WLS助剂改性的棉织物活性染料无盐染色效果评价

染整助剂综合实验论文(DOC)染整助剂综合实验学生姓名：学号：41301学院：纺织与材料学院专业班级：轻化工程13级(0)班指导教师：习智华、焦林、王雪燕目录摘要 (3)1、前言 (4)2、实验部分 (4)1、材料、药品及仪器 (5)2、实验过程 (5)3、改性工艺 (5)4、染色工艺 (6)5、测试指标 (7)3、结果与讨论 (9)1、色媒体用量的影响 (9)2、改性处理温度的影响 (10)3、改性处理时间的影响 (11)4、结论 (12)5、参考文献 (13)色媒体对棉织物活性染料染色性能的影响摘要活性染料染色时，因加人大量的无机盐(如氯化钠、元明粉)促染，以及加碱固色，导致染液中盐碱含量高，严重破坏生态环境。

本试验采用色媒体(广东德美精细化工股份有限公司)对棉织物进行改性，然后进行活性染料无盐染色。

研究了色媒体改性工艺温度、改性时问和色媒体用量对改性织物染色KS值和上染百分率的影响。

结果表明，色媒体对棉织物活性染料染色的染料固着率和上染率都有所提高。

改性棉织物的K/S值和上染百分率和加盐促染的K/S值和上染百分率一致。

改性剂色媒体用量应控制在5%（owf）为宜，改性35min，染色时，染料选择KN型活性染料2%（owf），纯碱用量为10 g/L，固色30min。

该工艺具有环保的意义。

关健词:染色；KN型活性染料；色媒体；棉纤维，改性Reactive dyes dyeing, adds a lot of inorganic salts such as sodium chloride, sodium sulfate promote dye and alkali fixation, leading to dye in the salt content was high, serious damage to the ecological environment. This test uses color media (Guangdong DEMEI Fine Chemical Co., Ltd.)modification of cotton fabric, and salt free dyeing of reactive dyes. The effects of color media modification process temperature, time and color media amount on KS value and dye uptake of modified fabric were studied. The results show that the color media on dyeing of cotton fabric with reactive dyes dye fixation and dyeing rate are improved. Modified cotton fabric K/S value and dye uptake and salt dyeing K/S value and dye uptake consistent. Modified agent color media consumption should be controlled at 5% (OWF) is appropriate, 35min, dyeing, dyestuff selection kn type reactive dye 2% (OWF), soda ash dosage of 10 g / L, solid color 30min. This process has the significance of environmental protection.Key words: dyeing, KN type reactive dyes, color media, cotton fiber，modification1、前言纤维素纤维在染浴中带负电荷，而大多数染棉的染料均呈阴离子性，由于静电斥力，染料上染受到抑制，染浴中往往需要加入大量的中性电解质来屏蔽静电斥力的作用，起促染作用，从而提高染料上染百分率。

改性棉织物活性荧光黄FL无盐染色王娜;陈艺佳;李峻;李武龙;胡会娜;李田田;曹机良【摘要】采用活性荧光黄FL对改性棉织物进行无盐染色,探讨了氯化钠和碳酸钠用量、染色温度和时间对改性棉织物染色性能的影响,测试了改性棉织物染色K/S 值和染色牢度.结果表明:活性荧光黄FL 1%(omf),碳酸钠10 g/L,染色温度65℃,保温时间40 min时,改性棉织物无盐染色具有较好的染色性能和较高的耐洗和耐摩擦色牢度.%The reactive florescent yellow FL was used in salt-free dyeing of modified fabrics. The effects of the concentration of sodium chloride and sodium carbonate, finishing temperature and time on the dyeing performance of modified cotton fabrics were researched, and the dyeing K/S value and color fastness were tested. The results showed that when the salt-free dyeing process was reactive fluorescent yellow FL 1% (omf), sodium carbonate 10 g/L, dyeing temperature 65 ℃, time 40 min, the dyeing performance and color fastness to washing and rubbing were good.【期刊名称】《印染助剂》【年(卷),期】2018(035)004【总页数】4页(P50-53)【关键词】棉织物;改性;活性荧光黄FL;染色;无盐【作者】王娜;陈艺佳;李峻;李武龙;胡会娜;李田田;曹机良【作者单位】河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院河南省服用纺织品工程技术研究中心,河南郑州450007;新乡市新科防护科技有限公司,河南新乡453003;河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院材料与化学工程学院,河南郑州450007;河南工程学院河南省服用纺织品工程技术研究中心,河南郑州450007【正文语种】中文【中图分类】TS116;TS193.6棉织物一般用活性染料染色，在碱剂条件下进行固色提高染色牢度，但染色过程中需要加入大量的中性电解质进行促染，由于大量电解质的存在，使印染废水中的无机盐量增大，对后期的废水处理带来很大困难，生产成本增加［1-2］。

