MoldFlow分析结果各项概念解释
- 格式：doc
- 大小：49.00 KB
- 文档页数：7
MPI初学者园地： MoldFlow分析结果讲习！！！
分析结果解释
分析结果的一个重要部分是理解结果的定义，并知道怎样使用结果。下面将列出常用结果的定义及怎样使用。
屏幕输出文件（screen output）和结果概要（results summary）
屏幕输出文件和结果概要都包含了一些分析的关键结果的总结性信息。屏幕输出文件还包含如图169所示的附加输出，表明分析正在进行，同时还提供重要信息。从它可以看出分析使用的压力和锁模力的大小、流率的大小和使用的控制类型。
Filling phase: Status: V = Velocity control
P = Pressure control
V/P= Velocity/pressure switch-over
|-------------------------------------------------------------|
| Time | Volume| Pressure | Clamp force|Flow rate|Status |
| (s) | (%) | (MPa) | (tonne) |(cm^3/s) | |
|-------------------------------------------------------------|
| 0.25 | 4.20 | 7.71 | 4.34 | 441.92 | V |
| 0.50 | 8.87 | 12.20 | 16.95 | 485.10 | V |
| 0.74 | 13.48 | 15.99 | 38.17 | 480.56 | V |
| 0.98 | 17.98 | 20.85 | 79.31 | 480.06 | V |
| 1.23 | 22.65 | 25.65 | 134.77 | 484.03 | V |
| 1.47 | 27.23 | 30.39 | 202.10 | 485.47 | V |
| 1.72 | 31.81 | 35.11 | 282.36 | 488.61 | V |
| 1.97 | 36.58 | 40.06 | 381.25 | 491.44 | V |
| 2.21 | 41.22 | 44.52 | 483.00 | 494.45 | V |
| 2.45 | 45.83 | 49.45 | 611.51 | 494.44 | V |
| 2.70 | 50.57 | 54.59 | 765.69 | 492.31 | V |
| 2.95 | 55.15 | 59.99 | 937.90 | 496.41 | V |
| 3.19 | 59.67 | 64.97 | 1105.54 | 499.49 | V |
| 3.43 | 64.36 | 70.14 | 1291.49 | 500.91 | V |
| 3.68 | 69.11 | 75.35 | 1494.82 | 502.35 | V |
| 3.92 | 73.66 | 80.19 | 1699.99 | 503.89 | V |
| 4.17 | 78.43 | 85.30 | 1934.89 | 505.82 | V |
| 4.41 | 83.13 | 90.23 | 2184.04 | 506.97 | V |
| 4.66 | 87.74 | 95.01 | 2439.39 | 508.52 | V |
| 4.91 | 92.48 | 100.01 | 2726.84 | 509.75 | V |
| 5.08 | 95.68 | | | | V/P |
| 5.08 | 95.68 | 106.06 | 3112.09 | 503.26 | P |
| 5.15 | 96.54 | 84.85 | 2592.91 | 247.17 | P |
| 5.40 | 98.17 | 84.85 | 3007.69 | 156.82 | P |
| 5.71 | 98.99 | 84.85 | 3399.84 | 82.69 | P |
| 5.90 | 99.38 | 84.85 | 3477.54 | 64.25 | P |
| 6.14 | 99.73 | 84.85 | 3537.26 | 49.34 | P |
| 6.37 | 99.97 | 84.85 | 3585.52 | 38.73 | P |
| 6.38 | 99.98 | 84.85 | 3592.73 | 37.66 | P |
| 6.39 |100.00 | 84.85 | 3599.93 | 37.66 |Filled |
充模分析的屏幕输出文件
屏幕输出文件和结果概要都有与图170相似的部分。它同时包含了分析过程中（第一部分）和分析结束时的关键信息。使用这些信息可以快速查看这些变量，从而判断是否需要详细分析某一结果，以发现问题。
Filling phase results summary for the part :
Bulk temperature - maximum (at 4.906 s) = 252.5450 C
Bulk temperature - 95th percentile (at 5.082 s) = 251.2430 C
Bulk temperature - 5th percentile (at 6.389 s) = 214.1860 C
