第1卷　第8期环境工程学报Vol.1,No.82007年8月Chinese Journal of Envir on mental EngineeringAug.2007废电池中氧化锰还原冶炼锰钢的实验研究唱鹤鸣　丁建东(南通大学化学化工学院,南通226007)摘　要　为促进我国锌锰废电池集中资源化处理,开发了一种高温回收废电池中锰的新工艺。

废电池分选后,破碎和筛分,其中二氧化锰与还原剂碳制成球团,烧结后在感应炉中还原锰,制成锰钢。

实验表明,球团中不加表面活性剂的二氧化锰还原率为34%,球团中加入硫化物表面活性剂促进二氧化锰在钢中的还原率,达到80%,钢液中锰含量可达3197%,本实验条件下,还原最佳时间为20m in 。

在铸钢生产中可以直接应用该工艺处理废电池。

关键词　废电池　锰钢　还原动力学　表面活性剂中图分类号　X705 文献标识码　A 文章编号　167329108(2007)0820111203Exper i m en t a l study of reducti on reacti on fro m used ba ttery M nO 2i n steel ref i n em en tChang He m ing D ing J iandong(School of Che m istry and Chem ical Engineering,Nant ong University ,Nant ong 226007)Abstract The ne w technol ogy of recovering manganese fr om used battery in high te mperature has been de 2vel oped in order t o p r omote the centralized treat m ent of used battery in our country .After used battery is separa 2ted,it is crushed and screened .The carbon and black manganese fr om used battery are made int o pellet and then sintered .The manganese steel is refined in inducti on furnace using the pellet .The experi m ents show that reducti on rate of black manganese is 34%if surface active agent is not added t o the pellet,but the reducti on rate of black manganese is 80%by adding sulfide surface active agent int o pellet .The final manganese content is a 2bout 3197%in the liquid steel .Under the conditi ons of the experi m ent,the best reducti on ti m e is 20m inutes .The technol ogy can be used t o treat used battery in the p r oducti on p r ocess of casting steel .Key words used battery;manganese steel;reducti on kinetics;surface active agent基金项目:江苏省教育厅资助项目(02KJB610003);南通大学资助项目(05Z018)收稿日期:2006-10-13;修订日期:2007-04-11作者简介:唱鹤鸣(1955～),男,教授,博士,主要从事固体废物处理技术与设备的研究。

猛氧化物催化剂催化燃烧挥发性有机物的研究进展黎靖程琰孙苓瑕杨楠(西南交通大学地球科学与环境工程学院，四川成都,611756)摘要挥发性有机物(VOCs)广泛存在于大气环境中，是直接引起复合型大气污染的主要原因。

现阶段，催化燃烧技术被称为去除VOCs最有效的方法之一，在一定条件下能够实现VOCs的完全无害化处理&本文从单一型、掺杂型和负载型三种类型的＜氧化物催化剂出发,对＜氧化物催化剂催化燃烧VOCs的最新研究进行了综述，并对未来＜氧化物催化剂的研究提出了展望&关键词：催化燃烧猛氧化物VOCs随着石油、化工行业的日益发展,VOCs逐渐成为环境空气污染物中的主要成分，并引起诸多环境问题,如臭氧、光化学烟雾等。

目前已有多种技术可用于VOCs的处理，如吸附、膜分离、冷凝、直接燃烧、催化燃烧和光催化等&在这些处理技术中，催化燃烧技术能够在较低温度下，对中、低浓度的挥发性有机物实现完全无害化处理，生成二氧化碳和水，不会造成二次污染，因此被认为是一种有效且绿色的处理技术(1)。

催化剂是催化燃烧技术的核心，因此如何设计高效的催化剂是催化燃烧VOCs的关键问题。

常用的催化剂主要有贵金属和过渡金属催化剂。

贵金属催化剂虽然性能优异，但是其成本较高，同时热稳定性较差且容易中毒，从而限制了其工业化的发展&因此,低成本、高稳定性的过渡金属氧化物催化剂得到了更多研究者的青睐。

