基金项目:广东省教育部产学研结合项目(2007A090302034)新型锂盐———二氟草酸硼酸锂付茂华1,刘素琴1,刘建生2,李永坤2(11中南大学化学化工学院,湖南长沙 410083; 21广州天赐高新材料股份有限公司,广东广州 510760)摘要:介绍了二氟草酸硼酸锂(LiODFB )的基本特性。
LiODFB 作为锂盐用于电解液中,对不同正极和石墨负极有良好的相容性,能显著提高电池的高、低温性能。
综述了LiODFB 在锂离子电池中的应用情况。
关键词:二氟草酸硼酸锂; 电解液; 锂离子电池中图分类号:TM91219 文献标识码:A 文章编号:1001-1579(2009)06-0316-03A ne w lithium salt ———lithium oxalyldifluoroborateFU Mao 2hua 1,L IU Su 2qin 1,L IU Jian 2sheng 2,L I Y ong 2kun 2(11College of Chemist ry &Chemical Engineering ,Cent ral South U niversity ,Changsha ,Hunan 410083,China ;21Guangz hou Tinci M aterials Technology Co 1,L td 1,Guangz hou ,Guangdong 510006,China )Abstract :The character of lithium oxalyldifluoroborate (LiODFB )was introduced 1LiODFB used as a lithium salt in electrolyte hadgood compatibility with different cathodes and graphite anode ,could improve the performance of Li 2ion battery at high temperature and low temperature obviously 1The application of LiODFB used in Li 2ion battery was reviewed 1K ey w ords :lithium oxalyldifluoroborate ; electrolyte ; Li 2ion battery 电解质锂盐的性质决定了电解液的基本电化学性能[1]。
2024年二氟草酸硼酸锂(LiODFB)市场调研报告1. 引言1.1 背景信息二氟草酸硼酸锂(LiODFB)是一种重要的化学品，在电池制造、电子材料和药物制造等领域有广泛应用。
本报告旨在对全球二氟草酸硼酸锂市场进行调研，分析其市场现状、发展趋势和主要参与者。
1.2 研究目的本报告的研究目的如下：•了解全球二氟草酸硼酸锂市场的规模和增长趋势；•分析二氟草酸硼酸锂的主要应用领域和市场需求；•调查二氟草酸硼酸锂的生产方式和产量分布；•研究全球二氟草酸硼酸锂市场的竞争格局和主要企业。
2. 方法本次市场调研采用了以下方法：•收集二氟草酸硼酸锂相关的市场数据和研究报告；•分析二氟草酸硼酸锂的生产工艺和产能；•调查并分析二氟草酸硼酸锂的主要应用领域；•调研全球二氟草酸硼酸锂市场的竞争格局；•分析二氟草酸硼酸锂市场的发展趋势。
3. 市场规模和增长趋势根据市场调研数据，二氟草酸硼酸锂市场的规模呈现稳步增长的趋势。
预计在未来几年内，市场规模将继续扩大，并且以较快的速度增长。
这主要归因于二氟草酸硼酸锂在电池制造、电子材料和药物制造等领域的广泛应用。
4. 应用领域和市场需求二氟草酸硼酸锂在电池制造领域具有重要意义，特别是在锂离子电池和锂硫电池的生产中。
此外，在电子材料和药物制造领域，二氟草酸硼酸锂也有广泛应用需求。
随着新能源行业的发展和科技进步，对二氟草酸硼酸锂的市场需求将进一步增长。
5. 生产方式和产量分布目前，二氟草酸硼酸锂的生产主要采用化学合成法。
产量分布主要集中在亚洲地区，特别是中国。
亚洲地区拥有丰富的资源和成熟的生产工艺，使其成为全球二氟草酸硼酸锂产量最大的地区。
6. 竞争格局和主要企业全球二氟草酸硼酸锂市场的竞争格局相对分散，市场上存在多个厂商和供应商。
国内外企业竞争激烈，技术创新和产品质量是企业竞争的关键因素。
目前，在市场上占据较大份额的企业有A公司、B公司和C公司等。
7. 发展趋势随着新能源行业的高速发展和能源转型的推进，二氟草酸硼酸锂市场有望继续保持快速增长。
作者简介:崔孝玲(1980-),女,山东人,兰州理工大学石油化工学院助教,硕士,研究方向:功能材料和锂离子电池材料;李世友(1980-),男,山东人,兰州理工大学石油化工学院讲师,博士,研究方向:锂离子电池,本文联系人;骆建国(1985-),男,甘肃人,兰州理工大学石油化工学院本科生,研究方向:锂离子电池材料。
基金项目:兰州理工大学科研发展基金(SB05200903)电解质锂盐草酸二氟硼酸锂的研究进展崔孝玲,李世友,骆建国(兰州理工大学石油化工学院,甘肃兰州 730050)摘要:介绍了电解质锂盐草酸二氟硼酸锂(LiODFB )的制备进展及在锂离子电池中的应用。
LiODFB 与常用电极材料表现出良好的匹配性,所组装电池的高低温性能优良、倍率放电性能较好、安全性能较高,有望成为动力电池用电解质锂盐。
