酸化凹凸棒石的制备及其对苯胺的吸附性能关媛;王少莽;易广;陈璐;吴鑫泉;陆武;翁彭【摘要】Natural palygorskite was acidified with different concentration of hydrochloric acid.The acid-ified palygorskite was characterized by XRD,SEM,BET,FTIR and ZATA potential.Under different process conditions,the adsorption performance of acidified palygorskite treated with different concen-tration of hydrochloric acid,was evaluated by removal of aniline in water.When the activation concen-tration of hydrochloric acid was 6mol·L-1 ,the pH value of the aniline solution was 6,the initial mass concentration of aniline was 50mg·L-1 ,the amount of adsorbent was 0.5g,the temperature was 30℃,the adsorption time was 240min,the acidified palygorskite could acquire better adsorption activity and remove more than 75.2% of aniline.In addition,the adsorption behavior of aniline over a-cidified palygorskite was more suitable to be described by pseudo-second-order kinetic model.%以天然凹凸棒石为原料,利用不同浓度的盐酸对其进行酸活化改性.对改性后的酸化凹凸棒石进行XRD,SEM,BET,FTIR以及ZATA电位的表征,并以苯胺为模拟污染物,考察不同浓度的盐酸,以及吸附工艺条件对其吸附性能的影响.研究表明,当盐酸的活化浓度为6mol·L-1,苯胺溶液的pH为6,苯胺初始质量浓度为50mg·L-1,吸附剂投料量为0.5g,温度为30℃,吸附时间为240min时,酸化凹凸棒石具有较高的吸附活性,可吸附脱除75.2%以上的苯胺.此外,苯胺在酸化凹凸棒石上的吸附行为符合假二级动力学模型.【期刊名称】《常州大学学报（自然科学版）》【年(卷),期】2017(029)006【总页数】11页(P15-25)【关键词】凹凸棒石;酸化改性;吸附;苯胺;假二级动力学模型【作者】关媛;王少莽;易广;陈璐;吴鑫泉;陆武;翁彭【作者单位】常州大学石油化工学院,江苏常州 213164;常州大学环境与安全工程学院,江苏常州 213164;常州大学石油化工学院,江苏常州 213164;常州大学石油化工学院,江苏常州 213164;常州大学石油化工学院,江苏常州 213164;常州大学环境与安全工程学院,江苏常州 213164;常州大学环境与安全工程学院,江苏常州 213164【正文语种】中文【中图分类】O611.4由于天然凹凸棒石(natural palygorskite, 简称NP)对污染物的吸附容量较低，因此就需要对其进行活化改性以提高吸附性能。
磁性聚苯胺吸附材料的制备及对碘的吸附性能研究
张祎鹏;吴展华
【期刊名称】《湿法冶金》
【年(卷),期】2024(43)3
【摘要】研究了以聚苯胺(PANI)包覆四氧化三铁制备Fe_(3)O_(4)@PANI磁性吸附材料,并用于吸附水中的碘单质。
采用SEM、TEM、FT-IR、XRD、VSM、XPS 和Raman等方法对该复合材料吸附前后的形貌与性质进行表征,探究了该复合材料的吸附机制,同时考察了吸附时间、碘溶液浓度、吸附温度及再生对吸附性能的影响。
结果表明:聚苯胺包覆四氧化三铁吸附溶液中的I_(2)时,碘分别与聚苯胺的苯环、醌环及醌环结构单元的氮原子结合;Fe_(3)O_(4)@PANI对I_(2)的吸附为自发吸热的过程,符合准二级动力学模型与Langmuir等温吸附模型;在303.15 K时,理论最大吸附量为1777.13 mg/g,负载吸附剂用乙醇脱附并循环使用3次后,其吸附率可达第1次吸附率的44.22%。
【总页数】9页(P284-292)
【作者】张祎鹏;吴展华
【作者单位】中国原子能科学研究院
【正文语种】中文
【中图分类】TQ424;O647.3
【相关文献】
1.活性炭/聚苯胺复合材料的制备及吸附性能研究
2.常温下聚苯胺吸附材料的制备及吸附性能研究
3.磁性氧化石墨烯/聚苯胺纳米复合材料的制备
及再生循环吸附性研究4.聚苯胺-氧化铁磁性复合材料的制备及其对甲基橙吸附性能的应用5.多壁碳纳米管/聚苯胺纳米纤维复合材料的制备及其吸附性能研究
因版权原因，仅展示原文概要，查看原文内容请购买。
凹凸棒土合成方钠石分子筛及对铬的吸附效果研究李红玑;李宁;吴喜勇;陈立军【摘要】In the synthesis methods of molecular sieve, the hydrothermal synthesis method with low cost and simple operation is very popular in the resent years. Because of its developed pore, unique adsorption and catalysis characteristics, the zeolite has been widely used in chemical industry, environmental protection, water treatment and other fields. In this study, using attapulgite as raw material, sodalite was synthesized by the hydrothermal synthesis method, and the adsorption effect of the sodalite to chromium was studied. The results show that adsorption capacity of the sodalite zeolite is 5.6 mg/g, the adsorption efficiency can reach to 89.5% in 8h.%在分子筛合成方法中，以廉价矿土的水热合成法，因其成本低、操作简单，在近些年的研究中倍受青睐。
而沸石分子筛因其孔道发达，吸附和催化性能独特，被广泛应用于化工、环保、水处理等领域。
以凹凸棒土为原料，经改性提纯后，按一定比例用水热合成法合成方钠石分子筛，并研究其对铬的吸附性能，该分子筛的吸附容量为5.6 mg/g，吸附效率在8 h 达89.5%。