当前位置：文档之家 › 各种硬度值换算表(布氏硬度_维氏硬度_洛氏硬度)

各种硬度值换算表(布氏硬度_维氏硬度_洛氏硬度)

  • 格式：xls
  • 大小：36.50 KB
  • 文档页数：4

VickersBrinellShore

HRAHRBHRCHRD15N30N45NHVHBHS

60kgf100kgf150kgf100kgf15kgf30kgf45kgf50kgf3000kgfjis

85.668.076.993.284.475.494097.6

85.367.576.593.084.074.392096.4

85.067.076.192.983.674.290095.2

84.766.475.792.783.173.688094.0

84.465.975.392.582.773.186092.8

84.165.374.892.382.272.284091.5

83.864.774.392.181.771.882090.2

83.464.073.891.881.171.080088.9

83.063.373.391.580.470.278087.5

82.662.572.691.279.769.476086.2

82.261.872.191.079.168.674084.8

81.861.071.590.778.467.772083.3

81.360.170.890.377.666.770081.8

81.159.770.590.177.266.269081.1

80.859.270.189.876.865.768080.3

80.658.869.889.776.465.367079.6

80.358.369.489.575.964.766078.8

80.057.869.089.275.564.165078.0

79.857.368.789.075.163.564077.2

79.556.868.388.874.663.063076.4

79.256.367.988.574.262.462075.6

78.955.767.588.273.661.761074.7

78.655.267.088.073.261.260073.9

78.454.766.787.872.760.559073.1

78.054.166.287.572.159.958072.2

77.853.665.887.271.759.357071.3

77.453.065.486.971.258.656070.4

77.052.364.886.670.557.855050569.6

76.751.764.486.370.057.054049668.7

76.451.163.986.069.556.253048867.7

76.150.563.585.769.055.652048066.8

75.749.862.985.468.354.751047365.9

75.349.162.285.067.753.950046564.9

74.948.461.684.767.153.149045664.0

74.547.761.384.366.452.248044863.0

74.146.960.783.965.751.347044162.0

73.646.160.183.664.950.446043361.0

73.345.359.483.264.349.445042560.0

72.844.558.882.863.548.444041559.0

72.343.658.282.362.747.443040558.0

71.842.757.581.861.946.442039756.9

71.441.856.881.461.145.341038855.9

70.840.856.081.060.244.140037954.8

70.339.855.280.359.342.939036953.7各种硬度值换算表

Steel

RockwellRockwell Superficial69.8110.038.854.479.858.441.738036052.6

69.237.753.678.257.440.437035051.5

68.7109.036.652.878.656.439.136034150.4

68.135.551.978.055.437.835033149.3

67.6108.034.451.177.454.436.534032248.1

67.033.350.276.853.635.233031347.0

66.4107.032.249.476.252.333.932030345.8

65.831.048.475.651.332.531029444.6

65.2105.529.847.574.950.231.130028443.4

64.829.247.174.649.730.429528042.8

64.5104.528.546.574.249.029.529027542.2

64.227.846.073.848.428.728527041.6

63.8103.527.145.373.447.827.928026540.9

63.526.444.973.047.227.127526140.3

63.1102.025.644.372.646.426.227025639.7

62.724.843.772.145.725.226525239.0

62.4101.024.043.171.645.024.326024738.4

62.023.142.271.144.223.225524337.8

61.699.522.241.770.643.422.225023837.2

61.221.341.170.142.521.124523336.5

60.798.120.340.369.641.719.924022835.9

96.718.023021934.1

95.015.722020933.2

93.413.421020031.8

91.511.020019030.4

89.58.519018129.0

87.16.018017127.7

85.03.017016226.5

81.70.016015225.0

78.715014323.7

78.014013322.1

71.213012420.6

66.712011419.1

62.311010517.6

56.21009516.1

52.09590

48.09086

41.08581

Vickers

HRBHRF15T30T45THV

100kgf60kgf15kgf30kgf45kgf50kgf

93.5110.090.077.566.0196.0

109.565.5194.0

93.077.065.0192.0

92.5109.076.564.5190.0

92.089.564.0188.0

91.5108.576.063.5186.0

91.075.563.0184.0

90.5108.089.062.5182.0

90.0107.575.062.0180.0

89.074.561.5178.0

88.5107.061.0176.0

88.088.574.060.5174.0

87.5106.573.560.0172.0

87.059.5170.0

86.0106.088.073.059.0168.0

85.572.558.5166.0

85.0105.572.058.0164.0

84.0105.087.557.5162.0

83.571.556.5160.0

83.0104.571.056.0158.0

82.0104.087.070.555.5156.0

81.5103.570.054.5154.0

80.5103.054.0152.0

80.086.569.553.5150.0

79.0102.569.053.0148.0

78.0102.068.552.5146.0

77.5101.586.068.051.5144.0

77.0101.067.551.0142.0

76.0100.585.567.050.0140.0

75.0100.066.549.0138.0

74.599.585.066.048.0136.0

73.599.065.547.5134.0

73.098.584.565.046.5132.0

72.098.084.064.545.5130.0

71.097.563.545.0128.0

70.097.083.563.044.0126.0

69.096.562.543.0124.0

68.096.083.062.042.0122.0

67.095.561.041.0120.0

66.095.082.560.540.0118.0

65.094.582.060.039.0116.0

64.094.081.559.538.0114.0

63.093.081.058.537.0112.0

62.092.680.558.035.5110.0各种硬度值换算表

Rockwellockwell Superficia61.092.057.034.5108.0

59.591.280.056.033.0106.0

58.090.579.555.032.0104.0

57.089.879.054.530.5102.0

