与冶金学院，贵阳550025；2.贵州省冶金工程与过程节能重点实验室，贵阳550025)摘要:磷石膏胶凝活性差,阻碍了它在建材领域的大宗消纳。

本文通过研究碱激发预处理后磷石膏物相和微观结构,以及用其制备高掺量免烧建材的抗压强度、物相和微观结构,从而获得磷石膏制备高掺量、高抗压强度免烧建材的工艺参数。

结果表明：100g磷石膏，碱激发剂为100mL,在室温下预处理24h后，磷石膏主晶相CaSO4-2H O的晶粒变小，结晶度降低,通过观察微观结构发现硫酸钙颗粒变大,细小颗粒量大幅降低，从而提高了其胶凝活性。

当磷石膏掺入量为80%(质量分数)时,与未处理磷石膏相比，所制备的免烧建材保养7d、28d和浸水后的抗压强度均明显提高，分别为13.79MPa、18.22MPa和11.44MPa，其微观形貌显示硫酸钙颗粒间没明显边界，几乎融为一体，致密度极高，对材料强度的增加十分有利。

关键词:磷石膏；预处理；碱激发；抗压强度；免烧建材中图分类号:X781.3文献标识码：A文章编号：1001-1625(2020)12-3897_08Excitation Pretreatment of Phosphogypsum and Preparationof Non-Burning Building MaterialsTIAN Jiayu1，2,WANG Haifeng1，2,YOU Xiaoyu1，2,CHEN Xiaoliang1，2,WANG Jiawei1，2(1.College of Materials and Metallurgy,Guizhou L niversity,Guiyang550025,China；2.Guizhou Provincial Key Laboratory of Metallurgical Engineering and Energy Saving,Guiyang550025,China)Abstract：Phosphogypsum has poor cementitious activity，which hinders its large consumption in the field of building materials.By studying the phase and microstructure of phosphogypsum pretreated by alkali excitation，and the compressive strength，phase and microstructure of the non-burning building materials prepared with the high content phosphogypsum，the process parameters of preparing high content and high compressive strength non-burning building materials with phosphogypsum were obtained.The result shows that，when100g phosphogypsum is added with100mL activator，after 24h of excitation under room temperature,the main crystalline phase CaSO q・2H2O of phosphogypsum has smaller grains and lower crystallinity.Microstructure analysis shows that the size of calcium sulfate particles increases and the amount of fine particles decreases significantly after pretreatment.Thus,its gelation activity is improved.When the content of phosphogypsum is80%(mass fraction)，compared with the untreated phosphogypsum，the compressive strength of the prepared non-burning building materials after maintening for7d，28d and immersion in water are significantly improved，which are13.79MPa，18.22MPa and11.44MPa，respectively.Its micromorphology shows that there is no obvious boundary between the calcium sulfate particles，they are almost integrated with high density，which is very beneficial to the strength of the materials.Key words：phosphogypsum；pretreatment；alkali excitation；compressive strength；non-burning building material0引言随着磷化工行业的飞速发展，湿法磷酸工业排放的磷石膏已呈现逐年增加趋势，目前世界磷石膏排放量每年约为3亿t[1],由于其含有水溶性磷、水溶性氟、游离酸等有害物质，导致其资源利用率低，仅为10%左基金项目：国家自然科学基金(51764006,51864012)；贵州省科技计划项目(黔科合基础[2019]1411号)作者简介：田佳瑜(1996—)，女，硕士研究生。

磷石膏生产线工艺
磷石膏生产线工艺
磷石膏生产线工艺是一种有效的磷石膏生产方法，主要包括以下过程：
一、预处理
1、原料准备：首先将原料取出，原料包括硫酸，磷酸三钙，液氨，氯化钠等，经过化验，根据配方组成，分拣出使用的原料，其次，将它们分别粉碎粒度，满足生产要求。

2、细粉定型：将定型料混入液体细粉，混合均匀，保证料的稳定性，提高最终成品的粒度均匀性和抗冲击强度。

二、烘干
将混合物倒入气流烘干机中，由气流强烈的旋转运动带动混合物进入气流，加热干燥，得到烘干结果。

三、破碎
将干燥的物料进行破碎，使其粒度符合要求。

四、电沉淀
将物料放入电沉淀池，采用真空型电沉淀工艺，电沉淀后可以实现较细的磷石膏粒度。

五、烧结
将磷石膏进行烧结，烧结可以提高磷石膏的抗冲击性，抗制酸性物质，以及提高磷石膏的粉末定形状态和粒度。

六、冷冻
将烧结的磷石膏以冷冻的方式进行冷却，以使其形状稳定，粉末表面完整，耐候性好。

七、筛分
将磷石膏放入筛分机中，筛分出满足客户要求的不同尺寸的磷石膏。

八、包装
将不同尺寸的磷石膏放入密封包装中，包装后送往物流中心，即可出库发货。

磷石膏预处理工艺研究摘要：针对我国磷石膏的排放现状及其性能特点，介绍了国内外对磷石膏进行预处理的各种方法，系统研究了水洗、石灰中和、球磨、浮选、筛分以及煅烧等预处理工艺，经过对比分析，对磷石膏建材资源化的预处理提出了可参考性意见。

