LEXAN™ EXL9330 resin聚碳酸酯SABIC Innovative Plastics产品说明Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.添加剂紫外线稳定剂阻燃性特性Chlorine Free 共聚物可加工性,良好无溴阻燃性RoHS 合规性RoHS 合规外观不透明加工方法注射成型物理性能额定值单位制测试方法比重 -- 1.18g/cm³ASTM D792 --1.19g/cm³ISO 1183 熔流率(熔体流动速率) (300°C/1.2 kg)10g/10 min ASTM D1238 溶化体积流率(MVR) (300°C/1.2 kg)9.00cm³/10min ISO 1133 收缩率内部方法 流动 : 3.20 mm 0.40 到 0.80%内部方法 横向流动 : 3.20 mm 0.40 到 0.80%内部方法 吸水率 ISO 62 饱和, 23°C0.35%ISO 62 平衡, 23°C, 50% RH 0.15%ISO 62 室外适用性f1UL 746C硬度额定值单位制测试方法球压硬度 (H 358/30)90.0MPaISO 2039-1机械性能额定值单位制测试方法拉伸模量 -- 12100MPa ASTM D638 -- 2100MPa ISO 527-2/1 抗张强度 屈服 258.6MPa ASTM D638 屈服 55.0MPa ISO 527-2/50 断裂 361.4MPa ASTM D638 断裂 60.0MPa ISO 527-2/50 伸长率 屈服 4 6.0%ASTM D638 屈服 6.0%ISO 527-2/50 断裂 5130%ASTM D638 断裂 130%ISO 527-2/50 弯曲模量 50.0 mm 跨距 62070MPa ASTM D790 -- 72200MPa ISO 178 弯曲应力 --85.0MPa ISO 178 屈服, 50.0 mm 跨距888.9MPaASTM D790冲击性能额定值单位制测试方法简支梁缺口冲击强度9ISO 179/1eA -30°C 60kJ/m²ISO 179/1eA 23°C75kJ/m²ISO 179/1eA 简支梁无缺口冲击强度10ISO 179/1eU志-为-塑-胶-提-供136（8665）6661-30°C 无断裂ISO 179/1eU 23°C 无断裂ISO 179/1eU 悬壁梁缺口冲击强度-50°C 590J/m ASTM D256 -30°C 680J/m ASTM D256 23°C 800J/m ASTM D256 23°C, 6.40 mm 640J/m ASTM D256 -30°C 1155kJ/m²ISO 180/1A -30°C 1265kJ/m²ISO 180/4A 23°C 1370kJ/m²ISO 180/1A 23°C 1480kJ/m²ISO 180/4A 无缺口悬臂梁冲击23°C 151100J/m内部方法-30°C 16无断裂ISO 180/1U 23°C 17无断裂ISO 180/1U 装有测量仪表的落镖冲击 (23°C, Total Energy)52.9J ASTM D3763 热性能额定值单位制测试方法载荷下热变形温度0.45 MPa, 未退火, 3.20 mm 134°C ASTM D6480.45 MPa, 未退火, 100 mm 跨距18135°C ISO 75-2/Be1.8 MPa, 未退火, 3.20 mm 121°C ASTM D6481.8 MPa, 未退火, 6.40 mm 124°C ASTM D6481.8 MPa, 未退火, 100 mm 跨距19124°C ISO 75-2/Ae 维卡软化温度-- 142°C ASTM D1525, ISO 306/B120 13 20-- 140°C ISO 306/B50Ball Pressure Test (125°C)Pass IEC 60695-10-2线形热膨胀系数流动 : -40 到 40°C 6.7E-5cm/cm/°C ASTM E831 流动 : 23 到 80°C 7.2E-5cm/cm/°C ISO 11359-2 横向 : -40 到 40°C 6.7E-5cm/cm/°C ASTM E831 横向 : 23 到 80°C 7.7E-5cm/cm/°C ISO 11359-2RTI Elec 125°C UL 746RTI Imp 115°C UL 746RTI 120°C UL 746电气性能额定值单位制测试方法表面电阻率> 1.0E+15ohms IEC 60093体积电阻率> 1.0E+15ohms cm IEC 60093介电强度3.20 mm, in Oil 17kV/mm ASTM D1493.20 mm, 在油中16kV/mm IEC 60243-1介电常数50 Hz 2.95ASTM D15060 Hz 2.95ASTM D1501 MHz 2.90ASTM D15050 Hz 2.60IEC 6025060 Hz 2.60IEC 602501 MHz 2.70IEC 60250耗散因数50 Hz 2.4E-3ASTM D15060 Hz 2.4E-3ASTM D1501 MHz 8.5E-3ASTM D150, IEC 6025050 Hz 1.0E-3IEC 6025060 Hz 1.0E-3IEC 60250相比耐漏电起痕指数(CTI) PLC 3UL 746漏电起痕指数225V IEC 60112高电弧燃烧指数(HAI) PLC 0UL 746热丝引燃 (HWI) PLC 1UL 746可燃性额定值单位制测试方法UL 阻燃等级UL 941.50 mm V-0UL 943.00 mm 5VA UL 94灼热丝易燃指数 (1.00 mm)960°C IEC 60695-2-12 热灯丝点火温度 (1.00 mm)825°C IEC 60695-2-13 极限氧指数35%ISO 4589-2注射额定值单位制干燥温度121°C干燥时间 3.0 到 4.0hr干燥时间,最大48hr建议的最大水分含量0.020%建议注射量40 到 60%料筒后部温度217 到 293°C料筒中部温度282 到 304°C料筒前部温度293 到 316°C射嘴温度288 到 310°C加工(熔体)温度293 到 316°C模具温度71.0 到 93.0°C背压0.345 到 0.689MPa螺杆转速40 到 70rpm排气孔深度0.025 到 0.076mm备注1.50 mm/min2.类型 1, 50 mm/min3.类型 1, 50 mm/min4.类型 1, 50 mm/min5.类型 1, 50 mm/min6. 1.3 mm/min7. 2.0 mm/min8. 1.3 mm/min9.80*10*3 sp=62mm10.80*10*3 sp=62mm11.80*10*312.63.5*12.7*3.213.80*10*314.63.5*12.7*3.215.Double-Gated16.80*10*317.80*10*318.120*10*4 mm19.120*10*4 mm20.标准 B (120°C/h), 载荷2 (50N)。

