透水混凝土研究及其应用

透水混凝土的试验研究及工程应用摘要：透水混凝土又称为无砂混凝土。

它由胶凝材料、粗骨料、水和外加剂按照一定的比例拌合而成。

由于透水混凝土硬化后水泥石中存在着较大的孔洞，具有良好的渗透性能，可缓解城市的“热岛效应”，吸声降噪，有效改善城市的热环境，北京奥林匹克公园中心区域绿化工程项目即采用了透水混凝土。

本文从水泥性能、粗骨料、水灰比、细骨料掺量等几个方面进行对比试验，研究了以上几个因素对透水混凝土性能的影响。

关键词：透水混凝土；骨料；水灰比；空隙率Abstract: Pervious concrete, also known as non-sand concrete, is mixed by cementitious material, coarse aggregate, water and admixtures in accordance with a certain proportion. Due to large holes in hardened cement paste of the permeable concrete, it has a good permeability, which c an alleviate the urban “heat island” effect, reduce noise, and effectively improve the urban thermal environment. Therefore, it has been applied in the greening project of the central area of Beijing Olympic Park. In the paper, the comparative tests from the cement performance, coarse aggregate content, water-cement ratio content, fine aggregate content are be presented, as well as the research on the impacts of the performance of pervious concrete from the above content factors.Key words: pervious concrete; aggregate; water-cement ratio; porosity1 引言城市道路、人行道、广场等城市设施无论是在设计还是在施工上，历来都强调要求混凝土密实、不透水。

高强度透水混凝土的研究与应用1前言随着人们对环保认识的提高、城市建设的快速发展和施工技术的进步，对透水混凝土的使用范围、技术指标和经济指标都提出了新的要求，促使透水混凝土向着高强和耐久等方向发展。

现在使用的透水混凝土砖，透水性基本满足使用要求，但是强度一般都比较低，大致在5—15MPa之间。

随着高层建筑的增加，公共安全问题显得越来越突出，在发生火灾或其他意外时，现有的透水混凝土砖地面无法达到载重消防车辆的通行和停放要求。

而沥青硬地面虽然能够满足载重消防车辆的通行和停放要求，但是无法实现透水功能。

透水混凝土砖一方面具有良好的透水性能，雨天不积水，表面不打滑，确保了游客的安全，改善了树木生长的环境；但较低的强度限制了它的推广应用。

在技术层面上，国内外透水混凝土的配制技术一直采用无砂大孔混凝土的设计思路，在混凝土配制过程中增大透水系数时混凝土强度不能满足设计要求，提高胶凝材料的用量时混凝土强度提高但透水系数又不能满足设计要求，这一矛盾一直困扰着混凝土生产企业和混凝土技术人员。

本研究以克服无砂大孔透水混凝土缺陷作为研究的技术基础，在保证混凝土透水顺畅的条件下，主要解决如何提高透水混凝土的强度问题。

2混凝土透水系数的确定2.1确定透水系数的气象依据为了科学地将特大暴雨记录降水量、降水速度与混凝土的孔隙率、透水速度之间建立量化关系，实现透水混凝土透水功能与气象条件的协调统一，我们首先要确定透水混凝土合理的透水系数指标范围。

我国气象上规定，降雨分为小雨、中雨、大雨、暴雨。

24小时降水量200毫米以上称“特大暴雨”。

为预防暴雨引起的破坏，设定了暴雨预警信号，暴雨预警信号分四级，分别以蓝色、黄色、橙色、红色表示。

在世界上最大的暴雨出现在南印度洋上的留尼汪岛，24由上表可知，透水混凝土开口孔隙率在15%--36%之间时，满足特大暴雨顺利通过的混凝土内最大水流动速度介于1.3mm/s—6.9mm/s之间。