关键词：磷石膏；杂质；预处理Abstract：Some methods about phosphogypsum pretreatment in China and abroad are introduced. Keywords: phosphogypsum；impurity；pretreatment0 前言磷石膏是磷酸及磷肥类工业在生产过程中所产生的一种工业废渣，每生产1t磷酸排出磷石膏约5～6t，目前全世界的磷酸工业每年生产磷石膏约在1.3亿t以上，我国每年排放的磷石膏业大约在2000万t以上，大多数国家仍然将磷石膏排入河流、湖泊和海洋中,或堆积在陆地上,大约有28%的磷石膏被再加工利用。

磷石膏经排放或堆存、雨水淋溶后其中的氟和残磷等有害物质将随着雨水而浸出,对水体、土壤环境和大气环境造成不同程度的污染。

据统计,目前而云南省每年排放的磷石膏就在500万t以上。

近年来我国在磷石膏的开发利用方面已经有了一定的研究工作,但其利用率依然不高。

根据我国磷石膏的情况,大力开发利用工业副产品磷石膏,保护资源和环境,符合我国资源和环境可持续发展的方向。

磷矿用硫酸分解制取磷酸时,磷矿含有的Fe、Al、Mg等杂质化合物大部分分解,溶于磷酸溶液。

在诸多杂质中磷对磷石膏性能影响最大,主要表现为延长磷石膏的凝结时间和降低石膏制品的强度。

少量未分解的磷矿、氟化物、酸不溶物、炭化了的有机物质呈细小的质点与反应生成的硫酸钙一起沉淀析出。

磷酸溶液与硫酸钙的沉淀过滤分离后,滤饼经过一定的洗涤后,还是含有少量的酸液。

这种磷酸生产的含有少量未分解磷矿和游离酸的二水硫酸钙称为磷石膏[1]。

磷石膏的外表一般呈灰白色,如果P2O5和水分含量较高时颜色相对较深,粉状,质量轻,比重一般在1.4～1.8t/m3。

预处理工艺影响磷石膏水泥砂浆性能研究摘要：磷石膏的预处理工艺包括酸浸法、中合法和水洗法，不同处理工艺都会对磷石膏的性能造成影响，尤其是流动性、凝结时间和抗压强度。

不同预处理工艺能够将石膏中杂质去除，然而由于预处理生成物与去除量之间存在差异性，因此导致砂浆性能差异性比较大。

此次研究主要是探讨分析预处理工艺影响磷石膏水泥砂浆性能，希望能够对相关人员起到参考性价值。

关键词：预处理工艺；磷石膏；水泥砂浆；性能在磷化工生产期间，会产生磷石膏等副产品，其成分包括二水硫酸钙，并且包含磷酸和五氧化二磷等杂质，有效处理磷石膏能够解决环境污染和资源浪费情况。

磷石膏水泥砂浆是按照标准比例，将砂石、水泥和粉煤灰混合制作的建筑材料。

磷石膏中所含有的氟化物和磷酸会影响砂浆性能，包括拌和耗水量以及强度等。

为了使磷石膏的杂质含量减少，加强砂浆性能，此次研究拟采用酸浸法、中合法和水洗法等处理工艺，且比较分析不同处理工艺对砂浆性能的影响。

1 试验分析1.1材料磷石膏，密度2.18g/cm³，成分如下：三氧化硫为39.35w/%；氧化钙为33.56w/%；二氧化硅为3.17w/%；五氧化二磷为0.78w/%；三氧化二铝为0.86/%；氧化镁为0.45w/%；氧化钾为0.15w/%；三氧化二铁为0.13w/%。