Description:SABIC® PPcompound 2500/6 is a mineral filled modified polypropylene. Typical material properties include very high flow, high impact, good stiffness and low shrinkage and CLTE. Typical material properties also include good chemical resistance and esthetical performance. Typical applications include automotive exterior trims such as lateral siding, bumper strips and bumpers. It can be used in painted and unpainted applications with UV stabilization added on demand.SABIC® PPcompound 2500/6 is a designated automotive grade.IMDS ID: 164860791)All measurements on injection molded samples.2)Speed of testing: 50 mm/min; Specimen ISO 527-5, 3.2 mm3)3-point loading4)N.B.: No Break5)U-shaped notch; N.B.: No BreakQuality:SABIC Europe is fully certified in accordance with the internationally accepted quality standard ISO9001.Storage and handling:Avoid prolonged storage in open sunlight, high temperatures (<50 °C) and /or high humidity as this could well speed up alteration and consequently loss of quality of the material and /or its packaging. Keep material completely dry for good processing.Disclaimer. The information contained herein may include typical properties of our products or their typical performances when used in certain typical applications. Actual properties of our products, in particular when used in conjunction with any third party material(s) or for any non-typical applications, may differ from typical properties.It is the customer's responsibility to inspect and test our product(s) in order to satisfy itself as to the suitability of the product(s) for its and its customers particular purposes. The customer is responsible for the appropriate, safe and legal use, processing and handling of all product(s) purchased from us.Nothing herein is intended to be nor shall it constitute a warranty whatsoever, in particular, warranty of merchantability or fitness for a particular purpose.SABIC Europe as referred to herein means any legal entity belonging to the SABIC Europe group of companies.。

宝瑞塑胶原料有限公司
概述材料聚碳酸酯/聚对苯二甲酸丁二醇酯（PBT）混合，非增强
类别：热塑性聚合物聚碳酸酯（PC）聚碳酸酯/聚对苯二甲酸丁二酯（PBT）共混物，非增强聚酯，TP，聚对苯二甲酸丁二醇酯（PBT）
材质说明：此属性数据MatWeb的数据库类别“聚碳酸酯/聚对苯二甲酸丁二酯（PBT）混合，非增强”总结了类似的材料。

