测区混凝土强度换算表平均回弹值Ｒm测区砼强度换算值(ＭＰa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.020.0 10.3 10.1 9.820.2 10.5 10.3 10.020.4 10.7 10.5 10.2 9.820.6 11.0 10.8 10.4 10.120.8 11.2 11.0 10.6 10.3 9.921.0 11.4 11.2 10.8 10.5 10.021.2 11.6 11.4 11.0 10.7 10.2 9.921.4 11.8 11.6 11.2 10.9 10.4 10.021.6 12.0 11.8 11.4 11.0 10.6 10.2 9.821.8 12.3 12.1 11.7 11.3 10.8 10.5 10.122.0 12.5 12.2 11.9 11.5 11.0 10.6 10.2 9.922.2 12.7 12.4 12.1 11.7 11.2 10.8 10.4 10.022.4 13.0 12.7 12.4 12.0 11.4 11.0 10.7 10.3 10.022.6 13.2 12.9 12.5 12.1 11.6 11.2 10.8 10.4 10.2 9.822.8 13.4 13.1 12.7 12.3 11.8 11.4 11.0 10.6 10.3 9.923.0 13.7 13.4 13.0 12.6 12.1 11.6 11.2 10.8 10.5 10.123.2 13.9 13.6 13.2 12.8 12.2 11.8 11.4 11.0 10.7 10.3 10.023.4 14.1 13.8 13.4 13.0 12.4 12.0 11.6 11.1 10.9 10.4 10.2 9.923.6 14.4 14.1 13.7 13.2 12.7 12.2 11.8 11.4 11.1 10.7 10.4 10.123.8 14.6 14.3 13.9 13.4 12.8 12.4 12.0 11.5 11.2 10.8 10.5 10.2 9.924.0 14.9 14.6 14.2 13.7 13.1 12.7 12.2 11.8 11.5 11.0 10.7 10.4 10.1(1)平均回弹值R m测区砼强度换算值(ＭＰa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 ≥6.024. 4 15．415.114.614.213.613.112.612.211.911．411．110．810．424. 6 15．615．314．814．413．713．312．812．312．011．511．210．910．624.8 15．915．615．114．614．013．513．012．612．211．811．411．110．725. 0 16．215．915．414．914．313．813．312．812．512．011．711．310．925. 2 16．416．115．615．114．413．913．413．012．612．111．811．511．025. 4 16．716．415．915．414．714．213．713．212．912．412．11．711．225. 6 16．916．616．115．714．914．413．913．413．012．512．211．811．325. 8 17．216．916．315．815．114．614．113．613．212．712．412．011．526. 0 17．517．216．616．115．414．914．413．813．513．012．612．211．626. 2 17．817．416．916．415．715．114．614．013．713．212．812．411．826.1817171615151414131313121226. 6 18．317．917．416．816．115．615．014．414．113．513．212．812．126. 8 18．618．217．717．116．415．815．314．614．313．813．412．912．327. 0 18．918．518．017．416．616．115．514．814．614．013．613．112．427. 2 19．118．718．117．616．816．215．715．014．714．113．813．312．627. 4 19．419．018．417．817．016．415．915．214．914．314．013．412．727. 6 19．719．318．718．017．216．616．115．415．114．514．113．612．927. 8 20．019．619．018．217．416．816．315．615．314．714．213．713．028. 0 20．319．719．218．417．617．016．515．815．414．814．413．913．228. 2 20．620．019．518．617．817．216．716．015．615．014．614．013．328. 4 20．920．319．718．818．017．416．916．