关键词:草酸二氟硼酸锂(LiODFB ); 双草酸硼酸锂(LiBOB ); LiBF 4; LiPF 6; 电解液中图分类号:TM91219 文献标识码:A 文章编号:1001-1579(2009)04-0233-03R esearch progress in electrolyte lithium salt lithium oxalyldifluoroborateCU I Xiao 2ling ,L I Shi 2you ,L UO Jian 2guo(College of Pet rochemical Technology ,L anz hou U niversity of Technology ,L anz hou ,Gansu 730050,China )Abstract :The progress in preparation of electrolyte lithium salt lithium oxalyldifluoroborate (LiODFB )and its application in Li 2ionbattery were introduced 1LiODFB showed fine compatibility with common electrode materials ,the battery assembled with it had good high temperature and low temperature performance ,fine rate discharge performance and favorable safety performance 1It was expected to become an electrolyte lithium salt of power battery 1K ey w ords :lithium oxalyldifluroborate (LiODFB ); lithium bis (oxalate )borate (LiBOB ); LiBF 4; LiPF 6; electrolyte 目前,商品化锂离子电池的电解质主要为LiPF 6及LiBF 4。
二氟草酸硼酸锂的制备与性能研究王永勤;郭贤慧;王建萍;许胜霞【摘要】以无水氯化铝为催化剂,以四氟硼酸锂和无水草酸为原料,制备高纯二氟草酸硼酸锂(LiODFB).研究了反应时间、反应温度和反应物配比(四氟硼酸锂与草酸物质的量比)对产品纯度的影响以及结晶温度和结晶时间对产品收率的影响.实验结果表明,在反应温度为10℃、反应时间为4h、反应物配比为1∶1、结晶温度为-20℃、结晶时间为4h条件下,制得LiODFB的纯度可达99.97％、收率可达95.9％.另外,以LiODFB作为电解液添加剂,可以有效改善锂电池的高温、常温和低温性能.【期刊名称】《无机盐工业》【年(卷),期】2018(050)009【总页数】4页(P46-49)【关键词】二氟草酸硼酸锂;无水氯化铝;四氟硼酸锂【作者】王永勤;郭贤慧;王建萍;许胜霞【作者单位】多氟多化工股份有限公司,河南焦作454006;多氟多化工股份有限公司,河南焦作454006;多氟多化工股份有限公司,河南焦作454006;多氟多化工股份有限公司,河南焦作454006【正文语种】中文【中图分类】TQ131.11目前，锂离子电池已经在人们的生活中起着越来越重要的作用。
但是，锂电池技术仍然存在一定的问题，其中最主要的原因就是锂电池中使用的电解质为六氟磷酸锂（LiPF6）。
LiPF6存在对水分非常敏感、高温性能不稳定以及分解产物HF对电极材料有腐蚀性等问题，从而导致锂电池的安全性能较差［1］。
同时，在低温环境中LiPF6也存在溶解性较差、电导率较低和锂离子迁移阻抗较大等问题，无法满足动力锂离子电池的使用要求［2］。
因此，开发性能优异的新型电解质锂盐引起相关研究者的兴趣。
迄今为止，研究机构已经开发出多种新型电解质锂盐，比较有代表性的就是四氟硼酸锂（LiBF4）和双草酸硼酸锂（LiBOB）。
其中，LiBOB具有高温不易分解、对水分不敏感、合成工艺简单无污染、电化学稳定窗口较宽且能够在负极表面形成良好的SEI膜等优点。
二氟草酸硼酸锂的制备与性能研究王永勤,郭贤慧,王建萍,许胜霞(多氟多化工股份有限公司,河南焦作454006)摘要:以无水氯化铝为催化剂,以四氟硼酸锂和无水草酸为原料,制备高纯二氟草酸硼酸锂(LiODFB )。
研究了反应时间、反应温度和反应物配比(四氟硼酸锂与草酸物质的量比)对产品纯度的影响以及结晶温度和结晶时间对产品收率的影响。
实验结果表明,在反应温度为10℃、反应时间为4h 、反应物配比为1∶1、结晶温度为-20℃、结晶时间为4h 条件下,制得LiODFB 的纯度可达99.97%、收率可达95.9%。
另外,以LiODFB 作为电解液添加剂,可以有效改善锂电池的高温、常温和低温性能。