报告的每个属性的值范围是适当MatWeb的条目的最小值和最大值。

的注释报告的平均值，用于计算平均值的数据点的数目。

值不一定是典型的任何特定的品位，尤其是不太常见的价值观和那些可以受影响最严重的添加剂或加工方法。

CoPA,injection molding grade,15%glass fibers ISO Shortname:ISO 1874-PA 6/66,MR,14-060,GF15PropertyTest ConditionUnitStandardguide valued.a.m.cond.Rheological properties Molding shrinkage,parallel 150x105x3;280°C /MT 80°C;500bar%acc.ISO 25770.29Molding shrinkage,transverse 150x105x3;280°C /MT 80°C;500bar%acc.ISO 25770.88Post-shrinkage,parallel 150x105x3;120°C;4h %acc.ISO 25770.08Post-shrinkage,transverse150x105x3;120°C;4h%acc.ISO 25770.21Mechanical properties (23°C/50%r.h.)C Tensile modulus 1mm/min MPa ISO 527-1,-263003600C Tensile Stress at break 5mm/min MPa ISO 527-1,-212575C Tensile Strain at break 5mm/min %ISO 527-1,-2 3.012C Charpy impact strength 23°C kJ/m²ISO 179-1eU 4570C Charpy impact strength -30°C kJ/m²ISO 179-1eU 3535C Charpy notched impact strength 23°C kJ/m²ISO 179-1eA <1010C Charpy notched impact strength -30°C kJ/m²ISO 179-1eA <10<10Charpy notched impact strength -40°C kJ/m²ISO 179-1eA <10<10Izod impact strength 23°C kJ/m²ISO 180-1U 3080Izod impact strength -30°C kJ/m²ISO 180-1U 3030Izod notched impact strength -30°C kJ/m²ISO 180-1A <10<10Izod notched impact strength -40°C kJ/m²ISO 180-1A <10<10Flexural modulus 2mm/min MPa ISO 178********Flexural strength2mm/min MPa ISO 178200120Flexural strain at flexural strength 2mm/min %ISO 178 5.08.0Flexural stress at 3.5%strain 2mm/min MPa ISO 17818090C Puncture maximum force 23°C N ISO 6603-26444C Puncture maximum force -30°C N ISO 6603-2585C Puncture energy 23°C J ISO 6603-24C Puncture energy -30°CJ ISO 6603-23Ball indentation hardness N/mm²ISO 2039-117080Thermal properties C Melting temperature10°C/min °C ISO 11357-1,-3213C Temperature of deflection under load 1.80MPa °C ISO 75-1,-2~190C Temperature of deflection under load 0.45MPa °C ISO 75-1,-2~210C Temperature of deflection under load 8.00MPa °C ISO 75-1,-2~60Vicat softening temperature50N;120°C/h °C ISO 306>200C Coefficient of linear thermal expansion,parallel 23to 55°C 10-4/K ISO 11359-1,-20.3C Coefficient of linear thermal expansion,transverse23to 55°C10-4/KISO 11359-1,-20.8Durethan BKV 15000000Page 1of 3PropertyTest ConditionUnitStandardguide valued.a.m.cond.C Burning behavior UL 94(1.6mm) 1.6mm Class UL 94HB C Burning behavior UL 94 3.2mm Class UL 94HB C Oxygen index Method A %ISO 4589-222Glow wire test (GWFI)2.0mm °C IEC 60695-2-12650Burning behavior US-FMVSS302>=1.0mm ISO 3795<60C Vicat softening temperature50N;50°C/h°CISO 306200Electrical properties (23°C/50%r.h.)C Relative permittivity 100Hz -IEC 60250 4.010C Relative permittivity 1MHz -IEC 60250 4.0 5.0C Dissipation factor 100Hz 10-4IEC 60250502000C Dissipation factor 1MHz10-4IEC 602501501200C Volume resistivity Ohm·m IEC 600931E131E10C Surface resistivity OhmIEC 600931E141E12C Electric strength1mm kV/mm IEC 60243-14035C Comparative tracking index CTI Solution A Rating IEC 60112600Comparative tracking index CTI M Solution BRatingIEC 60112425MOther properties (23°C)C Water absorption (Saturation value)Water at 23°C %ISO 62~8.5C Water absorption (Equilibrium value)23°C;50%RH%ISO 62~2.6C Density kg/m³ISO 11831230Bulk densitykg/m³ISO 60~700Processing conditions for test specimens C Injection molding-Melt temperature °C ISO 294280C Injection molding-Mold temperature °CISO 29480Processing recommendations Drying temperature °C -80Drying time dry air dryer h -2-6Residual moisture content %Acc.to Karl Fischer 0.03-0.12Melt temperature (Tmin -Tmax)°C -260-290Mold temperature°C-80-100C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO10350.Durethan BKV 15000000Page 2of 3DisclaimerDisclaimer for sales productsThis information and our technical advice -whether verbal,in writing or by way of trials -are given in good faith but without warranty,and this also applies whereproprietary rights of third parties are involved.Our advice does not release you from the obligation to verify the information currently provided -especially that contained in our safety data and technical information sheets -and to test our products as to their suitability for the intended processes and uses.The application,use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and,therefore,entirely your own responsibility.Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.Test valuesUnless specified to the contrary,the values given have been established on standardized test specimens at room temperature.The figures should be regarded as guide values only and not as binding minimum values.Kindly note that,under certain conditions,the properties can be affected to a considerable extent by the design of the mould/die,the processing conditions and the coloring.Processing noteUnder the recommended processing conditions small quantities of decomposition product may be given off during processing.To preclude any risk to the health and well-being of the machine operatives,tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at theworkplace in accordance with the Safety Data Sheet.In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products,the prescribed processing temperatures should not be substantially exceeded.Since excessively high temperatures are generally the result of operator error or defects in the heating system,special care and controls are essential in these areas.ConditioningConditioning in accordance with ISO 1110(70°C;62%r.h.)LANXESS DEUTSCHLAND GMBH |D -51369LEVERKUSEN ©LANXESS DeutschlandGmbHDurethan BKV 15000000Page 3of 3。