集料为河砂，水泥为硅酸盐水泥，聚羧酸减水剂，1级粉煤灰。

1.2预处理在对磷石膏进行预处理时，必须注重磷石膏再利用率，以此降低杂质对性能的影响。

磷石膏杂质为可溶氟、有机物和难溶性磷。

其中，可溶性氟和可溶性磷对磷石膏性能影响比较大。

使用标准筛（74µm）将磷石膏进行筛分处理。

水洗法处理工艺：将磷石膏置于水中进行冲洗，通过检测石膏pH值，判断净化效果。

水洗法能够将石膏中有机物、可溶性氟化与可溶性磷等杂质去除。

然而此种处理工艺需水量比较大，还需要对水洗废水进行处理，以免造成二次污染。

水洗工艺的温度设置在39摄氏度，按照1：3比例将磷石膏与水进行混合水洗，搅拌时间控制为10min，将预处理的石膏置于烘箱（60℃）内烘干。

磷石膏预处理方法磷石膏是一种常见的工业废弃物，主要由磷酸盐生产过程中的废水和废气中的磷酸钙沉淀物组成。

磷石膏含有大量的磷酸盐和钙，如果不加以处理，会对环境造成严重的污染。

因此，磷石膏的预处理方法非常重要。

磷石膏的预处理方法主要包括物理处理和化学处理两种方法。

物理处理主要是通过筛分、沉淀、过滤等方法将磷石膏中的杂质和水分去除，以便后续的处理。

化学处理则是通过添加化学药剂，使磷石膏中的磷酸盐和钙离子发生化学反应，形成可回收的磷酸盐和钙化合物。

物理处理方法物理处理方法主要包括筛分、沉淀和过滤三种方法。

筛分是将磷石膏通过筛网进行分离，去除其中的大颗粒杂质。

筛分的目的是为了减少后续处理过程中的能耗和化学药剂的使用量。

筛分的筛网大小一般为0.5mm-2mm，可以根据实际情况进行调整。

沉淀是将磷石膏中的悬浮颗粒通过重力沉降的方法进行分离。

沉淀的方法有很多种，常用的有静态沉淀和动态沉淀两种。

静态沉淀是将磷石膏放置在静止的容器中，让其中的悬浮颗粒自然沉降。

动态沉淀则是通过搅拌或气浮等方法，加速悬浮颗粒的沉降速度。

沉淀的时间和方法可以根据实际情况进行调整。

过滤是将磷石膏中的悬浮颗粒通过过滤器进行分离。

过滤器的选择和过滤介质的选择都非常重要。

常用的过滤器有压力过滤器和真空过滤器两种。

过滤介质可以选择砂子、滤纸、滤布等材料。

过滤的速度和效果可以根据实际情况进行调整。

化学处理方法化学处理方法主要是通过添加化学药剂，使磷石膏中的磷酸盐和钙离子发生化学反应，形成可回收的磷酸盐和钙化合物。

常用的化学药剂有硫酸、氢氧化钠、氯化钙等。

硫酸法是将磷石膏与硫酸反应，生成磷酸和硫酸钙。

反应方程式为：Ca3(PO4)2 + 3H2SO4 → 2H3PO4 + 3CaSO4氢氧化钠法是将磷石膏与氢氧化钠反应，生成磷酸钠和氢氧化钙。

反应方程式为：Ca3(PO4)2 + 6NaOH → 2Na3PO4 + 3Ca(OH)2氯化钙法是将磷石膏与氯化钙反应，生成磷酸钙和氯化钠。

磷石膏建材原料的预处理研究发布时间：2022-10-24T02:31:35.957Z 来源：《工程管理前沿》2022年6月第12期作者：刘次啟张强[导读] 本文主要围绕着磷石膏的预处理方法展开分析讨论，这具有极强的现实意义。

刘次啟张强贵州省建材产品质量检验检测院 550014摘要：能源的利用效率受到诸多因素的影响。

在实践中不难发现，磷石膏中的杂质会极大地损害磷石膏的利用价值。

因此，相关工作人员应当做好磷石膏建材原料的预处理工作，提升磷石膏的利用效率。

本文主要围绕着磷石膏的预处理方法展开分析讨论，这具有极强的现实意义。

关键词：磷石膏；建材原料；预处理技术；杂质一、引言二水硫酸钙作为磷石膏的主要构成要素，其产自生产湿法磷酸。

究其本质，为一种固体生产原料。

因磷石膏中含有大量的有害杂质，如果相关工作人员将其随意乱放，不仅会污染、损伤土地，还会使得公司的管理成本增加。

因此，近年来大量的建材公司致力于解决磷石膏的预处理问题，从而使得磷石膏这一建筑原料的利用效率得以提升。

现阶段，磷石膏的应用范围较为广泛，石膏砌块、石膏砖等建筑材料均为其典型代表。

二、磷石膏的预处理方法2.1磷石膏中有害成分分析磷石膏中的杂质主要包含以下四种：一、磷类物质。

在实际的建筑过程中，其能够使得磷石膏的凝固时间延长并使得建筑物的硬化强度降低，从而降低建筑物的建设效率；二、氟类物质。

该类杂质的存在将使得磷石膏晶体的粗化程度提高，进而使得分子之间的作用力降低，从而降低建筑物的结构紧密程度；三、有机物类。

该类杂质主要存在于相关工作人员添加的有机添加剂中，其会使得磷石膏晶体之间的结合程度降低，从而使得建筑物的结构日趋松散；四、其他杂质，主要包含石英、铁等物质。

该类杂质的存在极易使得干燥后的石膏体表面发霉。

此外，杂质中所含的放射性因素会对环境造成极大的损害。

2.2磷石膏的预处理方法有关技术人员采取何种方式完成磷石膏的预处理工作在一定程度上决定了磷石膏利用效能的多少。