我们定义单位面积上水流过混凝土的速度为透水系数，单位取mm/s。

透水混凝土及其应用技术摘要：透水混凝土是一种具有良好透水性能的建筑材料，可以有效地降低地表径流和洪涝风险，同时减少城市排水系统的压力。

本文从透水混凝土的特点和优势、应用技术、应用领域以及发展趋势等方面进行了详细的探讨和分析。

通过对透水混凝土的研究和应用，可以为城市建设提供更好的环保和可持续发展解决方案。

关键词：透水混凝土；应用技术；研究策略引言近年来，随着城市化进程的加快，城市面临的水资源和排水系统压力越来越大，因此需要寻找一种新的解决方案来管理和利用雨水。

透水混凝土作为一种新兴的建筑材料，在解决城市排水问题上具有巨大的潜力。

本文旨在介绍透水混凝土的特点和优势、应用技术、应用领域以及未来的发展趋势，以期为相关领域的研究和应用提供指导。

一、透水混凝土的特点及优势：透水混凝土是一种具有良好透水性能的建筑材料，它通过优化粒径配合设计和添加透水剂等方式，具备出色的渗水能力和较高的透水率。

相比传统的混凝土，透水混凝土具有独特的排水性能，能够有效地促进雨水渗入地下，减少地表径流量，从根本上降低城市洪涝风险。

与此同时，透水混凝土还能稳定地进行排水，改善城市排水系统的运行效果。

使用透水混凝土还具有环境保护的优势。

透水混凝土可以减少雨水径流对环境的冲击，有效保护水源和水体质量。

在雨水渗透的过程中，透水混凝土能够过滤雨水中的污染物，减少污染物的扩散和积聚，提高水质。

这使得透水混凝土在城市建设中得到广泛应用，并受到环境保护机构和相关部门的青睐。

此外，透水混凝土在强度和耐久性上也具有吸引力的特点。

通过控制水泥浆体的含水量以及采用特殊的粒料形状，透水混凝土可以在保持强度的前提下，保持良好的透水性能。

这种特点使得透水混凝土能够满足建筑物在使用寿命内的强度和耐久性要求。

综上所述，透水混凝土具有渗水能力强、透水率高、排水效果好的特点，可以有效地降低洪涝风险并改善城市排水系统的运行效果。

同时，透水混凝土在保护环境、增加水源可利用性方面也具备显著优势。

浅谈透水混凝土的性能与应用摘要：透水混凝土可在降雨过程中，将雨水原地渗透至土壤中，因而被越来越广泛地应用于建造停车场和低荷载公路路面，甚至高速公路路面。

本文主要从透水混凝土的制备方法、排水方式和维护手段等进行研究，探讨如何取得较高强度和较好透水效果等性能指标，旨在促进透水混凝土的性能优化和推广应用。

关键词：透水性；混凝土；荷载；水灰比1.引言传统的混凝土道路没有透水性和透气性。

为保证路面的耐久性，提高路面的密实度，提高混凝土的抗渗性。

虽然传统的混凝土道路自使用以来为人们的生活、工作和旅行提供了很大的交通便利，与此同时，传统混凝土的不透水性给城市交通到来了很大的负面影响。

透水混凝土的主要用途是能够节约水资源、保护环境和防止城市在强降雨过程中发生洪涝灾害。

它的作用是通过其本身和基底，将水渗入其表面或靠近土壤的地方，以维持当地的地下水位，净化水质，减少城市排水系统。

低洼地区的排水负荷和雨水积聚。

目前，由于技术的限制，透水混凝土材料主要用于停车场、人行道和低交通荷载路面（如公园、住宅区或停车库至主干道）的修建，用于收集降雨落在路面上的雨水，并收集附近普通混凝土路面、停车场和草地上，以及从公寓和屋顶排出的雨水。

2.透水混凝土特点2.1优点透水混凝土作为一种新型的工程材料，具有适应道路施工的特点。

其主要优点是：一是透水性好。

改进这种材料的初衷是使材料及时完成渗水。

在日常生活中，地表水和地下水是相通的，这里的水循环链没有中断，水循环系统是统一和连通的。

在极端降水天气，它也可以作为水库拦截部分洪水。

此外，这种材料的表面比传统的混凝土材料粗糙，因此摩擦力更大。

在洪水的极端天气，它可以降低水流速度，也可以减少洪水造成的危害。

这个过程也相当于循环水。

沿途的植物也可以在地面吸水的过程中得到滋养。

透水混凝土材料渗水后，地下水也发生回流补给，可以减少地下水大规模开采的影响。

第二点是这种材料可以吸收声音并降低噪音。

这一功能也是由于粗集料的加入，混凝土材料有较多的空隙，所以当地面上有噪音通过混凝土材料时，混凝土材料不反射噪音，而是通过空隙吸收噪音。

透水混凝土施工技术与应用研究摘要：透水混凝土为多孔形式的轻质混凝土，采用透水混凝土铺装具有过滤净化、存蓄滞留雨水的作用，可以改善城市的热、湿环境。

同时，透水混凝土可以减小对铺装层下土壤环境的破坏，对改善城市的自然环境和维护生态平衡等具有重要的现实意义，是建设生态城市及海绵城市的重要基础设施。

本文通过对透水混凝土施工技术的总结，阐述了透水混凝土施工的技术要点及保障混凝土强度、透水性方面的一些控制措施，并对透水混凝土的应用前景进行了展望，希望能为工程建设提供参考。