215．815．214．814．213．5(2)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.028.6 21.2 20.6 20.0 19.1 18.2 17.6 17.1 16.4 16.0 15.4 15.0 14.3 13.628.8 21.5 20.9 20.2 19.4 18.5 17.8 17.3 16.6 16.2 15.6 15.2 14.5 13.829.0 21.8 21.1 20.5 19.6 18.7 18.1 17.5 16.8 16.4 15.8 15.4 14.6 13.929.8 23.0 22.3 21.6 20.7 19.8 19.1 18.4 17.7 17.2 16.6 16.2 15.3 14.530.0 23.3 22.6 21.9 21.0 20.0 19.3 18.6 17.9 17.4 16.8 16.4 15.4 14.7 30.2 23.6 22.9 22.2 21.2 20.3 19.6 18.9 18.2 17.6 17.0 16.6 15.6 14.9 30.4 23.9 23.2 22.5 21.5 20.6 19.8 19.1 18.4 17.8 17.2 16.8 15.8 15.1 30.6 24.3 23.6 22.8 21.9 20.9 20.2 19.4 18.7 18.0 17.5 17.0 16.0 15.230.8 24.6 23.9 23.1 22.1 21.2 20.4 19.7 18.9 18.2 17.7 17.2 16.2 15.431.0 24.9 24.2 23.4 22.4 21.4 20.7 19.9 19.2 18.4 17.9 17.4 16.4 15.5 31.2 25.2 24.4 23.7 22.7 21.7 20.9 20.2 19.4 18.6 18.1 17.6 16.6 15.7 31.4 25.6 24.8 24.1 23.0 22.0 21.2 20.5 19.7 18.9 18.4 17.8 16.9 15.8 31.6 25.9 25.1 24.3 23.3 22.3 21.5 20.7 19.9 19.2 18.6 18.0 17.1 16.031.8 26.2 25.4 24.6 23.6 22.5 21.7 21.0 20.2 19.4 18.9 18.2 17.3 16.232.0 26.5 25.7 24.9 23.9 22.8 22.0 21.2 20.4 19.6 19.1 18.4 17.5 16.4 32.2 26.9 26.1 25.3 24.2 23.1 22.3 21.5 20.7 19.9 19.4 18.6 17.7 16.6 32.4 27.2 26.4 25.6 24.5 23.4 22.6 21.8 20.9 20.1 19.6 18.8 17.9 16.8 32.6 27.6 26.8 25.9 24.8 23.7 22.9 22.1 21.3 20.4 19.9 19.0 18.0 17.0(3)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.032.8 27.9 27.1 26.2 25.1 24.0 23.2 22.3 21.5 20.6 20.1 19.2 18.3 17.233.0 28.2 27.4 26.5 25.4 24.3 23.4 22.6 21.7 20.9 20.3 19.4 18.5 17.4 33.2 28.6 27.7 26.8 25.7 24.6 23.7 22.9 22.0 21.2 20.5 19.6 18.7 17.6 33.4 28.9 28.0 27.1 26.0 24.9 24.0 23.1 22.3 21.4 20.7 19.8 18.9 17.8 33.6 29.3 28.4 27.4 26.4 25.2 24.2 23.3 22.6 21.7 20.9 20.0 19.1 18.034.6 31.1 30.2 28.9 27.4 26.2 25.2 24.3 23.6 22.7 21.9 21.0 20.0 18.834.8 31.4 30.5 29.2 27.6 26.4 25.4 24.5 23.8 22.9 22.1 21.2 20.2 19.035.0 31.8 30.8 29.6 28.0 26.7 25.8 24.8 24.0 23.2 22.3 21.4 20.4 19.2 35.2 32.1 31.1 29.9 28.2 27.0 26.0 25.0 24.2 23.4 22.5 21.6 20.6 19.4 35.4 32.5 31.5 30.2 28.6 27.3 26.3 25.4 24.4 23.7 22.8 21.8 20.8 19.6 35.6 32.9 31.9 30.6 29.0 27.6 26.6 25.7 24.7 24.0 23.0 22.0 21.0 19.835.8 33.3 32.3 31.0 29.3 28.0 27.0 26.0 25.0 24.3 23.3 22.2 21.2 20.036.0 33.6 32.6 