在众多过渡金属氧化物中,MnO x因为其具有多种可变化合价(+ 2、+3、+4、+7)以及良好的电子转移能力，能够进行快速的氧化还原反应，而表现出优异的催化活性&＜氧化物催化剂的催化活性与其结构、形态、表面化学状态以及多组分间协同作用等多种因素有着密切的关系&本文综述了近年来＜氧化物催化剂对VOCs催化燃烧的相关研究，讨论了单一型、掺杂型和负载型＜氧化物催化剂的结构形态以及对其催化活性的影响，为今后催化燃烧VOCs的研究提供一定参考。

第50卷第10期 辽 宁 化 工 Vol.50，No. 10 2021年10月 Liaoning Chemical Industry October，2021收稿日期： 2021-03-30 作者简介： 李彦秋（1996-），女，吉林省通化市人，硕士，2021年毕业于辽宁石油化工大学工程热物理专业，研究方向：污染气体处理。

锰基催化剂催化氧化VOCs 技术的研究进展李彦秋1，刘人玮1，朱美玉1，高姿乔2（1. 辽宁石油化工大学， 辽宁 抚顺 113001； 2. 中油辽河工程有限公司，辽宁 盘锦 124010）摘 要： 针对挥发性有机化合物（VOCs）有毒有害、污染大气等问题，开展了锰系催化剂催化氧化VOCs 的分类研究。

探讨了单一锰氧化物、锰基复合氧化物、一些特殊的锰基氧化物、锰基负载型催化剂以及锰系单体的催化活性及其影响因素、形貌结构和催化特点等，并对锰系催化剂的改进合成方法提出了建议，为未来锰系催化剂的研究发展提供了方向。

关 键 词：VOCs；低温催化氧化；锰系催化剂；催化机理中图分类号：X701.7 文献标识码： A 文章编号： 1004-0935（2021）10-1502-05VOCs 是一种有机化合物，沸点在室温到260 ℃之间，具有很高的蒸气压，在大气中含量很低，是工业生产过程中无法避免的对人类和大气产生危害的气体之一[1-2]。

因此，为了降低大气污染、保护人类赖以生存的家园，实现可持续发展，控制VOCs 的产生与排放是目前亟待解决的一大技术难题。

催化燃烧工作温度较低，所需燃料较少[3-4]，可以有效地用于处理VOCs 浓度和流速各不相同的废气流[5]，生成的二噁英和毒性物质较少，因此相对而言对环境更友好[6]，常适用于管道末端VOCs 的处理[7]。

通过适当设计催化剂体系，其他有毒反应中间体的形成也可以减至最少。

针对不同种类的VOCs，催化剂主要分成以下3种：贵金属催化剂[8]、非贵金属氧化物催化剂[9]、混合金属催化剂[10]。

生物质还原氧化锰矿中回收钴镍的试验分析
李文斌
【期刊名称】《中国金属通报》
【年(卷),期】2016(000)001
【摘要】本研究选择氧化锰矿还原获得一氧化锰为电解锰原料,选择电解锰调整工艺,沉淀Ni、Co等浸出液,有效富集镍钴。

实验结果得出,氧化锰矿经生物质还原与焙烧后能够提取微量镍钴,5.5：1的最佳固液比,90℃的最佳浸出温度,30min的最佳浸出时间,镍钴浸出率为94%~99%。

【总页数】2页(P42-43)
【作者】李文斌
【作者单位】云南省个旧圣比和实业有限公司云南红河自治州661000
【正文语种】中文
【中图分类】TF815
【相关文献】
1.用ICP-AES法同时测定锰矿中氧化钙、氧化镁、钴、镍、锌、铅、铜含量的应用 [J], 张斯美;吴银军;段宏然
2.从软锰矿酸浸沉淀渣中回收钴镍 [J], 李伯骥;粟海锋;文衍宣
3.氧化焙烧从废弃锰矿中回收钴的研究 [J], 烟伟;金作美
4.从碳酸锰矿中综合回收钴镍的方法研究 [J], 刘登祥;张森;何溯结;李美娴;杨勇;魏汉可
5.软锰矿协同氧化浸出硫化渣回收锰钴镍工艺研究 [J], 曾军;叶有明;陈进中;农永萍;谢雪珍;蔡井泉
因版权原因，仅展示原文概要，查看原文内容请购买。