Bulk temperature - minimum (at 6.379 s) = 105.0260 C
Wall shear stress - maximum (at 6.389 s) = 0.6826 MPa
Wall shear stress - 95th percentile (at 0.249 s) = 0.3107 MPa
Shear rate - maximum (at 4.906 s) = 4725.2798 1/s
Shear rate - 95th percentile (at 0.249 s) = 2489.9800 1/s
End of filling phase results summary for the part :
Total part weight = 2512.5301 g
Bulk temperature - maximum = 247.0680 C
Bulk temperature - 95th percentile = 244.5620 C
Bulk temperature - 5th percentile = 214.1860 C
Bulk temperature - minimum = 105.0370 C
Bulk temperature - average = 233.7720 C
Bulk temperature - RMS deviation = 12.9527 C
Wall shear stress - maximum = 0.6826 MPa
Wall shear stress - 95th percentile = 0.1478 MPa
Wall shear stress - average = 0.0926 MPa
Wall shear stress - RMS deviation = 0.0443 MPa
Frozen layer fraction - maximum = 0.5465
Frozen layer fraction - 95th percentile = 0.1257
Frozen layer fraction - 5th percentile = 0.0649
Frozen layer fraction - minimum = 0.0000
Frozen layer fraction - average = 0.0898
Frozen layer fraction - RMS deviation = 0.0263
Shear rate - maximum = 2176.5300 1/s
Shear rate - 95th percentile = 58.9857 1/s
Shear rate - average = 22.8884 1/s
Shear rate - RMS deviation = 27.0947 1/s
结果概要输出
充模时间（Fill Time）
充模时间显示的是熔体流动前沿的扩展情况，其默认绘制方式是阴影图，但使用云纹图可更容易解释结果。云纹线的间距应该相同，这表明熔体流动前沿的速度相等。制件的填充应该平衡。当制件平衡充模时，制件的各个远端在同一时刻充满。对大多数分析，充模时间是一个非常重要的关键结果。
压力（Pressures）
有几种不同的压力图，每种以不同的方式显示制件的压力分布。所有压力图显示的都是制件某个位置（一个节点）、或某一时刻的压力。
使用的最大压力应低于注射机的压力极限，很多注射机的压力极限为140 MPa (~20,000 psi)。模具的设计压力极限最好为100 MPa (~14,500 psi)左右。如果所用注塑机的压力极限高于140MPa，则设计极限可相应增大。模具的设计压力极限应大约为注射机极限的70%。假如分析没有包括浇注系统，设计压力极限应为注射机极限的50%。
象充模时间一样，压力分布也应该平衡。压力图和充模时间图看起来应该十分相似，如果相似，则充模时制件内就只有很少或没有潜流。
具体的压力结果定义如下：
· 压力（Pressure）
压力是一个中间结果，每一个节点在分析时间内的每一时刻的压力值都记录了下来。默认的动画是时间动画，因此，你可以通过动画观察压力随时间变化的情况。压力分布应该平衡，或者在保压阶段应保证均匀的压力分布和几乎无过保压。
· 压力（充模结束时）（Pressure (end of filling)）
充模结束时的压力属于单组数据，该压力图是观察制件的压力分布是否平衡的有效工具。因为充模结束时的压力对平衡非常敏感，因此，如果此时的压力图分布平衡，则制件就很好地实现了平衡充模。
· 体积/压力控制转换时的压力（Pressure at V/P switchover ）
体积/压力控制转换时的压力属于单组数据，该压力图同样是观察制件的压力分布是否平衡的有效工具。通常，体积/压力控制转换时的压力在整个注塑成型周期中是最高的，此时压力的大小和分布可通过该压力图进行观察。同时，你也可以看到在控制转换时制件填充了多少，未填充部分以灰色表示。
· 注射位置压力：XY图（Pressure at injection location: XY Plot ）
注射节点是观察2维XY图的常用节点。通过注射位置压力的XY图可以容易地看到压力的变化情况。当聚合物熔体被注入型腔后，压力持续增高。假如压力出现尖峰（通常出现在充模快结束时），表明制件没有很好达到平衡充模，或者是由于流动前沿物料体积的明显减少使流动前沿的速度提高。