31.2 29.6 28.2 27.2 26.2 25.2 24.5 23.5 22.4 21.4 20.2 36.2 34.0 33.0 31.6 29.9 28.6 27.5 26.5 25.5 24.8 23.8 22.6 21.6 20.4 36.4 34.4 33.4 32.0 30.3 28.9 27.9 26.8 25.8 25.1 24.1 22.8 21.8 20.6 36.6 34.8 33.8 32.4 30.6 29.2 28.2 27.1 26.1 25.4 24.4 23.0 22.0 20.9 36.8 35.2 34.1 32.7 31.0 29.6 28.5 27.5 26.4 25.7 24.6 23.2 22.2 21.1(4)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.037.0 35.5 34.4 33.0 31.2 29.8 28.8 27.7 26.6 25.9 24.8 23.4 22.4 21.3 37.2 35.9 34.8 33.4 31.6 30.2 29.1 28.0 26.9 26.2 25.1 23.7 22.6 21.5 37.4 36.3 35.2 33.8 31.9 30.5 29.4 28.3 27.2 26.5 25.4 24.0 22.9 21.8 37.6 36.7 35.6 34.1 32.3 30.8 29.7 28.6 27.5 26.8 25.7 24.2 23.1 22.037.8 37.1 36.0 34.5 32.6 31.2 30.0 28.9 27.8 27.1 26.0 24.5 23.4 22.338.0 37.5 36.4 34.9 33.0 31.5 30.3 29.2 28.1 27.4 26.2 24.8 23.6 22.5 38.2 37.9 36.8 35.2 33.4 31.8 30.6 29.5 28.4 27.7 26.5 25.0 23.9 22.7 38.4 38.3 37.2 35.6 33.7 32.1 30.9 29.8 28.7 28.0 26.8 25.3 24.1 23.039.4 40.3 38.8 37.3 35.3 33.6 32.4 31.0 30.0 29.2 27.8 26.4 25.2 24.2 39.6 40.7 39.1 37.6 35.6 33.9 32.7 31.2 30.2 29.4 28.0 26.6 25.4 24.439.8 41.2 39.6 38.0 35.9 34.2 33.0 31.4 30.5 29.7 28.2 26.8 25.6 24.740.0 41.6 39.9 38.3 36.2 34.5 33.3 31.7 30.8 30.0 28.4 27.0 25.8 25.0 40.2 42.0 40.3 38.6 36.5 34.8 33.6 32.0 31.1 30.2 28.6 27.0 26.0 25.2 40.4 42.4 40.7 39.0 36.9 35.1 33.9 32.3 31.4 30.5 28.8 27.6 26.2 25.4 40.6 42.8 41.4 39.4 37.2 35.4 34.2 32.6 31.7 30.5 29.1 27.8 26.5 25.740.8 43.3 41.6 39.8 37.7 35.7 34.5 32.9 32.0 31.2 29.4 28.1 26.8 26.041.0 43.7 42.0 40.2 38.0 36.0 34.8 33.2 32.3 31.5 39.7 28.4 27.1 26.2(5)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.041.2 44.1 42.3 40.6 38.4 36.3 35.1 33.5 32.6 31.8 30.0 28.7 27.3 26.5 41.4 44.5 42.7 40.9 38.7 36.6 35.4 33.8 32.9 32.0 30.3 28.9 27.6 26.7 41.6 45.0 43.2 41.4 39.2 36.9 35.7 34.2 33.3 32.4 30.6 29.2 27.9 27.041.8 45.4 43.6 41.8 39.5 37.2 36.0 34.5 33.6 32.7 30.9 29.5 28.1 27.242.0 45.9 44.1 42.2 39.9 37.6 36.3 34.9 34.0 33.0 31.2 29.8 28.5 27.5 42.2 46.3 44.4 42.6 40.3 38.0 36.6 35.2 34.3 33.3 31.5 30.1 28.7 27.8 42.4 46.7 44.8 43.0 40.6 38.3 36.9 35.5 34.6 33.6 31.8 30.4 29.0 28.0 42.6 47.2 45.3 43.4 41.4 38.7 37.3 35.9 34.9 34.0 32.1 30.7 29.3 28.342.8 47.6 45.7 43.8 41.4 39.0 37.6 36.2 35.2 