单宁酸-硫酸体系浸出氧化锰矿中锰的研究
卢友志;苏李敏;赵义
【期刊名称】《无机盐工业》
【年(卷),期】2022(54)6
【摘要】为探究单宁酸作为还原剂在硫酸体系中浸出还原低品位软锰矿中锰的可行性,通过单因素实验考察了单宁酸用量、反应时间、反应温度、硫酸浓度等因素对锰浸出率的影响。

基于单因素实验结果,通过响应曲面法对工艺参数进行了进一步优化。

研究结果表明,在单宁酸用量为3倍理论量、反应时间为3 h、硫酸浓度为1.5 mol/L、反应温度为90℃条件下,锰矿中锰的浸出率达到90.86%。

反应参数对锰浸出率的影响由大到小的顺序依次为反应温度、单宁酸用量、反应时间、硫酸浓度。

该工艺具有锰浸出率较高、硫酸初始浓度低的特点。

【总页数】6页(P84-89)
【作者】卢友志;苏李敏;赵义
【作者单位】桂林理工大学南宁分校
【正文语种】中文
【中图分类】TQ137.12
【相关文献】
1.建水氧化锰矿直接浸出制取硫酸锰溶液的小型试验
2.用二氧化硫浸出软锰矿制备的硫酸锰产品的净化、结晶研究
3.硫酸化焙烧氧化锰矿浸出锰的循环工艺
4.铁强
化电解锰阳极液体系中氧化锰矿烟气脱硫和锰浸出工艺5.氧化锰矿直接浸出生产硫酸锰
因版权原因，仅展示原文概要，查看原文内容请购买。

低品位软锰矿还原技术的研究进展李康强1，李鑫培1，和飞1，陈菓2,3，陈晋1*(1.昆明理工大学非常规冶金教育部重点实验室，云南昆明650093；2.云南民族大学云南省高校民族地区资源清洁转化重点实验室，云南昆明650500；3.中南大学锰资源高效清洁利用湖南省重点实验室，湖南长沙410083)摘要：锰在钢铁工业、有色冶金、电池、电子等领域的应用日益广泛。

为提高大量低品位软锰矿的资源利用率，特别是由软锰矿生产一氧化锰工艺的优化，进一步降低生产成本，从而推进低品位锰矿资源的高效利用和锰系产品的质量升级。

本文对近年来低品位软锰矿的还原工艺及研究进展进行了综述，同时针对不同的低品位软锰矿湿法浸出工艺，重点介绍其还原剂的选择和应用，为合理开发利用不同的低品位软锰矿提供了理论依据。

关键词:低品位软锰矿；微波还原；直接还原浸出；生物质热解还原Review of reduction technology of low grade pyrolusite LI Kangqiang1, LI Xinpei1, HE Fei1, CHEN Guo2,3, CHEN Jin1,*(1. Key laboratory of Unconventional Metallurgy, Ministry of Education, Kunming University ofScience and Technology, Kunming, Yunnan 650093, China;2. Key Laboratory of Resource Clean Conversion in Ethnic Regions, Education Department ofYunnan, Yunnan Minzu University, Kunming, Yunnan 650500, China;3. Hunan Provincial Key Laboratory of Efficient and Clean Utilization of Manganese Resources,Central South University, Changsha, Hunan 410083, China)Abstract:Manganese has been widely applied in the steel industry, non-ferrous metallurgy, batteries, electronics and other fields. Therefore, for improving the resource utilization rate of a large number of low-grade pyrolusite, especially the optimization of the process of producing manganese monoxide from pyrolusite, and reducing the production cost, further to promote the efficient utilization of low-grade manganese ore resources and the quality upgrade of manganese products, the reduction process and research progress of low-grade pyrolusite in recent years were reviewed in this paper; moreover, the selection and application of reducing agent in wet leaching low-grade pyrolusite process were introduced, aiming at providing a theoretical basis for the rational development and utilization of different low-grade pyrolusite.Keywords: low-grade pyrolusite; microwave reduction; direct reduction leaching; biomass pyrolysis reduction0引言锰是重要的是国家战略储备资源。