关键词:二氟草酸硼酸锂;无水氯化铝;四氟硼酸锂中图分类号:TQ131.11文献标识码:A文章编号:1006-4990(2018)09-0046-04Study on preparation and properties of lithium-difluoro(oxalato)borateWang Yongqin ,Guo Xianhui ,Wang Jianping ,Xu Shengxia(Do-Fluoride Chemicals Co.,Ltd.,Jiaozuo 454006,China )Abstract :Lithium ⁃difluoro (oxalato )borate (LiODFB )with high purity was synthesized by the raw materials of lithium tetra ⁃fluoroborate and anhydrous oxalic acid ,with anhydrous aluminum chloride as the catalyst.The influences of reaction time ,re ⁃action temperature ,and the amount ⁃of ⁃substance ratio of lithium tetrafluoroborate to anhydrous oxalic acid on the purity of product and the influences of crystallization temperature and crystallization time on the yield of product were investigated.The best conditions were described as follows :the reaction temperature was 10℃,the reaction time was 4h ,the amount ⁃of ⁃sub ⁃stance ratio of the reaction materials was 1∶1,the crystallization temperature was -20℃and the crystallization time was 4h.Under the best conditions ,the purity of LiODFB was 99.97%and the yield was 95.9%.In addition ,adding LiODFB in elec ⁃trolyte could effectively improve the performance of battery at high temperature ,room temperature and low temperature.Key words :lithium ⁃difluoro (oxalato )borate ;anhydrous aluminum chloride ;lithium tetrafluoroborate目前,锂离子电池已经在人们的生活中起着越来越重要的作用。
2024年二氟草酸硼酸锂(LiODFB) 市场分析现状简介二氟草酸硼酸锂(LiODFB)是一种重要的锂离子电池电解液添加剂。
本文将对LiODFB市场的现状进行分析，并探讨其未来的发展趋势。
市场规模根据市场调研数据显示，近年来全球LiODFB市场规模呈逐年增长的趋势。
预计到2025年，全球LiODFB市场规模将达到XX亿美元。
市场驱动因素LiODFB作为锂离子电池电解液的重要组成部分，其市场需求受多个因素的驱动。
锂离子电池需求增加随着电动汽车及可再生能源市场的快速发展，对高性能锂离子电池的需求不断增加。
而作为电解液添加剂的LiODFB的需求也相应增加。
锂电池技术进步锂电池技术不断进步，推动了LiODFB市场的增长。
新一代锂离子电池的发展，使得对更高纯度的LiODFB及更高性能的电解液添加剂的需求增加。
政府政策支持各国政府鼓励电动交通工具的普及和可再生能源的发展，并出台一系列政策和补贴措施，促进锂离子电池产业的发展。
这些政策支持也推动了LiODFB市场的增长。
市场竞争格局目前，全球LiODFB市场竞争格局较为分散，主要的市场参与者包括A公司、B公司和C公司等。
这些公司在技术研发、生产规模和市场份额等方面存在差异。
市场趋势和机遇未来LiODFB市场面临着一些趋势和机遇。
新能源汽车市场增长预计未来几年，新能源汽车市场将保持快速增长，进一步推动LiODFB市场的发展。
新技术的应用随着锂离子电池技术的不断创新，新技术的应用将进一步提升电池性能和安全性。
这将对LiODFB市场带来新的机遇。
环保意识提升环保意识的提升促使人们寻求更清洁、可持续的能源解决方案。
作为一种绿色环保的电解液添加剂，LiODFB有望受益于此。
挑战和风险除了机遇，LiODFB市场也面临一些挑战和风险。
市场竞争加剧随着市场规模的扩大，竞争也越发激烈。
公司需要不断提高产品质量和技术水平，以保持竞争优势。
材料成本波动LiODFB的生产涉及到原材料成本和能源成本等方面的考量。
第35卷第6期2007年6月化 工 新 型 材 料N EW CH EMICAL MA TERIAL S Vol 135No 16・39・作者简介:谢辉(1983-),男,博士。
可用于锂离子电池的新型锂盐:LiODFB谢 辉13 唐致远1 李中延2(11天津大学化工学院,天津300072;21东莞市迈科科技有限公司,东莞523700)摘 要 介绍一种新型的可用于锂离子电池的锂盐:LiODFB (lithium oxalyldifluoroborate )。
LiODFB 独特的化学结构,使其结合了双乙二酸硼酸锂(LiBOB )及四氟硼酸锂(LiBF 4)的优势。
与LiBOB 相比,LiODFB 在碳酸酯中的溶解性和溶剂的黏度有了明显改善,从而使锂离子电池具有更好的低温性能和倍率放电性能。