34.3 32.4 30.9 29.5 28.643.0 48.1 46.2 44.2 41.8 39.4 38.0 36.6 35.6 34.6 32.7 31.3 29.8 28.9 43.2 48.5 46.6 44.6 42.2 39.8 38.3 36.9 35.9 34.9 33.0 31.5 30.1 29.143.8 47.9 45.9 43.2 40.9 39.4 37.9 36.9 35.9 33.9 32.4 30.9 29.944.0 48.4 46.4 43.8 41.3 39.8 38.3 37.3 36.3 34.3 32.8 31.2 30.2 44.2 48.8 46.7 44.2 41.7 40.1 38.6 37.6 36.6 34.5 33.0 31.5 30.5 44.4 47.2 44.6 42.1 40.5 39.0 38.0 36.9 34.9 33.3 31.8 30.8 44.6 47.6 45.0 42.4 40.8 39.3 38.3 37.2 35.2 33.6 32.1 31.044.8 48.0 45.4 42.8 41.2 39.7 38.6 37.6 35.5 33.9 32.4 31.345.0 48.5 45.8 43.2 41.6 40.1 39.0 37.9 35.8 34.3 32.7 31.6 45.2 48.9 46.3 43.6 42.0 40.4 39.4 38.3 36.2 34.6 33.0 31.9(6)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.045.4 46.6 44.0 42.3 40.7 39.7 38.6 36.4 34.8 33.2 32.2 45.6 47.1 44.4 42.7 41.1 40.0 39.0 36.8 35.2 33.5 32.545.8 47.5 44.8 43.1 41.5 40.4 39.3 37.1 35.5 33.9 32.846.0 47.9 45.2 43.5 41.9 40.8 39.7 37.5 35.8 34.2 33.1 46.2 48.3 45.5 43.8 42.2 41.1 40.0 37.7 36.1 34.4 33.3 46.4 48.7 45.9 44.2 42.6 41.4 40.3 38.1 36.4 34.7 33.6 46.6 46.3 44.6 42.9 41.8 40.7 38.4 36.7 35.0 33.946.8 46.7 45.0 43.3 42.2 41.0 38.8 37.0 35.3 34.247.0 47.2 45.2 43.7 42.6 41.4 39.1 37.4 35.6 34.5 47.2 47.6 45.8 44.1 42.9 41.8 39.4 37.7 36.0 34.8 47.4 48.0 46.2 44.5 43.3 42.1 39.8 38.0 36.3 35.1 47.6 48.4 46.6 44.8 43.7 42.5 40.1 38.4 36.6 35.4 47.8 48.8 47.0 45.2 44.0 42.8 40.5 38.7 36.9 35.748.2 47.8 46.0 44.8 43.6 41.1 39.3 37.5 36.3 48.4 48.2 46.4 45.1 43.9 41.5 39.6 37.8 36.6 48.6 48.6 46.7 45.5 44.3 41.8 40.0 38.1 36.948.8 49.0 47.1 45.9 44.6 42.2 40.3 38.4 37.249.0 47.5 46.2 45.0 42.5 40.6 38.8 37.5 49.2 47.9 46.6 45.4 42.8 41.0 39.1 37.8 49.4 48.3 47.1 45.8 43.2 41.3 39.4 38.2(7)平均碳化值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.049.6 48.7 47.4 46.2 43.6 41.7 39.7 38.549.8 47.8 46.5 43.9 42.0 40.1 38.850.0 48.2 46.9 44.3 42.3 40.4 39.1 50.2 48.5 47.2 44.6 42.6 40.7 39.4 50.4 49.0 47.7 45.0 43.0 41.0 39.7 50.6 48.0 45.4 43.4 41.4 40.050.8 48.4 45.7 43.7 41.7 40.351.0 48.8 46.1 44.1 42.0 40.7 51.2 46.4 44.4 42.3 41.0 51.4 46.8 44.7 42.7 41.3 51.6 47.2 45.1 43.0 41.651.8 47.5 45.4 43.3 41.852.0 47.9 45.8 43.7 42.3 52.2 48.3 46.2 44.0 42.652.6 49.0 46.9 44.7 43.352.8 47.3 45.1 43.653.0 47.6 45.4 43.9 53.2 48.0 45.8 44.3 53.4 48.3 46.1 44.6 53.6 48.7 46.4 44.9(8)平均回弹值R m测区砼强度换算值(MPa)平均碳化深度值ｄm(ｍｍ)0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5≥6.053.8 46.8 45.354.0 47.1 45.6 54.2 47.5 46.0 54.4 47.9 46.3 54.6 48.2 46.654.8 48.5 47.055.0 48.9 47.3 55.2 47.7 55.4 48.0 55.6 48.4 55.8 48.7 注：本表系按全国统一曲线制度。
