洛氏硬度、布氏硬度、维氏硬度的换算表

洛氏硬度、布氏硬度、维氏硬度对照表以下是洛氏硬度、布氏硬度、维氏硬度的常用范围值的对照表。

洛氏硬度HRC 洛氏硬度HRA 布氏硬度HB 30D2维氏硬度HV 近似强度σ(MPa)70.0 86.6 - 1037.0 --69.5 86.3 -1017.069.0 86.1 - 997.0 -68.5 85.8 - 978.0 -68.0 85.5 - 959.0 -67.5 85.2 - 941.0 -67.0 85 - 923.0 -66.5 84.7 - 906.0 -66.0 84.4 - 889.0 -65.5 84.1 - 872.0 -65.0 83.9 - 856.0 -64.5 83.6 - 840.0 -64.0 83.3 - 825.0 -63.5 83.1 - 810.0 -63.0 82.8 - 795.0 -62.5 82.5 - 780.0 -62.0 82.2 - 766.0 -61.5 82.0 - 752.0 -61.0 81.7 - 739.0 -60.5 81.4 - 726.0 -60.0 81.2 - 713.0 2607 59.5 80.9 - 700.0 2551 59.0 80.6 - 688.0 2496 58.5 80.3 - 676.0 2443 58.0 80.1 - 664.0 2391 57.5 79.8 - 653.0 2341 57.0 79.5 - 642.0 2293 56.5 79.3 - 631.0 2247 56.0 79.0 - 620.0 2201 55.5 78.7 - 609.0 2157 55.0 78.5 - 599.0 2115 54.5 78.2 - 589.0 2074 54.0 77.9 - 579.0 2034 53.5 77.7 - 570.0 1995 53.0 77.4 - 561.0 1957 52.5 77.1 551.0 1921 52.0 76.9 543.0 1885 51.5 76.6 534.0 1851 51.0 76.3 525.0 1817 50.5 76.1 517.0 1785 50.0 75.8 509.0 1753 49.5 75.5 501.0 1722 49.0 75.3 493.0 1692 48.5 75.0 485.0 1662 48.0 74.7 478.0 163547.5 74.5 470.0 1608 47.0 74.2 449 463.0 1581 46.5 73.9 442 456.0 1555 46.0 73.7 436 449.0 1529 45.5 73.4 430 443.0 1504 45.0 73.2 424 436.0 1480 44.5 72.9 413 429.0 1457 44.0 72.6 407 423.0 1434 43.5 72.4 401 417.0 1411 43.0 72.1 396 411.0 1389 42.5 71.8 391 405.0 1368 42.0 71.6 385 399.0 1347 41.5 71.3 380 393.0 1327 41.0 71.1 375 388.0 1307 40.5 70.8 370 382.0 1287 40.0 70.5 365 377.0 1268 39.5 70.3 360 372.0 1250 39.0 70.0 355 367.0 1232 38.5 69.7 350 362.0 1214 38.0 69.5 345 357.0 1197 37.5 69.2 341 352.0 1180 37.0 69.0 336 347.0 1163 36.5 68.7 332 342.0 1147 36.0 68.4 327 338.0 1131 35.5 68.2 323 333.0 111535.0 67.9 318 329.0 1100 34.5 67.7 314 324.0 1080 34.0 67.4 310 320.0 1070 33.5 67.1 306 316.0 1056 33.0 66.9 302 312.0 1042 32.5 66.6 298 308.0 1028 32.0 66.4 294 304.0 1015 31.5 66.1 291 300.0 1001 31.0 65.8 287 296.0 989 30.5 65.6 283 292.0 976 30.0 65.3 280 289.0 964 29.5 65.1 276 285.0 951 29.0 64.8 273 281.0 940 28.5 64.6 269 278.0 928 28.0 64.3 266 274.0 917 27.5 64.0 263 271.0 906 27.0 63.8 260 268.0 895 26.5 63.5 257 264.0 884 26.0 63.3 254 261.0 874 25.5 63.0 251 258.0 864 25.0 62.8 248 255.0 854 24.5 62.5 245 252.0 844 24.0 62.2 242 249.0 835 23.5 62.0 240 246.0 825 23.0 61.7 237 243.0 81622.5 61.5 234 240.0 80822.0 61.2 232 237.0 799以上数据摘自《实用五金手册》广东科技出版社，2004.3硬度试验是机械性能试验中最简单易行的一种试验方法。