56.089.078.553.529.5100.0

54.088.078.052.528.098.0

53.087.277.551.526.596.0

51.086.377.050.524.594.0

49.585.476.549.023.092.0

47.584.475.548.021.090.0

46.083.575.047.019.088.0

44.082.374.545.517.086.0

42.081.273.544.014.584.0

40.080.073.043.012.582.0

37.578.672.041.010.080.0

35.077.471.539.57.578.0

32.576.070.538.04.576.0

30.074.870.036.01.074.0

27.573.269.034.072.0

24.571.568.032.070.0

21.570.067.030.068.0

18.568.566.028.066.0

15.556.865.025.564.0

12.568.063.523.062.0

10.063.062.520.560.0

61.061.018.058.0

58.860.015.056.0

56.558.512.054.0

63.557.052.0

50.555.550.0

49.054.549.0

47.053.548.0

45.047.0

合集下载

各种硬度换算表

各种硬度换算表

维氏布氏肖氏Vickers

HRAHRBHRCHRD15N30N45NHVHBHSHRBHRF15T30T45THV

60kgf100kgf150kgf100kgf15kgf30kgf45kgf50kgf3000kgfJIS100kgf60kgf15kgf30kgf45kgf50kgf

85.66876.993.284.475.494097.693.51109077.566196

85.367.576.5938474.392096.4109.565.5194

856776.192.983.674.290095.2937765192

84.766.575.792.783.173.68809492.510976.564.5190

84.465.975.392.582.773.186092.89289.564188

84.165.374.892.382.272.284091.591.5108.57663.5186

83.864.774.392.181.771.882090.29175.563184

83.46473.891.881.17180088.990.51088962.5182

8363.373.391.580.470.278087.590107.57562180

82.662.572.691.279.769.476086.28974.561.5178

82.261.872.19179.168.674084.888.510761176

81.86171.590.778.467.772083.38888.57460.5174

81.360.170.890.377.666.770081.887.5106.573.560172

81.159.770.590.177.266.269081.18759.5170

80.859.270.189.876.865.768080.386106887359168

80.658.869.889.776.465.367079.685.572.558.5166

硬度换算表

硬度换算表

洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算

硬度 是衡量材料软硬程度的一个性能指标。硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。最普通的是静负荷压入法硬度试验，即布氏硬度(HB)、洛氏硬度(HRA，HRB，HRC)、维氏硬度(HV)，橡胶塑料邵氏硬度(HA,HD)等硬度其值表示材料表面抵抗坚硬物体压入的能力。最流行的里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，其值代表金属弹性变形功的大小。因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。

钢材的硬度 ：金属硬度(Hardness)的代号为H。按硬度试验方法的不同，

●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。

●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。

●HV-适用于显微镜分析。维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)。

●HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/ VA（冲击速度）。

●目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列 》）

洛氏硬度、布氏硬度等硬度对照表

洛氏硬度、布氏硬度等硬度对照表

一、硬度简介

硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高，耐磨性越好。常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。

1. 布氏硬度(HB)

以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。

2. 洛氏硬度(HR)

当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示：

• HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。

• HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。

• HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。

3. 维氏硬度(HV) 以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。

注：洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。 洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。因此标尺B适用相对较软的材料，而标尺C适用较硬的材料。实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。但各种材料的换算关系并不一致。

洛氏硬度(HRC)、布氏硬度(HB)硬度换算表

洛氏硬度(HRC)、布氏硬度(HB)硬度换算表

洛氏硬度（HRC）、布氏硬度（HB）硬度换算表（表格在后面）

硬度是衡量材料软硬程度的一个性能指标。硬度试验的方法较多，原理也不相同，测得硬度

值和含义也不完全一样。最常用的是静负荷压入法硬度试验，硬度其值表示材料表面抵抗坚

硬物体压入的能力。里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，代表金属弹性

变形功的大小。因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧

性等的一种综合性能指标（参照GB/T231－1984），生产中常用布氏硬度法测定经退火、正

火和调质得刚健，以及铸铁、有色金属、低合金结构钢等毛胚或半成品的硬度。

1、钢材的硬度 ：金属硬度(Hardness)的代号为H。按硬度试验方法的不同，

●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及

HRC较为常用。

●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。两者区别在于硬度计之

测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。

●HV-适用于显微镜分析。维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压

入器压入材料表面，用材料压痕凹坑的表面积除以载荷值。

●HL手提式硬度计，利用冲击球头冲击硬度表面后产生弹跳；利用冲头在距试样表面1mm处

的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/VA（冲

击速度）。

2、HB - 布氏硬度； 一般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。

HB是以一定大小的试验载荷，将一定直径的淬硬钢球或硬质合金球压入被测金属表面，保持

规定时间，然后卸荷，测量被测表面压痕直径，载荷除以压痕球形成的表面积所得的商。一

般为：以一定的载荷(一般3000kg) 把一定大小 (直径一般为10mm) 的淬硬钢球压入材料表

面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