C 30水水泥砂石子0.51 1.78 2.66#####Mpa Mpa ###Mpa35mf cuf cuk mf cu ###MpaMpa0MPa29mf cu,min mf cu,min＜λ4*f cu注册建造师（技术负责人）：（签字）审核人：（签字）四川省建设厅监制年 月 日年 月 日年 月 日年 月 日监理工程师：（注册方章）评定人：（签字）SG-29mf cu =λ3*f cuk 前一检验期强度标准差同一验收批强度标准差Sf cu 验收批各组试件弯拉强度：0.95P.O42.5R合格判定系数mf cu,min弯拉强度试件小于10组λ4*f cuk =根据《混凝土强度检验评定标准》GB/T50107-2010的非统计#VALUE!方法进行评定λ3*f cuk mf cu,minmf cu =试件组数n=单位工程名称：解放北路一段139号商住项目一期同一验收批强度平均值标准差已知统计方法mf cu,min =f cuk *0.7δ0=f cuk -0.7δ0f cuk =混凝土（弯拉）强度合格评定水泥品种及标号混凝土强度等级同条件养护10#楼墙柱结构部位1.15λ2=施工单位：河北建工集团有限责任公司配合比（重量比）外加剂0.018坍落度（cm）同批混凝土代表数量（）养护条件18±2λ3=λ1=λ4=λ2f cuk最小值f cu,min =非统计方法mf cu -λ1Sf u f cu,minλ2f cuk=验收评定结论：标准差未知统计方法mf cu -λ1Sf cu =#DIV/0!弯拉强度试件大于10组f cuk *0.7δ0f cuk -0.7δ0=。
混凝土抗压强度计算表详解1统计方法评定：混凝土（砂浆）试块试验结果汇总表中达到强度%，用混凝土（砂浆）的强度÷标准强度×100%（即试压结果÷强度等级×100%）n ——代表所有参与评定的混凝土组数（主体按同标号评定，分验阶段） 入1 ——查（混凝土强度检验评定标准）表........根据参与评定的组数确定。
Mfcu ——同一验收批混凝土强度的平均值Fuc ——抗压强度Fcu,min ——同一验收批混凝土强度的最小值Fcu,k ——设计混凝土强度标准值（即c20=20兆，c30=30兆） Sfcu ——同一验收批混凝土强度的标准值M 2 fcu ——同一验收批混凝土强度平均值的平方fcu,i ——第I 组混凝土试件强度值(N/mm 2)1n 1fcu2nm 2i fcu,-∑=-=n i Sfcn1/—组数强度平均数的平方组数—平方数的和同一验收批混凝土强度⨯=Sfcn∑=ni 1代表评定的每一组混凝土强度值平方后相加 nm 2fcn ——n 为组数，m 2fcn 为评定的所有试件强度的平均值再平方，计算后两数相乘n —1 所有组数减1Sfcn 为以上各数计算后相除再开平方mfcn —入1Sfcn 的计算方法：将前面计算出同代号的值代入计算 0.85fcu,k ——0.85乘以混凝土强度标准值0.95fcu,k ——0.95乘以混凝土强度标准值 ② 砂浆抗压强度计算表R n ——为砂浆强度平均值R 标 ——为砂浆设计强度等级（即M5=M5pa ，M7.5=M7.5pa ）R min ——为砂浆强度最小值③ 混凝土抗压强度计算表说明混凝土强度不低于1.15fcu,k ，当单位工程试块数量在2~9组时。
按非统计方法评定；单位工程试块数量在10组及其以上时，按统计方法进行评定。
④ 判定标准mfcu-入1Sfcu ≥0.9fcu,k统计方法fcu,min ≥入2fcu,kmfcu ≥1.15fcu,k非统计方法fcu,min ≥0.9fcu,k mfcu ——同一验收批混凝土强度的平均值——(N/mm 2)fcu,k ——设计混凝土强度的标准值——(N/mm 2)fcu,min ——同一验收批混凝土强度的最小值——(N/mm 2)Sfcu ——同一验收批混凝土强度的标准值——(N/mm 2)如Sfcu 的计算值小于0.06fcu,k 时，则取Sfcu=0.06fcu,k混凝土强度合格判定系数砂浆抗压强度计算表说明：1、同品种、同强度等级砂浆各组试块的平均强度不小于R 标2、任意一种试块强度不小于0.75R 标3、砂浆强度按单位工程为同一验收批，当单位工程种仅有一组试块时，其强度不低于R 标2非统计方法评定当试件组小于10组是，采用非评定方法评定需计算的量为：mfcu ——评定的所有试件强度平均值fcu,min ——评定的所有试件中强度的最小值1.15fcn ——1.15乘以混凝土强度标准值0.95fcn ——0.95乘以混凝土强度标准值。