关键词：透水混凝土；路面铺装；施工技术0 引言：透水混凝土路面铺装工程包括4m灰色透水混凝土园路和彩色透水混凝土路。

由于本工程主要为园林绿化工程，所以对降雨量多时的排水性能及园林整体的水土保持功能有较高要求。

透水混凝土的渗透系数与混凝土原材料、施工工艺都有关系，所以如何改善施工工艺，提高混凝土的透水性能，同时兼顾混凝土的强度性能，就需对透水混凝土原材料、配合比、浇筑方式、温度、外加剂等各种影响因素进行精细控制。

1 透水混凝土施工工艺1.1材料准备水泥：水泥采用P.O 42.5级的硅酸盐水泥，质量符合现行国家标准《通用硅酸盐水泥》GB175的要求。

稳定剂：由于透水混凝土水分蒸发非常快，加入稳定剂，有利于保水实现快速摊铺，及早进行养护，稳定剂应符合现行国家标准《混凝土外加剂》GB8076的规定。

增强剂：透水混凝土增强剂又称“胶结料”，是透水混凝土中必不可少的外加剂，其主要作用是通过聚合物在水泥中的交联而大幅度提高骨料间的“点粘接”强度，同时起到润滑、缓凝和改善透水混凝土施工性、和易性的作用。

掺加增强剂的透水混凝土在施工中不流淌、不封底。

增强剂还能有效地提高混合料的包裹力和塑化性能，更有利于大面积快速摊铺作业，提高施工效率，节约成本。

集料：使用质地坚硬、耐久、洁净、密实的碎石料，碎石的性能指标符合现行国家标准《建筑用卵石、碎石》GB/T14685中的二级要求。

透水混泥土技术与其应用研究高顺平(理工大学2011级研究生学号：2011710008 专业：建筑与土木工程)摘要：透水混凝土是一种生态环保混凝土，是经过特殊工艺制成的具有连续孔隙的混凝土，具有一定的强度，又有一定的透气透水性。

本文介绍了透水混凝土的定义、特性、材料要求、优越性与施工养护，阐述了透水混凝土的配合比设计与试验方法等容，表明了透水混凝土技术将是解决道路使用要求与排水问题的最佳方案，是今后发展的重要方向。

关键词：透水混凝土，配合比设计，骨料，透水系数，强度Pervious concrete technology researchGaoshunping(Kunming university of science and technology level of 2011 graduate studentsID:2011710008 Professional: Architecture and Civil Engineering)Abstract: Concrete is an eco-friendly concrete, made through a special process with continuous pores of the concrete, have a certain strength, but also some of the breathable permeable. This paper introduces the pervious concrete’s e definition, characteristics of, material requirements, advantages and construction maintenance,Elaborated the pervious concrete mix design and test methods of content, shows the pervious concrete technology will be used to solve the road and drainage problem of optimal scheme, is an important direction for future development.Keywords:Pervious Concrete, Mixture ratio design, Aggregate, Water permeability coefficient of, Strength为了体现环保节能和可持续发展，在多处“面子工程”的设计中均考虑使用绿色环保透水混凝土。

应用技术与设计2018年第18期87城市内涝一直是困扰城市建设和发展的难题，多地“城市看海”的消息时常见诸报端，给民众的生命和财产安全造成损失。

造成城市内涝既有自然的原因，也有城市排洪设施设计不合理，城市生态建设滞后的因素。

解决城市内涝，需要统筹城市规划，从设计、施工和材料各方面通盘考虑。

透水混凝土孔隙率大，装饰性强，雨水通过透水混凝土的孔隙结构进行地表渗透，有效调节了雨水径流速度，是海绵城市建设重要的基础材料。

经过国内外学者的不断研究，在透水混凝土的配合比设计、性能和应用诸多方面取得了丰硕的成果，本文将对以上研究成果进行梳理，以期为透水混凝土的研究与应用提供参考。

1　原材料组成透水混凝土通常由级配合理的粗骨料、拌合水水、胶凝材料、化学外加剂组成，由于设计的原因，细骨料在整个透水混凝土的掺量较少，或者不掺以获得较大的开孔孔隙率。