锰氧化物合成及催化酯化反应的研究摘要：本论文通过对一系列纳米结构锰氧化物的制备及对其性质的表征，旨在寻找具有特殊性能的新型催化剂及其制备方法。

实验利用Zn(Ac)2和Mn(Ac)2为原料，H2O2为氧化剂在NaOH溶液中共沉淀制备ZnMn2O4。

基于这种方法，改变反应条件（反应物摩尔配比，氧化剂用量，陈化时间，反应温度等）最终在常温常压的温和条件下得到了单一晶形的均匀纳米颗粒，粒径在10nm ~20nm。

同时也利用水热法制得了α-MnO2纳米线，λ-MnO2纳米颗粒。

最后利用XRD，TEM对所制得的产品进行表征。

利用在不同条件下制得的一系列锰的氧化物催化合成乙酸异戊酯，分别得到其酯化率为：α-MnO2纳米线：80%左右；λ-MnO2纳米颗粒：86%左右；ZnMn2O4（煅烧200℃~500℃）：88%~94%。

关键词：纳米结构锰氧化物；纳米颗粒；水热法；乙酸异戊酯；酯化率Abstract: In order to look for the method of preparing new pattern of catalyst，which had some special performances, we prepared a chain of nanostructured manganeseoxides and attributed their behavior in this articles. Zn(Ac)2 and Mn(Ac)2 wereused to prepare ZnMn2O4 in the NaOH solution by the oxidizer of H2O2. Basedon such a method, we transferred reaction conditions, such as the mol matchingof the reactant, oxidizer dosage, ageing time , reaction temperature and so on.Ultimately, we had received unique crystal form and uniform nanoparticles,their diameter is about 10nm ~20nm. Meanwhile, α-MnO2nanolines and λ-MnO2 nanoparticles were synthesized by the method of hydrothermal synthesis.Finally，XRD and TEM techniques were used to characterize the as-preparedproducts. Then we synthesized isoamyl acetate by using manganic oxide thatbeen synthesized in different condition. The esterification ratio was concludedthat α-MnO2nanolines: about 80%, λ- MnO2nanoparticles: about 86%,ZnMn2O4 (furnacing200℃~ 500℃)：88%~94%.Keywords: nanostructured manganese oxides; nanoparticles; hydrothermal synthesis;isoamyl acetate; esterification ratio毕业设计（论文）原创性声明和使用授权说明原创性声明本人郑重承诺：所呈交的毕业设计（论文），是我个人在指导教师的指导下进行的研究工作及取得的成果。