色媒体改性棉织物直接染料无盐浸染染色作者：王洪海钟建生赵春梅来源：《纺织导报》2014年第03期摘要：采用改性剂色媒体改性棉织物，通过分析改性剂色媒体用量、染色温度、染色时间、染色浴比等工艺参数对染色效果的影响，优化改性棉织物直接染料无盐浸染染色工艺，并对织物改性前后的染色效果进行对比。

当染料用量为1%（o.w.f）时，试验得出的优化工艺条件为：改性剂用量3%（o.w.f），染色温度90 ℃，染色时间50 min，染色浴比1∶30。

对比实验的结果表明，棉织物改性后直接染料浸染染色的K/S值有所提高，耐皂洗色牢度和耐摩擦色牢度等级与传统工艺基本一致，可实现直接染料无盐浸染染色；关键词：棉织物；改性剂；直接染料；浸染中图分类号：TS193.632 文献标志码：ASalt-free Dip Dyeing of Cotton Fabric Modified by Color Media with Direct DyeAbstract： Cationic modifier Color Media was applied in modification of cotton fabric， and then the influences of process conditions such as modifier dosage， dyeing temperature， dyeing time and dyeing liquor ratio on dyeing modified cotton fabric were analyzed. The dyeing effect of modified cotton fabric and unmodified cotton fabric were compared. The process of salt-free direct dye dip dyeing of modified cotton fabric was optimized， and the optimal process conditions were as follows： modifier dosage 3%（o.w.f）， dyeing temperature 90℃ dyeing time 50 min and dyeing liquor ratio 1∶30， when the dosage of direct dye was 1%（o.w.f）. The results indicated that cotton fabric modified with Color Media featured high K/S value， similar washing and rubbing fastness to those of traditional dyeing， and the salt-free dip dyeing was viable and practical.Key words： cotton fabric； cationic modifier； direct dye； dip dyeing直接染料色谱齐全，染色工艺简便，价格低廉，是棉纤维制品染色常用的染料之一。

WLS助剂改性棉纱线活性染料的动力学与热力学性能的研究郝波;王立平【摘要】本文介绍了染色基本理论：染色动力学理论和染色热力学理论的原理，用阳离子改性剂WLS对棉纱线进行改性，对WLS改性棉纱线进行染色处理，并分析了改性前后的棉纱线染色原理的变化，为以后的活性染料的无盐染色的实际应用提供理论依据。

【期刊名称】《中国纤检》【年(卷),期】2014(000)011【总页数】4页(P78-81)【关键词】活性染料;染色动力学理论;染色热力学理论;阳离子改性剂WLS【作者】郝波;王立平【作者单位】淄博市纤维纺织产品监督检验所;淄博市纤维纺织产品监督检验所【正文语种】中文活性染料自1956年问世以来，由于其解决了棉纱线染色湿处理牢度差的问题，同时具有色谱齐全、色泽鲜艳、应用工艺简便、实用性强、价格相对便宜等优点，近年来已成为棉纱线所用染料中产量和产值最大的染料。

但是，在活性染料染棉的传统工艺中，需要加入无机盐促进染料上染，因此导致废水中无机离子过多难以处理，致使污水处理成本大大增加。

本文主要是针对无机盐促染，染料水解利用率不高以及增加废水处理负担的问题，选择自制的阳离子改性剂改性棉纱线并进行染色处理。

重点研究改性前后棉纱线染色动力学和染色热力学性能变化，并评价改性效果，为以后活性染料无盐染色的实际应用提供理论依据。

1 染色基本理论1.1 染色动力学理论上染速率通常以纤维上染料浓度对时间的变化率来表示，或者以达到一定上染百分率所需的时间来表示。

上染百分率表示吸附在纤维上的染料量占投入染料总量的百分率。

在恒温条件下进行染色，以纤维上染料浓度或上染率为纵坐标，染色时间为横坐标作图，所得曲线称为上染速率曲线，是染色动力学的基础。

1.2 染色热力学理论染色热力学研究染色平衡问题，其中吸附等温线是其研究的一个重要问题。

吸附等温线是在恒定温度下，上染达到平衡时，纤维上的染料浓度和染液中染料浓度的关系曲线即为吸附等温线，这是染色热力学的基础，表达染料在一定温度下对纤维的上染能力。

2010年 2 月阳离子改性蛋白助剂WLS-10在棉印染上的应用（西安工程大学 陕西 西安 710048）摘要：用自制的阳离子改性蛋白助剂WLS-10对棉织物进行改性，然后采用活性染料无盐染色。