1.1　胶凝材料水泥作为透水混凝土中形成强度和互相粘接的最主要的组分，比普通混凝土水泥用量少，一般选用早强的硅酸盐水泥或者普通硅酸盐水泥。

水泥的用量太多会影响骨料之间的孔隙率，太少又造成透水混凝土强度不足，通常以骨料表面形成均匀的水泥浆体膜为宜。

矿物掺合料如硅灰、粉煤灰的使用可以提高透水混凝土的后期强度和耐久性。

1.2　骨料透水混凝土中粗骨料的骨料不应含有有机质、风化物或其他有害杂质，其含泥量应低于 1%，同时针片状含量不高于 15% 。

孙家瑛等研究表明，以石灰石作骨料的透水混凝土，其 28d 强度约为13MPa 粒径较小的骨料能够增大机械咬合力与粘结强度，进而提高抗压强度。

大量的研究者研究了细骨料对透水混凝土性能的影响，研究表明，当细骨料掺入量为粗骨料质量的5%-7% 时，透水混凝土强度提升显著，同时可有效改善其抗冻融循环能力。

1.3　外加剂外加剂是透水混凝土提高强度和粘接性能的重要组成部分，添加适量的减水剂能改善其和易性，减少强度损失。

适量的聚合物乳液和增稠剂能够提高透水混凝土的粘接强度，着色剂可以对透水混凝土外观增色。

透水混凝土技术及其应用研究透水混凝土技术及其应用研究摘要：透水混凝土是一种生态环保混凝土，是经过特殊工艺制成的有连续空隙的混凝土，具有一定的强度，又有一定的透气透水性。

本文着重介绍透水混凝土的定义、特性、材料要求、优越性及施工养护，阐述了透水砼配合比设计及试验方法等内容，表明了透水混凝土技术将是解决道路使用要求及排水问题的最佳方案，是今后发展的重要方向。

关键词：透水混凝土，配合比设计，骨料，透水系数，强度。

透水混凝土模型现今国内对透水混凝土配合比设计方法和成型工艺以及透水系数的测定等还不足，对透水混凝土的生态环保效益的研究也十分欠缺。

这些问题的解决对透水混凝土材料的应用和推广是十分有利的。

一、定义和特点透水混凝土通常定义为一种含有较多粗集料、微量或无细集料且无足量水泥的混凝土材料。

通过配合比设计满足具有适当强度,高透水性, 无析离等工程需求,主要可以作为无需压密的回填材料或水工材料,抗压强度约在1.5MPa～14MPa之间。

与一般混凝止:相比,具有如下特点:1、透水混凝土比重一般约在1400kg/m3～1 900/m3之间；2、热传导系数小；3、水的毛细现象不显著；4、水泥用量少；5、成型时侧压力小, 可使用各种轻型模板；6、表面存在蜂窝状孔洞,表面抹平施工方便；7、可以防止雨天路面集水和夜间反光,增加行走舒适性和安全性,同时减少降雨季节道路排水系统负担；8、可以吸收车辆行走产生的噪音，有利于创造安静舒适的交通环境；9、可以补充城市地下水资源, 保护上壤温度,改善城市地表植物和土壤生物的生存条件，有利于生态平衡；10、可以增加城市可透水透气面积，调节城市气候，降低地表温度，缓解城市“热岛”表现象；此外，透水混凝土靠自重即可成型，施工简易方便，对于工人的施工技术要求不高更是其主要特色。

二、优越性1、良好的渗水透水性1）收集雨水；2）有效补充地下水；3）保持土壤湿度；4）改善地表植物和土壤微生物的生存条件。

透水混凝土标准施工技术的研究与应用一、引言透水混凝土是一种新型的、环保的、可持续的建筑材料，具有出色的透水性能和良好的抗压强度。

随着城市化进程的加快和城市排水难题的日益突出，透水混凝土的应用越来越广泛。

本文将对透水混凝土的标准施工技术进行研究和应用，以期为透水混凝土的施工提供参考。

二、透水混凝土的特点透水混凝土是一种可以透水的特种混凝土，其特点如下：1. 透水性能好：透水混凝土具有良好的透水性能，雨水可以自然渗透到地下水层，减轻城市排水压力。