LEXAN* EXL1414T ResinPolycarbonateSABIC Innovative Plastics/prospectorTechnical Data1of 4Form No.TDS-78422-entemperature (-40°C)ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IMcycle times compared to standard PC.Lexan EXL1414T resin is a general purpose product available in transparent and opaque colors and is an1Features •Copolymer •Ductile•Fast Molding Cycle •General Purpose •Good Processability •Medium FlowUses •General Purpose Appearance•Clear/Transparent •OpaqueProcessing Method •Injection MoldingSpecific Gravity1.19g/cm³ISO 1183Melt Mass-Flow Rate (MFR)(300°C/1.2kg)10g/10min ASTM D1238Melt Volume-Flow Rate (MVR)(300°C/1.2kg)9.50cm³/10minISO 1133Molding Shrinkage Internal MethodFlow:3.20mm0.40to 0.80%Across Flow:3.20mm 0.40to 0.80%Water Absorption ISO 62Saturation,23°C0.12%-- 42190MPa ASTM D638--2310MPa ISO 527-2/1Tensile StrengthYield 557.6MPa ASTM D638Yield56.8MPa ISO 527-2/50Break 559.1MPa ASTM D638Break55.3MPa ISO 527-2/50Tensile ElongationYield 5 5.6%ASTM D638Yield5.4%ISO 527-2/50Break 5120%ASTM D638Break110%ISO 527-2/50Flexural Modulus50.0mm Span 62180MPa ASTM D790-- 72120MPa ISO 178Flexural Strength-- 7, 888.6MPa ISO 178Yield,50.0mm Span 692.0MPaASTM D7902of 4Form No.TDS-78422-enCharpy Notched Impact Strength-30°C 60kJ/m²23°C70kJ/m²Charpy Unnotched Impact Strength 9ISO 179/1eU-30°C No Break 23°CNo BreakNotched Izod Impact-30°C 710J/m ASTM D25623°C 820J/mASTM D256-30°C 1055kJ/m²ISO 180/1A 23°C 1065kJ/m²ISO 180/1A Unnotched Izod Impact Strength 10ISO 180/1U-30°C No Break 23°CNo BreakInstrumented Dart Impact ASTM D3763-30°C,Total Energy 77.4J1.8MPa,Unannealed,3.20mm 121°C ASTM D6481.8MPa,Unannealed,64.0mm Span 11116°C ISO 75-2/Af Vicat SofteningTemperature--139°C ASTM D1525 12ISO 306/B120 12--138°C ISO 306/B50Ball Pressure Test (125°C)PassIEC 60695-10-2CLTEFlow:-40to 95°C 0.000067cm/cm/°C ASTM E831Flow:23to 80°C0.000067cm/cm/°C ISO 11359-2Transverse:-40to 95°C 0.000080cm/cm/°C ASTM E831Transverse:23to 80°C 0.000080cm/cm/°CISO 11359-2RTI Elec 130°C UL 7460.800mm HB 3.00mmV-2 Glow Wire Flammability Index (3.00mm)960°CIEC 60695-2-12Glow Wire Ignition Temperature IEC 60695-2-130.800mm 850°C Haze (2540µm) 3.0%ASTM D1003Drying Time3.0to4.0hr3of 4Form No.TDS-78422-enSuggested Max Moisture 0.020% Suggested Shot Size 40to 60% Rear Temperature 271to 293°C Middle Temperature 282to 304°C Front Temperature 293to 316°C Nozzle Temperature 288to 310°C Processing (Melt)Temp 293to 316°C Mold Temperature 71.1to 93.3°C Back Pressure 0.345to 0.689MPaScrew Speed 40to 70rpm Vent Depth0.025to 0.076mmNotes1 These links provide you with access to supplier literature.We work hard to keep them up to date;however you may find the most current literature from the supplier.2A UL Yellow Card contains UL-verified flammability and electrical characteristics.UL IDES continually works to link Yellow Cards to individual plastic materials in Prospector,however this list may not include all of the appropriate links.It is important that you verify the association between these Yellow Cards and the plastic material found in Prospector.For a complete listing of Yellow Cards,visit the UL Yellow Card Search.3 Typical properties:these are not to be construed as specifications.4 50mm/min5 Type I,50mm/min6 1.3mm/min7 2.0mm/min8 Yield980*10*3sp=62mm 10 80*10*31180*10*4mm12Rate A (50°C/h),Loading 2(50N)4of 4Form No.TDS-78422-enWhere to BuyPittsfield,MA USATelephone:800-845-0600Web :/Telephone :800-531-7106Web :/Availability :North AmericaFounded in1986and based in Laramie,Wyoming,IDES is now part of the UL family of companies.UL is a premier global independent safety science company with more than a century of proven history.Employing nearly10,000 professionals in over100countries,UL has five distinct business units--Product Safety,Environment,Life&Health, Knowledge Services and Verification Services--to meet the expanding needs of our customers and to deliver on our public safety mission.Alternative Resins Search–find replacement plastics within minutes.Automotive Plastics Search–easily locate automotive approved plastics.Curve Data–view,overlay and export curve data.For more information,call:800.788.4668or307.742.9227ext.220。