维氏、布氏、洛氏硬度的换算表根据德国标准DIN50150,以下是常用范围的钢材维氏硬度、布氏硬度、洛氏硬度的对照表:常见金属（如碳钢，合金钢等）的硬度换算表洛氏硬度表面洛氏硬度维氏布氏肖氏HRA HRB HRC HRD15N30N45N HV HB HS 60kgf100kgf150kgf100kgf15kgf30kgf45kgf50kgf3000kgf JIS 85.66876.993.284.475.494097.6 85.367.576.5938474.392096.4 856776.192.983.674.290095.2 84.766.575.792.783.173.688094 84.465.975.392.582.773.186092.8 84.165.374.892.382.272.284091.5 83.864.774.392.181.771.882090.2 83.46473.891.881.17180088.9 8363.373.391.580.470.278087.5 82.662.572.691.279.769.476086.2 82.261.872.19179.168.674084.8 81.86171.590.778.467.772083.3 81.360.170.890.377.666.770081.8 81.159.770.590.177.266.269081.1 80.859.270.189.876.865.768080.3 80.658.869.889.776.465.367079.6 80.358.369.489.575.964.766078.8 8057.86989.275.564.16507879.857.368.78975.163.564077.2 79.556.868.388.874.66363076.4 79.256.367.988.574.262.462075.6 78.955.767.588.273.661.761074.7 78.655.2678873.261.260073.9 78.454.766.787.872.760.559073.1 7854.166.287.572.159.958072.2 77.853.665.887.271.759.357071.3 77.45365.486.971.258.656070.4 7752.364.886.670.557.855050569.6 76.751.764.486.3705754049668.7 76.451.163.98669.556.253048867.7 76.150.563.585.76955.652048066.8 75.749.862.985.468.354.751047365.9 75.349.162.28567.753.950046564.9 74.948.461.684.767.153.149045664 74.547.761.384.366.452.248044863 74.146.960.783.965.751.347044162 73.646.160.183.664.950.446043361 73.345.359.483.264.349.445042560 72.844.558.882.863.548.444041559 72.343.658.282.362.747.443040558 71.842.757.581.861.946.442039756.9 71.441.856.881.461.145.341038855.9 70.840.8658160.244.140037954.8 70.339.855.280.359.342.939036953.7 69.811038.854.479.858.441.738036052.669.237.753.679.257.440.437035051.5 68.710936.652.878.656.439.136034150.4 68.135.551.97855.437.835033149.3 67.610834.451.177.454.436.534032248.1 6733.350.276.853.635.233031347 66.410732.249.476.252.333.932030345.8 65.831.648.475.851.832.831029444.6 65.2105.529.847.574.950.231.130028443.4 64.829.247.174.649.730.429528042.8 64.5104.528.546.574.24929.529027542.2 64.227.84673.848.428.728527041.6 63.8103.527.145.373.447.827.928026540.9 63.526.444.97347.227.127526140.3 63.110225.644.372.646.426.227025639.7 62.724.843.772.145.725.226525239 62.41012443.171.64524.326024738.4 6223.142.271.144.223.225524337.8 61.699.522.241.770.643.422.225023837.2 61.221.341.170.142.521.124523336.5 60.798.120.340.369.641.719.924022835.996.71823021934.19515.722020933.293.413.421020031.891.51120019030.489.58.51901812987.1618017127.7853********.581.701601522578.715014323.77814013322.171.213012420.666.712011419.162.311010517.656.21009516.1注：上表中有洛氏硬度、表面洛氏硬度之分，这有什么区别呢，简单来说，如果零件比较薄,如下面这种管壁状的零件：由于这样的产品壁比较薄，普通的洛氏硬度测试头直接把产品压扁，但这并不代表零件本身没有硬度，所以这种情况下采用的是表面洛氏硬度测量法。

硬度是指金属材料抵抗更硬物体压入其表面的能力。

在模具、机械等行业的实际生产工作中，无论是我们的技术人员，亦或是业务人员，都需要接触到不同钢材的硬度。

因为硬度存在着洛氏硬度、布氏硬度、维氏硬度等几种不同的测试方法，所以为了便于比较，我们需要对不同的硬度进行换算。

洛氏、布氏、维氏等硬度之间究竟如何换算?换算公式是怎样的呢?【硬度换算公式】1.努氏硬度与维氏硬度的换算(1)以相同硬度的物体对努氏维氏两种压头具有相等的抗力为依据，分别对维氏努氏两种压头在加载荷下的应力进行推导，再根据σHK=σHV得出：HV=0.968HK。

本公式是在低载荷下测得，误差比较大。

此外在硬度值大于HV900时此公式误差很大，失去参考价值。

(2)经过推导与修正提出努氏硬度与维氏硬度的换算公式为经实际数据验证，该公式的最大相对换算误差为0.75%，具有较高的参考价值。

2.洛氏硬度与维氏硬度的换算(1)对Hans·Qvarnstorm提出的The Qvarnstorm换算公式进行修正后得出洛氏硬度与维氏硬度的换算公式为：此公式用我国公布的黑色金属硬度标准数据进行换算，其HRC误差基本上在±0.4 HRC 范围内，其最大误差也仅士0.9HRC，计算的HV误差最大为±15HV。