2. 抗压强度高：透水混凝土的抗压强度高，可以满足城市道路、广场等场所的荷载要求。

3. 环保节能：透水混凝土的制作过程中不需要烧结，不产生二氧化碳等有害物质，符合环保要求。

4. 耐久性好：透水混凝土的耐久性好，使用寿命长。

三、透水混凝土的标准施工技术透水混凝土的标准施工技术是保证透水混凝土性能的重要保障，其施工步骤如下：1. 基础处理：首先要对基础进行处理，确保基础平整、无杂物、无油污等。

2. 砂浆层铺设：在基础上铺设5-10厘米厚的砂浆层，用水泥砂浆将砂浆层与基础牢固粘合。

3. 填充料铺设：在砂浆层上铺设填充料，填充料的粒径应为5-20毫米，填充料的厚度应为10-15厘米。

4. 水泥混凝土铺设：在填充料上铺设水泥混凝土，水泥混凝土的配合比应按照设计要求进行。

5. 表层处理：在水泥混凝土表层上进行处理，可以采用机械磨光、喷涂或刷涂等方法，以保证表面平整、美观。

四、透水混凝土的应用透水混凝土具有良好的透水性能和抗压强度，广泛应用于城市道路、广场、公园、停车场、体育场馆、码头等场所。

1. 城市道路：透水混凝土可以减少城市排水压力，改善城市环境。

2. 广场：透水混凝土可以提高广场的美观性和透水性能，增加人们的活动空间。

3. 公园：透水混凝土可以增加公园的绿化面积，改善城市生态环境。

4. 停车场：透水混凝土可以减少停车场的积水现象，提高停车场的使用效率。

5. 体育场馆：透水混凝土可以提高体育场馆的透水性能，减少雨天比赛的影响。

1透水混凝土的定义与应用背景透水混凝土是由骨料、水泥、水、外加剂及掺和料进行搅拌制成的多孔混凝土，具有类似于蜂窝结构的多孔形貌，具有较强的透气性，重量轻便。

现阶段透水混凝土只应用在城市广场路面、道路建设和公路两侧的路肩。

透水混凝土有大孔隙，可以积攒大量的热能，减少热岛效应现象的出现，还可以吸附空气中的颗粒、绿化环境，也能减少噪音污染，具有较高的经济效益和环保效益。

2透水混凝土的特点透水混凝土具有三个主要特点：一是孔隙率为15%～30%时具有较强的透水性；二是透水混凝土的施工相对简单；三是透水混凝土基本实现了与环境共存的状态，是一种能够提高人们生活质量的环保型绿色材料。

3国内外研究和应用现状3.1透水混凝土在国外的研究和应用现状在透水混凝土的发展历程中，美国在上世纪60年代首次使用透水混凝土建了停车场，并获得透水性混凝土的专利。

随后，美国开始大规模使用透水混凝土用于停车区路段。

德国在上世纪80年代就提出对不透水路面工程的改革政策，指标是将全国90%以上的不透水工程进阶为透水工程，并且于2010年前完成该项任务。

弗莱堡这座城市经过十年的时间将城市内的不透水路面全部改用透水混凝土，经过长时间的透水作用，地下水位得以回升，植物能吸取到充足的水分和营养，使得该城市被植被所包围，形成了生态文明城市。

日本对环境保护和资源利用也很重视。

为此，日本政府在混凝土与生态环境关系讨论中提出构建生态混凝土研究机构，并进行多次关于透水混凝土应用的会议，号召全国推广使用透水混凝土。

据统计，日本在透水混凝土的应用主要在路面。

3.2透水混凝土在国内的研究和应用现状上海世博会中，各项场地的建设都普遍应用到了透水混凝土，据资料显示，在上海世博园的大片区域内，地面和公共设施的建设中60%以上都采用了透水材料。

4配制技术4.1配合比的设计透水混凝土是根据一定的黏性和强度要求，用水泥浆将骨料包围起来，将骨料之间相互结合起来，形成具有较高强度且多孔的整体结构。