TPEE杜邦7246物性表注塑参数TPEE美国杜邦Hytrel?7246物性表：产品⽂字提供久隆塑胶原料tEl134********Hytrel?的7246:肖⽒硬度为72D;颜⾊稳定;含抗氧化剂及增塑剂;可与⾷品接触,FDA认证;良好的耐化学性;良好的抗蠕变性;热稳定,抗⾼温氧化性能,可电镀;⾼硬度;减震降噪;⾼性能成型技术，如常规的热塑性树脂加⼯成型:熔体铸造和挤压;120℃时仍有突出的机械性能，优异的烃基电阻和低渗透。

⽤途：管材\电线和电缆护套\齿轮和链轮\流延膜\管道软管及汽车上的应⽤等。

熔体流动指数12.5g/10分ASTM D1238温度240°C-加载 2.16公⽄-成型收缩率（MD）0.016毫⽶/毫⽶ASTM D955密度（73°F）1250公⽄/⽴⽅⽶ASTM D792吸⽔率（24⼩时）0.3％ASTM D570拉伸断裂强度45.8兆帕ASTM D638断裂伸长率360％ASTM D638弯曲模量570兆帕ASTM D790邵⽒D硬度72-ASTM D2240悬臂梁冲击强度缺⼝（1/8）0.21千焦⽿/⽶ASTM D256悬臂梁缺⼝冲击强度（低温）0.04千焦⽿/⽶ASTM D256温度-40°C ASTM D256UL94阻燃等级HB-UL94测试⽤试样的厚度 1.5毫⽶-热膨胀系数（MD）171E-6/K ASTM D696热膨胀系数（TD）180E-6/K ASTM D696DTUL@66PSI130°C ASTM D648DTUL@264磅52°C ASTM D648熔化温度218°C ASTM D3418介电强度（短时间）18.1千伏/毫⽶ASTM D149熔体密度1110公⽄/⽴⽅⽶-熔体的热传导性0.15W/（M K）-产品规格。

熔体的热容量2150J/（千克K）-联邦军。

热扩散 5.44E-8平⽅⽶/秒-喷射温度150°C-TPEE美国杜邦Hytrel?7246加⼯成型参数：⼲燥温度为110°C⼲燥时间，除湿机=2-3⼩时处理⽔分含量<0.08％熔融温度的最佳=245°C模具最适温度为45°C模具温度范围45-55°C保持最佳压⼒= 70MPa。