氧化锰矿还原工艺技术研究进展武芳芳;钟宏;王帅【摘要】介绍焙烧还原和湿法还原两大类还原浸出氧化锰矿的还原工艺和研究进展.研究表明,相对传统的焙烧工艺,湿法还原浸出法具有广阔的研究前景和应用背景,且生物质湿法浸出氧化锰矿的过程将成为进一步研究的方向.%The processes of manganese oxide ores reduction treatment which includes reducing roasting and hydrometallurgical and its recent research advance was also presented. The results showed that compared with reducing roasting process, the hydrometallurgical reducing process of manganese oxide has broad prospects of research and application, and the reduction leaching of manganese oxide using biomass as reductant will become the future research trend in the field of manganese oxide ores reduction process.【期刊名称】《应用化工》【年(卷),期】2012(041)008【总页数】5页(P1443-1447)【关键词】氧化锰矿;还原剂;还原工艺【作者】武芳芳;钟宏;王帅【作者单位】中南大学化学化工学院有色金属资源化学教育部重点实验室,湖南长沙410083;中南大学化学化工学院有色金属资源化学教育部重点实验室,湖南长沙410083;中南大学化学化工学院有色金属资源化学教育部重点实验室,湖南长沙410083【正文语种】中文【中图分类】TF792锰是钢铁冶炼中不可缺少的重要原料之一，无锰不成钢。

生物锰氧化物的合成及其在重金属去除中的应用Sythesis of biogenic manganese oxide and its application for heavy metalsremovalAbstractManganese oxidizing bacteria is a type of phylogenetical microbe which can oxidizes soluble Mn2+ into insoluble Mn3+/Mn4+ oxides. Nowadays, there are plenty of reports about pure cultured manganese oxidizing bacteria (MnOB), but rare work concerned on the manganese oxidizing consortium. In terms of application, manganese oxidizing consortium was more suitable than pure cultured MnOB. This work was performed to obtain an acclimated microbial consortium from the marine sediments and conduct the 16S rRNA gene sequencing of microbial consortium. Then the growth and Mn2+oxidation performance of microbial consortium in various conditions was investigated. The results showed that a significantly shift has taken place during the acclimation process. In the phylum level, the relative abundance of Proteobacteria firstly decrease from 56.72% to 35.1%, and then increase again to 76.12%. When the initial concentration of Mn2+ was up to 5 mM, the consortium could still oxidize manganese ion. Metal ions had different effects on Mn2+oxidation performance of community and Zn2+ ,Co2+ and Cd2+ restrained the Mn2+ oxidation capacity to varying degree, but Fe3+ could accelerate the rate of Mn2+ oxidation. pH 7.0 and the salinity below 3.5% are suitable for growth and Mn2+ oxidation of community. The characterization results showed that the BioMnO X was amorphous with specific surface area of 31-41 m2 g-1.In order to study the heavy metals removal efficiency which performed in bioreactor by manganese oxidizing consortium, we firstly studied the heavy metals removal by BioMnO X only. Element mapping and N2 adsorption/desorption curves indicated that it contains C, O, N, Mn and Fe elements, and with specific surface area of 81.426 m2 g-1. Then BioMnO X was used to adsorb various heavy metals, and the results showed that BioMnO X have stronger affinity for Pb2+over other metal ions. The results of FTIR and exciation-emission matrix fluoscence spectra indicated that the amide group, hydroxyl group, tryptophan protein-like molecules and aromatic protein-like molecules on BioMnO X surface plays an important role in adsorption of Pb2+. The adsorption of Pb2+ on BioMnO X could be approximated favorably by pseudo-second-order model and Langmuir model, and the maximum adsorption capacity of Pb2+ was 507.61 mg g-1. The adsorption was spontaneous of monolayer adsorption and exothermic process. It also suggested that the chemisorption was main process in the adsorption of Pb2+.Finally, we attempted to enrich MnOB in bioreactor and produce BioMnO X in situ to remove Mn2+. We built the biological aerated filter (BAF) bioreactor and moving bed biofilm reactor (MBBR) to remove Mn2+. The results showed that the removal efficiency of Mn2+ by BAF was unstable. The falling biofilm has a bad effluent quality. However, the MBBR kept theremoval of Mn2+ and the removal efficiency of Mn2+ was up to 86.53% when the influent Mn2+ concentration was 5.5 mg L-1. Therefore, the MBBR is more suitable for enriching MnOB and produce BioMnO X in situ.Key words:manganese oxidizing consortium; biogenic manganese oxide; heavy metal; adsorption; biofilm reactor生物锰氧化物的合成及其在重金属去除中的应用目录摘要 (I)Abstract (II)引言 (1)1 绪论 (2)1.1 重金属污染现状 (2)1.1.1 重金属污染的来源 (2)1.1.2 重金属的危害 (2)1.1.3 重金属污染的处理方法 (3)1.2 锰氧化菌 (7)1.2.1 锰氧化菌的种类 (7)1.2.2 锰氧化菌氧化Mn2+的原因 (7)1.3 锰氧化物 (8)1.3.1 化学合成的锰氧化物 (9)1.3.2 生物锰氧化物 (10)1.3.3 生物锰氧化物的应用 (10)1.4 研究目的、内容和研究路线 (12)1.4.1 研究目的 (12)1.4.2 研究内容 (12)2 锰氧化微生物群落的驯化及锰氧化特性研究 (14)2.1 材料和方法 (14)2.1.1 实验材料 (14)2.1.2 实验方法 (16)2.2 结果与讨论 (19)2.2.1 锰氧化微生物群落的解析及鉴定结果 (19)2.2.2 不同培养条件对群落的锰氧化性能的影响 (20)2.2.3 生物锰氧化物的表征 (24)2.3 结论 (27)3 生物锰氧化物的特性及其对重金属的吸附 (28)3.1 材料和方法 (28)3.1.1 生物锰氧化物的合成 (28)3.1.2 生物锰氧化物的表征 (28)3.1.3 生物锰氧化物对金属离子的吸附性能 (29)3.1.4 生物锰氧化物对Pb2+的吸附动力学 (29)3.1.5 生物锰氧化物对Pb2+的吸附等温线 (30)3.1.6 生物锰氧化物对Pb2+的吸附热力学 (31)3.2 结果与讨论 (31)3.2.1 生物锰氧化物的表征 (31)3.2.2 生物锰氧化物对金属离子的吸附性能 (40)3.2.3 生物锰氧化物吸附Pb2+的吸附动力学 (41)3.2.4 生物锰氧化物对Pb2+的吸附等温线 (43)3.2.5 生物锰氧化物对Pb2+的吸附热力学 (46)3.3 结论 (47)4 生物膜反应器对Mn2+的去除 (48)4.1 BAF生物膜反应器对Mn2+的去除 (48)4.1.1 BAF反应器的构建和操作条件 (48)4.1.2 分析方法 (49)4.1.3 结果与讨论 (49)4.2 MBBR生物膜反应器对Mn2+的去除 (51)4.2.1 MBBR反应器的构建和操作条件 (52)4.2.2 分析方法 (53)4.2.3 结果与讨论 (53)4.3 结论 (55)结论 (56)1 结论 (56)2 展望 (57)3 创新点 (57)参考文献 (58)攻读硕士学位期间发表学术论文情况 (66)致谢 (67) (68)引言重金属的挖掘与使用在现代工业中具有至关重要的作用，如采矿、冶金、制革、化学工业等行业，产生的大量含有重金属的废水，这些废水如果未经处理直接排放，将造成严重的环境污染。