而与LiBF 4相比,LiODFB 能促进稳定固态电解液界面(solid electrolyte interface ,SEI )的形成,改善了锂离子电池的高温性能。
该种新型锂盐还具有以下优点:与金属锂的化学稳定性好,在高电位下能够很好地使铝箔得到钝化和提高锂离子电池安全性能及抗过充的能力。
这些性能使得LiODFB 成为一种极有可能替代LiPF 6的新型锂盐。
关键词 锂盐,LiODFB ,LiBOB ,锂离子电池LiODFB :A unique lithium salt for lithium ion batteryXie Hui 1 Tang Zhiyuan 1 Li Zhongyan 2(11School of Chemical Engineering and Technology ,Tianjin U niversity ,Tianjin 300072;21McNair Technology Co.,Ltd.,Dongguan ,523700)Abstract We introduced a latest developed lithium salt ,lithium oxalyldifluoroborate as a candidate for lithium ion batteries.The research indicated that due to its unique chemical structure ,LiODFB combined advantages of Lithium bis (oxalato )borate (LiBOB )and LiBF pared with LiBOB ,an apparent improvement has been shown that the salt was more soluble in carbonates and the solutions so 2formed were less viscous ,which made lithium ion batteries with better low temperature and high rate performance.And compared with LiBF4,LiODFB was capable to facilitate the formation of sta 2ble solid electrolyte interface on the surface of metallic lithium or graphite anode ,which enables lithium ion batteries to be operated at high temperature properly.This brand new type lithium salt also has other merits ,including the chemical com 2patibility with metallic lithium ,the ability to passivate aluminum foil at high potentials and the capability to increase lithi 2um ion batteries safety and overcharge tolerance.These properties make LiODFB a potential substitute for LiPF6.K ey w ords lithium salt ,lithium oxalyldifluoroborate ,LiBOB ,lithium ion battery 锂离子电池自诞生并在1991年被Sony 公司商品化以来,由于其优越的性能,一直受到广大消费者的青睐,其应用领域主要有:便携式电子产品、可植入医疗设备(implantable medical devices )以及电动工具(electric vehicles or hybrid elec 2tric vehicles )等[1,2]。
专利名称：一种锂离子电池电解质盐草酸二氟硼酸锂(LiODFB)的制备方法
专利类型：发明专利
发明人：周宏明,孙文佼,李荐
申请号：CN201510049889.7
申请日：20150201
公开号：CN104628754A
公开日：
20150520
专利内容由知识产权出版社提供
摘要：本发明涉及一种锂离子电池电解质盐草酸二氟硼酸锂（LiODFB）的制备方法。
该方法包括草酸锂和三氟化硼乙醚在碳酸二甲酯（DMC）等溶剂中催化合成得到含草酸二氟硼酸锂和四氟硼酸锂（LiBF4）的液相混合物和少量未反应的草酸锂固体，过滤后蒸发结晶，得到粗产品LiODFB。
粗产品LiODFB经过重结晶后符合锂离子电池电解质盐的要求。
收集过滤后的母液和结晶母液，加入草酸和催化剂，催化转化得到主要含LiODFB的液相混合物，再返回到蒸发结晶。
该工艺流程成本低廉，制备得到的草酸二氟硼酸锂（LiODFB）的纯度达到99.9%以上，产率在90%以上，操作方便，具有良好的经济效益和环境效益，适合工业化生产。
申请人：湖南省正源储能材料与器件研究所,中南大学
地址：410083 湖南省长沙市岳麓区麓山南路932号
国籍：CN
更多信息请下载全文后查看。