通过研究确定出改性剂WLS-10改性棉织物的最佳工艺条件，并评价改性织物活性染料的染色性能。

结果表明，改性棉织物采用活性染料无盐染色，可获得比未改性棉织物常规加盐染色更高的上染百分率和染色牢度，并具有更好的润湿性。

WLS-10助剂改性的棉织物可实现活性染料无盐染色。

关键词：改性；无盐染色；活性染料；棉织物中图分类号：TS 193.2 文献标识码：B 文章编号：1005-9350(2010)02-0035-05收稿日期：2009-09-16作者简介：卢焕敏（1985-），女，河南许昌人，西安工程大学在读硕士研究生，主要从事纺织品功能整理理论与技术的研究卢焕敏 王雪燕 陈 乐 丁 娟活性染料染纤维素纤维存在吸尽率和固色率低的问题，染浴中往往需要加入大量的无机电解质盐来提高染料的上染百分率。

这些电解质随染色废液排出，给环境造成了极大的污染。

用含有不同反应性基团的胺类或季铵盐类阳离子低分子物或高分子物改性剂对纤维素纤维进行化学改性，减少或消除纤维上负电荷效应，显著提高纤维对阴离子染料吸附能力，从而为实现活性染料低盐、或无盐染色提供一条有效途径[1]。

本实验采用自制的阳离子改性的高分子鸡毛蛋白助剂WLS-10对棉织物进行改性。

WLS-10是一种用含有环氧乙烷活性基阳离子助剂改性的鸡毛蛋白助剂。

此改性剂不仅含有正电荷，而且含有蛋白结构所具有的氨基、羟基等极性基团，易溶于水。

在碱性条件下与纤维素纤维有很好的反应性。

用其改性棉织物，可增强对阴离子活性染料的吸附性能，实现活性染料无盐染色，同时有望进一步改善棉织物的服用性能。

本文重点研究WLS-10助剂对棉织物的改性及其改性织物活性染料无盐染色性能。

1.1 材料材料：纯棉织物:20×20，60×60，47＂，阳离子改性蛋白助剂WLS-10：自制。

基于活性阳离子改性剂ECO活性染料零盐染色工艺研究陈文【摘要】用阳离子改性剂ECO对棉织物进行阳离子化改性,然后采用活性染料无盐染色.确定了阳离子改性剂ECO改性棉织物的最佳工艺条件及其染色工艺条件,评价了改性织物的染色性能.结果表明:改性棉织物采用活性染料无盐染色,可获得比未改性棉织物常规加盐染色更高的K/S值和染色牢度.阳离子改性剂ECO改性的棉织物可实现活性染料深色无盐染色.【期刊名称】《浙江纺织服装职业技术学院学报》【年(卷),期】2018(017)002【总页数】6页(P19-23,28)【关键词】冷堆;浸染;零盐染色;活性染料;K/S值【作者】陈文【作者单位】浙江纺织服装职业技术学院纺织学院,浙江宁波315211【正文语种】中文【中图分类】TS193.6321 前言活性染料具有优良的湿牢度和匀染性能，而且色泽鲜艳，使用方便，色谱齐全，成本低廉，是目前印染企业广泛应用的染料。

但是活性染料染色利用率低，为了促进染料上染，染色时需要加入大量的中性电解质，在大浴比时更为突出。

加入中性电解质虽然提高了染料利用率，减少了染料在污水中的质量分数，但电解质对环境污染严重，使淡水盐化，而且很难处理。

为此，近年来国内外大力研究如何减少盐用量，进行低盐或无盐染色，并已成为一个重要研究课题。

活性染料又称反应性染料，是在染色时与纤维起化学反应的染料。

这类染料分子中含有能与纤维发生化学反应的基团，染色时染料与纤维反应，二者之间形成共价键，成为整体，使耐洗和耐摩擦牢度提高。

根据染色理论，在活性染料浸染时，盐有多方面的作用，最重要的是起电荷屏蔽作用。

在碱性水溶液中，纤维素纤维表面带负电荷，吸附上活性染料阴离子后，负电荷还会增加，阻止活性染料阴离子上染，降低上染速度、平衡上染量、染料利用率和染深性。

加入中性电解质后，它的阳离子起电荷屏蔽作用，减少了染料阴离子与纤维负电荷的斥力，起促染作用。

为了减少盐的用量或实现无盐染色，业界目前采用的主要方法是对纤维进行阳离子化处理。