生物有机物还原软锰矿研究进展黄秀兰;李毅恒;冯康露;何奥希;陈菓;彭金辉【期刊名称】《中国锰业》【年(卷),期】2017(035)006【摘要】锰在我国钢铁工业中是一种不可或缺的金属,在其中充当着脱氧剂、脱硫剂、合金元素等角色,并且在电池、电子、建筑材料及农业领域中均有应用.虽然我国锰矿资源多,但可利用的高品位锰矿资源日益降低.要实现锰资源的高效利用,就需要找到合适经济的还原剂还原锰矿.以生物质、有机物质、生物细菌等作为还原剂近年来被许多研究人员所报道.研究结果表明:以生物有机物作为还原剂既提高了锰的还原浸出效率,又实现了生物有机物的循环再生利用,对环境无危害.总结了近年来国内外生物有机还原软锰矿的研究进展,主要阐述了以生物质还原剂、有机还原剂及生物细菌还原剂等还原锰矿的研究工作.【总页数】6页(P140-145)【作者】黄秀兰;李毅恒;冯康露;何奥希;陈菓;彭金辉【作者单位】云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500;云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500;云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500;云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500;云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500;中南大学锰资源高效清洁利用湖南省重点实验室,湖南长沙 410083;云南民族大学云南省高校民族地区资源清洁转化重点实验室,云南昆明 650500;云南民族大学云南省跨境民族地区生物质资源清洁利用国际联合研究中心,云南昆明 650500【正文语种】中文【中图分类】TQ137.12【相关文献】1.生物质焦焙烧还原低品位软锰矿的研究 [J], 武改琴2.生物质焦焙烧还原低品位软锰矿及其动力学 [J], 冯雅丽;张士元;李浩然;周宇照3.低品位软锰矿还原技术研究进展 [J], 李康强;李鑫培;和飞;陈菓;陈晋4.低品位软锰矿无机还原浸出研究进展 [J], 卢友志; 黄润均; 王军正5.生物质三组分还原软锰矿的TG-FTIR分析（英文） [J], 龙云飞;阮乐;吕小艳;吕奕菊;苏静;文衍宣因版权原因，仅展示原文概要，查看原文内容请购买。

