50 t EBT EAF-LF(VD)-CC流程生产G55SiMoVA轴承钢的工艺实践

莱钢50t EBT EAF2LF(V D)2CC生产GCr15轴承钢的工艺实践李法兴1　兰新哲1　宋永辉1　胡蒙均1　孙永喜2(1西安建筑科技大学,西安710055;2莱芜钢铁股份有限公司,莱芜271105)摘　要　莱钢采用E AF全程泡沫渣埋弧操作,E BT出钢合金化,LF2次精炼渣碱度410～510,精炼渣的主要成分(%)为:45～50CaO,9～13S iO2,9～13Al2O3,7～8MgO,S iC扩散脱氧和40～60LΠmin流量氩气搅拌,VD处理时间≥15min,连铸全程保护浇铸生产G Cr15轴承钢。

G Cr15轴承钢中的平均氧含量为719×10-6,最高氧含量为10×10-6。

关键词　G Cr15轴承钢　E AF2LF(VD)2CC　氧含量Practice of GCr15B earing Steel Production by50tEBT EAF2LF(V D)2CC ProcessLi Faxing1,Lan X inzhe1,S ong Y onghui1,Hu Mengjun1,and Sun Y ongxi2(1X i’an Architecture and T echnology University,X i’an710055;2Laiwu Iron and S teel C o Ltd,Laiwu271105)Abstract　The G Cr15bearing steel is produced at Laiwu S teel by using foaming slag submerged arc operation in whole period of E AF steelmaking,E BT tapping alloying,LF secondary refining slag basicity being410～510,main composition of refining slag245～50CaO,9～13S iO2,9～13Al2O3,7～8MgO,diffusion2deoxidizing by S iC and Ar stirring with flow rate40～60LΠmin,VD treatment time≥15min,and casting with shielding practice in whole period.The average oxygen content in G Cr15bearing steel is719×10-6,and the maximum oxygen content is10×10-6.Material I ndex　G Cr15Bearing S teel,E AF2LF(VD)2CC Process,Oxygen C ontent 莱钢特殊钢厂近年来在降低轴承钢氧含量、降低轴承钢夹杂物级别、消除轴承钢碳化物液析等方面取得了显著进步,并获得了国家钢铁产品实物质量“金杯奖”。

50 t EBT+LF+VD冶炼特级优质轴承钢钛含量控制工艺研究王德勇 齐 锐 张 群（本钢板材股份有限公司技术研究院 本溪 117000）摘　要：研究分析了原材料中的钛含量及冶炼过程中钛的变化情况，通过选用低钛合金及造渣材料，采用EBT氧化法进行脱钛，精炼过程控制合理的碱度及Al2O3的活度，减少LF精炼过程中因渣中氧化钛还原导致的钢液增钛，实现了[Ti]≤15×10-6的特级轴承钢的控制水平。

关键词：特级优质轴承钢；钛含量；LF；VDTHE PROCESS STUDY ON TITANIUM CONTENT CONTROL OF SUPERFINE BEARING STEEL BY 50 tEBT+LF+VDWang Deyong QI Rui Zhang Qun（Technology Research Institute of Benxi Steel Plates Co.，Ltd， Benxi 117000， China)Abstract： Analyzes the titanium content in the raw materials and the change of titanium in the process of smelting， by choosing low titanium content alloy and slag making material， adopting EBT oxidation of titanium， refining process control reasonable basicity and Al2O3 activity， reduce the titanium oxide reduction as a result of titanium increase in liquid steel during LF refining process of ， implements [Ti] 15 x 10-6 or less and reach super high quality bearing steel level.Key words： super high quality bearing steel； titanium content；LF；VD第一作者：王德勇，男，44岁，高级工程师收稿日期：2021-3-22净度提高了，特别是钛含量的降低，大大提高了轴承的疲劳寿命。

轴承钢EAF-LF-VD-CC生产工艺的优化与实践孙丽娜;吴国玺;陈韧;宋满堂【摘要】本钢特殊钢公司轴承钢连铸坯生产初期,钢材质量低倍检验合格率低,消耗指标高,冶炼周期长.通过电弧炉配入40％铁水、采用炉门氧枪及炉壁氧气喷吹系统配合供氧的操作模式；优化LF精炼渣、中包保护渣、结晶器保护渣成分及操作工艺,使轴承钢质量低倍合格率明显提高,GCr15钢的化学成分全部达到本钢制定的标准要求,其中[0]=8 - 10×10-6、其它检验项目均满足GB/T18254 - 2002标准要求,GCr15钢实物质量已经达到国内先进水平.【期刊名称】《辽宁科技学院学报》【年(卷),期】2012(014)001【总页数】3页(P6-8)【关键词】电炉炼钢;连铸;轴承钢;低倍质量【作者】孙丽娜;吴国玺;陈韧;宋满堂【作者单位】辽宁科技学院,辽宁本溪117004;辽宁科技学院,辽宁本溪117004;辽宁科技学院,辽宁本溪117004;本钢板材股份有限公司技术中心,辽宁本溪117000【正文语种】中文【中图分类】TF741电炉生产轴承钢，传统的生产工艺是EAF－LF－VD—模注，国际上先进的生产工艺是:EAF－LF－RH－CC(连铸)。

连铸铸坯凝固速度快，钢水过热度小，加上电磁搅拌作用，可使成分更加均匀、夹杂物充分上浮，加上密封浇注，减轻了钢液的二次氧化，进一步降低钢中全氧含量，控制钢中夹杂物的形态，显著提高轴承钢的疲劳寿命〔1〕。

此外连铸可以提高综合成材率、节省能源，所以轴承钢连铸无论是在提高质量方面还是在降低成本方面都是最佳的工艺路线。

本钢特殊钢公司，现有一套235×265三流连铸机，因此轴承钢的生产工艺也采用了EAF－LF－VD－CC 路线。

但是，工业生产钢材质量检验统计结果表明，连铸工艺生产的轴承钢钢材中心疏松、偏析及缩孔等低倍缺陷更加严重，影响了轴承钢产品质量。

为了更好的发挥这一先进生产线水平，对轴承钢生产工艺进行了优化研究，取得了良好的冶金效果。