此共聚物不需中和，就能获得良好的水分散性。
设计出了AMPS 改性环氧树脂的反应路线，通过正交实验和对比实验，对反应物配比、聚合温度和引发剂用量等反应条件进行了优化，并探讨了影响反应稳定性的因素。
由于AMPS的高聚合活性，须采用一些较为特殊的单体滴加方法，以保证共聚反应的稳定进行。
关键词：环氧树脂；丙烯酰胺基—2—甲基丙磺酸(AMPS)；接枝反应；水溶性Synthesis and Performance Study of Water-soluble Epoxy ResinSun Kan, College of Chemistry and Materials ScienceAbstract: The epoxy resin emulsion derived from chemical method received much attention due to absence of surfactant. It is characteristic of self-emulsification,dispersoid particle was small at nano level. The modifier reported in the literature to prepare anionic epoxy resin was mostly acrylic monomers. Epoxy resin can obtain water-disposability after carboxyl group was introduced and neutralized. The emulsion prepared by this approach only could keep stable under the alkalescent circumstance. If pH value vary, the system tend to agglomerate or gelate which is bad to preservation and untilization.Key words: epoxy resin, 2-acrylamido-2-methyl-l-propanesulfonic acid, graft polymerization, water solubility1.引言环氧树脂(Epoxy resin)是泛指含有两个或者两个以上环氧基，以脂肪族、脂环族或芳香族等有机化合物为骨架并通过环氧基团反应形成的热固性产物的高分子低聚体，是一种从液态到粘稠态、固态多种形态的物质。
水性环氧树脂的制备与性能研究李进，张良均，童身毅，唐进伟(武汉工程大学化工与制药学院湖北省新型反应器与绿色化学工艺重点实验室，武汉430074) 慧聪涂料网讯：摘要：采用中等相对分子质量环氧树脂与聚醚反应，合成了非离子环氧树脂乳化剂，再结合相反转技术，制备水性环氧树脂乳液。
讨论了乳化剂的用量对乳液粒径和稳定性的影响；研究了乳化剂、环氧固化剂用量与涂膜吸水率、凝胶含量、机械性能之间的关系。
关键词：环氧树脂；水性环氧树脂；相反转技术0.引言环氧树脂固化物具有优异的物理化学性能，尤其以优良的耐水性、耐化学品性、极佳的粘附性能而广泛应用于涂料领域[1]。
现在，人们在追求涂料高性能的同时，对于节约资源、保护生态环境越来越重视，研究开发水性环氧涂料已经成为涂料工业发展的一大趋势，具有广阔的前景。
转相乳化法是制备高分子聚合物水基化微粒体系的有效方法[2]，但制备乳胶粒径小且分布均匀、稳定性好的乳液体系受许多因素影响，其中乳化剂的影响最为重要。
近年来，对于非离子型乳化剂及其合成乳液的报道已经很多[3-7]，本文利用环氧基团的高反应活性，在Lewis酸的催化作用下，与亲水性的聚乙二醇进行亲核加成反应，合成了具有两亲性同时又带有与油相成分完全相同组分的高分子乳化剂，同时对在乳化剂用量不同的条件下乳液的粒径和稳定性进行了考察，并且研究了乳化剂的用量、AB-HGF固化剂用量与涂膜吸水率、凝胶含量、机械性能之间的关系。
1.实验部分1.1原材料双酚A型环氧树脂：江苏三木集团；聚醚：分析纯，上海化学试剂公司；乙二醇丁醚：化学纯，天津东天正精细化学试剂厂；三氟化硼乙醚络合物：化学纯，国药集团化学试剂有限公司；AB-HGF水性环氧固化剂：浙江安邦新材料发展有限公司。
1.2环氧树脂乳化剂的合成在干燥氮气保护下，将脱水的聚醚和环氧树脂按环氧基与羟基物质的量的比为1∶1.0～1.2的比例加到装有温度计、搅拌装置和回流冷凝器的四口烧瓶中，搅拌下，升温至80～90℃使原料熔化，搅拌混匀，滴加催化剂三氟化硼乙醚络合物，在90～110℃下反应5～6h，出料，室温冷却即得乳化剂EP-S。
水性环氧树脂专用乳化剂的制备及性能研究倪维良,柳云骐,陈克磊 (中国石油大学(华东)化学化工学院,山东青岛266555)摘 要:采用环氧树脂E-51与二乙醇胺反应合成与环氧树脂分子结构匹配的高分子离子型乳化剂,并利用不同的成盐方式测定其乳化性能。
采用相反转法制备出水性环氧乳液。
采用溴代乙烷成盐,醋酸调整p H 5 6合成得到季铵盐型离子表面活性剂。
采用高速分散相反转技术制备的环氧乳液,粒径大小在200nm左右。