甲酸还原硫酸浸出低品位氧化锰矿卢友志;马华菊;黄润均;袁爱群;黄增尉;周泽广【摘要】研究了甲酸作为还原剂在硫酸介质中还原浸出低品位氧化锰矿的工艺.采用单因素试验研究了甲酸用量、硫酸浓度、反应温度、反应时间及液固比对锰、铁、铝3种金属浸出率的影响.利用XRD和SEM对矿粉和矿渣的成分和表面形貌进行了分析和表征,利用响应曲面法对还原浸出条件进行了优化.结果表明,各因素影响浸出率的主次顺序为甲酸用量＞硫酸浓度＞反应温度＞反应时间.当硫酸体积分数为15％,液固比为6,甲酸用量0.4 mL/g,反应时间2h,反应温度90℃时,锰浸出率最大,为90.05％,此时铁和铝浸出率为80.07％和31.55％.【期刊名称】《矿冶工程》【年(卷),期】2015(035)006【总页数】4页(P93-96)【关键词】氧化锰矿;锰;甲酸;硫酸;还原浸出【作者】卢友志;马华菊;黄润均;袁爱群;黄增尉;周泽广【作者单位】广西民族大学化学化工学院化学与生物转化过程新技术重点实验室,广西南宁530006;桂林理工大学南宁分校,广西南宁530001;桂林理工大学南宁分校,广西南宁530001;广西民族大学化学化工学院化学与生物转化过程新技术重点实验室,广西南宁530006;广西民族大学化学化工学院化学与生物转化过程新技术重点实验室,广西南宁530006;广西民族大学化学化工学院化学与生物转化过程新技术重点实验室,广西南宁530006【正文语种】中文【中图分类】TF803.2由于高品位锰矿石枯竭，中低品位锰矿石的开发利用引起广泛关注[1]。

火法还原、湿法还原和生物浸出是目前氧化锰矿还原利用的主要方式。

火法还原中的两矿[2]、单质硫[3]、木屑[4]、玉米秸秆[5]等还原剂在工艺实践中存在能源消耗大、污染严重等问题。

生物浸出具有消耗小、环保等优点，但能够用于工业生产的菌种很少。

湿法还原生产成本低、浸出率也能满足工业需求，柚子皮[6]、燕麦秸秆[7]、黄原胶废水[8]等生物质还原剂都被报道过，但在规模化生产中发现这些还原剂还原后产生大量的衍生有机物，严重影响硫酸锰的电解，造成阳极板爆板、黑板等问题。