(2)根据不同压头所受应力σHRC=σHV，通过对洛氏硬度与维氏硬度压痕深度关系曲线的分析得出公式本公式与国家标准实验换算值对照,换算式计算结果与标准实验值之误差为±0.1HRC。

(2)根据实际的实验数据利用线性回归的方法对洛氏硬度与维氏硬度的换算进行探讨，得出公式：本公式使用范围小，误差较大，但计算简便，在对精度要求不高时可以使用。

3.洛氏硬度与布氏硬度的换算(1)对布氏压痕和洛氏压痕深度关系进行分析，根据压头的应力σHRC =σHB得出换算公式计算结果与国家标准实验值对照，换算式计算结果与标准实验值之误差为±0.1HRC。

硬度換算公式:1.肖氏硬度(HS)=勃式硬度(BHN)/10+122.肖式硬度(HS)=洛式硬度(HRC)+153.勃式硬度(BHN)= 洛克式硬度(HV)4.洛式硬度(HRC)= 勃式硬度(BHN)/10-3硬度測定範圍:HS<100HB<500HRC<70HV<1300铸铁的布氏(HB)硬度在140左右铜及其合金的布氏硬度在35-200 轻金属及其合金布氏硬度大概在35-80(80~88)HRA, (85~95)HRB, (20~70)HRC洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。

洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。

标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。

因此标尺B适用相对较软的材料，而标尺C适用较硬的材料。

实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。

因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。

但各种材料的换算关系并不一致。

硬度表示材料抵抗硬物体压入其表面的能力。

它是金属材料的重要性能指标之一。

一般硬度越高，耐磨性越好。

常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。

1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。

2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。

硬度知识一、硬度简介：硬度表示材料抵抗硬物体压入其表面的能力。

它是金属材料的重要性能指标之一。

一般硬度越高，耐磨性越好。

常用的硬度指标有布氏硬度、洛氏硬度和维氏硬度。

1.布氏硬度(HB)以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2 (N/mm2)。

2.洛氏硬度(HR)当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。

它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。

根据试验材料硬度的不同，分三种不同的标度来表示：•HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。

•HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。

•HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。

3 维氏硬度(HV)以120kg以的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度HV值(kgf/mm2)。

############################################################################################# 注：洛氏硬度中HRA、HRB、HRC等中的A、B、C为三种不同的标准，称为标尺A、标尺B、标尺C。

洛氏硬度试验是现今所使用的几种普通压痕硬度试验之一，三种标尺的初始压力均为98.07N(合10kgf)，最后根据压痕深度计算硬度值。

标尺A使用的是球锥菱形压头，然后加压至588.4N(合60kgf)；标尺B使用的是直径为1.588mm(1/16英寸)的钢球作为压头，然后加压至980.7N(合100kgf)；而标尺C使用与标尺A相同的球锥菱形作为压头，但加压后的力是1471N(合150kgf)。

洛氏-布氏-维氏-努氏硬度换算表1、努氏与维氏硬度换算(两种方法)a、HV=0.968HK注：本公式误差较大，在大于HV900时此公式失去参考价值b、HV=3033HK/{3066/{62.555/{（1088-HK）+0.9077}}}+|HK-355|注：此公式具有较高参考价值，最大换算误差为0.75％2、洛氏与维氏硬度换算（三种方法）a、HRC=100*HV-15100/HV+223HV在520以上HRC=100*HV-13700/HV+223HV在200-520之间注：此公式换算HRC基本上在±0.4范围内；最大误差为±0.9HRC，±15HVb、HRC=99.6-√{(1585324-658HV)*HV}注：此公式换算HRC基本上在±0.1范围内；√是开根号的意思c、HRC=8.32+0.0834HV329<HV<517注：此公式使用范围小，误差较大，但计算简便，对精度要求不高情况下使用。

3、洛氏与布氏硬度换算（两种方法）a、HRC=52.76-√{（103500000-218600*HB）/HB2}注：此公式换算HRC基本上在±0.1范围内；√是开根号的意思b、HRC=6.96+0.089HB323<HB<501注：此公式使用范围小，误差较大，但计算简便，对精度要求不高情况下使用。

4、布氏与维氏硬度换算a、HB=(HV+10.5)/1.05注：此公式换算HV基本上在±2范围内；5、努氏与洛氏硬度换算a、HK=0.1663021*（HRC）2-2.6482344*HRC+239.71320注：此公式比较精确，可以作为使用参考；。