关键词:水性环氧乳化剂;乳液稳定性;表面活性剂;粒径分布中图分类号:TQ630 4+9 文献标识码:A 文章编号:0253-4312(2010)12-0061-04Study on Synthesis and Properties ofSpecific Em ulsifier forW aterborne Epoxy R esi nN iW e iliang,Liu Yunq,i Chen Ke lei(Co llege of Che m istry and Che m ica l Engineer i ng,China University of Petroleum,Q ingdao Shandong,266555,Chi na) Abstrac t:A high m o lecular w ei g ht i o nic e m u lsifiers w ere synthesized by epoxy resi n and d iet h ano-la m ine.E m u lsificati o n ab ility w as dete m ined by usi n g different salify i n g m ethods.B ro m oethane w as used to prepare quater nary a mm on i u m sa l.t A cetic acid w as used to adjust p H to5 6to obta i n a quaternar y a mm on-i um salts of ion ic surfactan.t The w aterborne epoxy resi n e m u lsion w as prepared by the phase-inversi o n techn ique w ith high-speed d ispersi o n.The e m ulsion partic le size is about200n m.K ey W ords:w ater borne epoxy e m u lsion;e m u lsion stab ility;surfactan;t particle size d istribution0 引 言环氧树脂不溶于水(H LB 3),现有的环氧树脂涂料大多采用有机溶剂体系,有悖于社会对环境友好的要求和无污染或低污染涂料的发展方向,水性涂料作为一种新型的功能材料得到了迅速发展。
水性环氧树脂乳化型固化剂固化特性研究秦卫，舒武炳，明杜（西北工业大学理学院应用化学系，陕西西安710129）摘要：在多元胺中引入环氧树脂（EP ），再通过成盐反应，合成出含仲胺盐结构、可乳化液体EP 的固化剂；然后采用相反转法制备出稳定的水性EP 乳液。
结果表明：该固化剂在室温时具有一定的潜伏性（水性EP 乳液室温储存期超过14d ），而在较高温度时具有快速固化的特点。
仲胺盐的起始分解温度（T i ）约为113℃，当固化温度较低时，仲胺盐热分解反应难以进行，封闭的仲胺基与环氧基的固化反应难以发生，表现为成盐率越高，乳液凝胶时间越长；当固化温度>T i 时，仲胺盐快速热分解后释放出被封闭的活性仲胺基，乳液可快速固化，成盐率对乳液凝胶时间的影响不大。
各固化膜均具有较低的吸水率（<3.1%），其耐水性和耐丙酮性能优良，但耐强酸、强碱性能较差且随固化剂成盐率提高而下降。
关键词：环氧树脂；固化剂；固化性能；凝胶时间中图分类号：TQ314.256文献标识码：A文章编号：1004－2849（2011）02－0009-04收稿日期：2010-10-21；修回日期：2010-12-29。
作者简介：秦卫（1984-），女，河北石家庄人，硕士，主要从事高聚物的合成与改性等方面的研究。
E-mail ：siji.student@ 通讯作者：舒武炳。
E-mail ：wbshu@0前言环氧树脂（EP ）因含有多种极性基团和高活性环氧基团而具有较高的内聚力，故其对被粘接材料（尤其是高表面活性材料）具有较高的胶接强度；另外，EP 固化过程中基本上无低分子挥发物产生，故其尺寸稳定性较高。
因此，EP 作为一种热固性树脂，以其强度高、硬度好、电绝缘性能佳和固化收缩率低（材料内应力小）等优势，在诸多领域中得到广泛应用[1]。
传统溶剂型EP 在使用过程中会挥发出大量有机溶剂，从而不利于环保，因此水性EP 体系研究已成为重要课题之一[2]。
摘要高速铁路中使用的混凝土轨道板在野外环境下不可避免的受到自然因素的侵蚀，混凝土轨道板在使用周期范围内的保养和维持以及后期在混凝土轨道板使用周期结束后的翻新消耗都会非常巨大。
为能够有效阻止自然因素对混凝土轨道板的侵蚀，降低后期维修和重建混凝土轨道板的成本，本论文拟研究一种初期就涂覆在混凝土轨道板表面的涂料。
涂料行业所使用的原料种类繁多，自身具有非常优异性能的环氧树脂脱颖而出，并在涂料行业中被广泛使用。
由于市面上常见的传统环氧树脂涂料对人体有损害，并且对大气有危害的溶剂型环氧涂料。
所以本论文拟研究一种新型的绿色环保环氧树脂乳液，这种新型绿色环保乳液摒弃了以有机溶剂溶解环氧树脂的方法，选择以常用的水作为替代品来分散环氧树脂。
水性环氧涂料在固化剂存在的条件下，通过其对水性环氧树脂乳液的固化，形成的一种具有一定机械性能和力学性能的涂膜。
由于水性环氧树脂乳液是制备涂膜过程中不可缺失的一环，所以涂膜的力学性能和机械性能甚至化学性能都要受到水性环氧树脂乳液性能的影响。
因此制备一种符合市场要求和使用性能的水性环氧树脂乳液迫在眉睫。
新型绿色环保水性环氧树脂乳液的制备方法繁多，本论文研究了其中的两种，即化学方法和物理方法相结合的方法，下文是对研究内容的具体阐释：首先，由于环氧树脂分子结构两端各有一个环氧基，聚乙二醇两端各有一个醇羟基，并且聚乙二醇分子中具有很多醚键，亲水性加强。
在适当温度和适当引发剂存在的条件下，利用引发剂的引发作用使得环氧树脂上的某一端环氧基开环，随后聚乙二醇的一个醇羟基会被引入到开环的环氧基上。
由于聚乙二醇的另外一个醇羟基和分子链中相当多的醚键存在，被引入聚乙二醇分子的亲油性环氧树脂也因此具有了一定程度的亲水性，成功运用自乳化法制备出聚乙二醇改性环氧树脂自配乳化剂。
开环反应中通过对环氧值变化的检测，得到反应过程中不同反应因素对开环过程的影响。
通过测试试验产物的红外光谱图，得到了试验改性前后试验产物的结构变化。