收稿日期:2013-09-17一一修改日期:2013-11-01Surface Modification of Carbon Black Used to the Display Technology and Its Properties ?
RONG Mengxin 1,LIN Zulun 1?,YE Xiangping 2,QI Kangcheng 2,WANG Xiaoju 2
(1.School of Optoelectronic Information ,University of Electronic Science and Technology of China ,Chengdu 610054,China ;2.Guangdong Huizhou Quality and Measuring Supervision Testing Institute ,Huizhou Guangdong 516003,China )
Abstract :The surface of carbon black particles were modified by concentrated nitric acid(50%)and silane coupling agent (KH550).The particle size,morphology and element content of the modified carbon black were characterizated by using scanning electronic microscope(SEM)and energy-dispersive X-ray spectroscopy (EDS).The dispersity of modified carbon black in TCE was analyzed by using metalloscope and UV-VIS spectrophotometer.The electric field response characteristic of the oxidation modified carbon black was tested by using the self-made electrophoretic apparatus.The results indicated that the conductivity of the modified carbon black was decreased,and it has better dispersity and electric field response characteristic.Also,the dispersity of the modified carbon black in the TCE can be effectively improved with charge control agent span -80.Key words :carbon black;surface modification;dispersity;electric field responset transparent rate EEACC :0520一一一一doi :10.3969/j.issn.1005-9490.2014.06.005
用于显示技术的炭黑表面改性及其特性研究?
荣孟欣2,林祖伦1?,叶祥平2,祁康成2,王小菊2
(1.电子科技大学光电信息学院,成都610054;2.广东省惠州市质量计量监督检测所,广东惠州516003)摘一要:采用浓硝酸(50%)与硅烷偶联剂(KH550)分别对炭黑进行了表面改性三采用SEM二EDS 研究了改性炭黑的粒径二形貌及元素含量;采用金相显微镜和紫外-可见光分光光度计分析了改性炭黑在四氯乙烯中的分散性三利用自制电泳装置测试了氧化改性炭黑的电场响应特性三结果表明,表面改性后的炭黑电导率下降,具有更优良的分散性与电场响应特性三电荷控制剂span -80可以有效提高改性炭黑在TCE 中的分散性三
关键词:炭黑;表面改性;分散性;电场响应;透过率
中图分类号:TN104.3一一一一文献标识码:A一一一一文章编号:1005-9490(2014)06-1034-05
一一炭黑是一种微观结构二粒子形态和表面性能都极为特殊的炭素材料,[1]具有良好的耐光性二抗静电性二耐热性二耐化学性二耐候性以及低热膨胀系数,且来源丰富二价格低廉三主要应用于橡胶二涂料二塑料二油墨二化纤以及电炭等行业三[2-4]在飞速发展的显示技术中,无论是在电子墨水中作为电泳颗粒,还是在裸眼3D 显示中作为视差屏障的光栅,炭黑都有着广泛的应用三然而,炭黑是由大量的原生粒子聚集而成的,该聚集体表面积大,且又含有丰富的极性基团,故在炭黑有机溶剂体系中存在表面润湿性
低,分散性能差,电导率较大等特点,限制了炭黑在
显示领域的应用三[5-6]为了解决这些问题,炭黑的表
面改性受到人们的广泛关注三目前,炭黑的改性方
法有包覆改性法二表面吸附处理改性法二表面接枝改
性法二表面氧化改性法二表面卤化改性法等三[7-8]本
实验根据炭黑作为显示技术功能材料的要求,针对
炭黑的分散性,电场响应特性以及电导率,对炭黑进
行了表面改性研究三同时对氧化改性和接枝改性的
炭黑性能作了初步研究三得到适用于显示颗粒的改
性炭黑三