UPGRADING OF A LOW-GRADE TITANIUM SLAG BY SULPHATION ROASTING TECHNIQUE TO PRODUCE SYNTHETIC RUTILE
Fouad O. A.
Central Metallurgical Research and Development Institute, CMRDI, P.O.Box: 87 Helwan 11421, Cairo, Egypt, E-mail: oafouad@https://www.doczj.com/doc/cf18247634.html,
ZVY?ENIE KVALITY NíZKO KVALITNEJ TITáNOVEJ TROSKY POMOCOU SULFATA?NéHO PRA?ENIA PRE ú?ELY PRíPRAVY SYNTETICKéHO RUTILU Fouad O. A.
Central Metallurgical Research and Development Institute, CMRDI, P.O.Box: 87 Helwan 11421, Cairo, Egypt, E-mail: oafouad@https://www.doczj.com/doc/cf18247634.html,
Abstrakt
Cie?om práce bolo pre?tudova? mo?nosti zvy?enia kvality nízko kvalitnej titánovej trosky (~55 hm.% TiO2) s vysokym obsahom oxidov kremíka, vápnika, hor?íka a ?eleza prostredníctvom sulfata?ného pra?enia, po ktorom nasleduje kyslé lúhovanie. Rtg. difrak?ná fázová analyza sulfata?ne pra?enej trosky poukázala na prítomnos? kennedyitu (Fe2O3.MgO.3TiO2), rutilu (TiO2), sulfátu vápenatého (CaSO4) a kalciumsilkátovej fázy (3CaO.SiO2). Zvy?ok po lúhovaní obsahuje najm? kennedyit, rutil, vo?ny oxid kremíka a stopy kalciumsilikátovej fázy. Ak je vzorka pra?ená pri 800°C po dobu jednej hodiny, je mo?né dosiahnu? odstránenie 80% vápnika, 37% hor?íka a 20% ?eleza. Pri vy??ích teplotách pra?enia sa stáva povrch peliet viac kompaktnym, ?o sp?sobuje spoma?ovanie difúzie sulfata?ného plynu do vnútra peliet a následne sa zni?uje stupeň sulfatácie. Obohatená troska obsahuje okolo 72% TiO2. Pred sulfatáciou je potrebné kyslé lúhovanie za ú?elom odstránenia v???iny ?eleza v dvojmocnej forme. Takéto predlúhovanie napomáha v de?trukcii v?zieb v troske, ?o má za následok zvy?enie stupňa sulfatácie a napomáha k odstráneniu okolo 40% vápnika, 20% hor?íka a 40% ?eleza. Postupom popísanym v tejto práci je mo?né získa? synteticky rutil s obsahom TiO2 okolo 83%. Termodynamické vypo?ty poskytujú racionálne zd?vodnenia získanych vysledkov a nazna?ujú, ktoré reakcie v tomto procese prebiehajú.
Abstract
Upgrading of a low-grade titanium slag (~55% TiO2) with high silica, calcia, magnesia and iron contents has been studied using sulphation roasting technique followed by acid leaching. XRD analysis of the sulphated slag reveals the presence of kennedyite (Fe2O3. MgO. 3TiO2), rutile (TiO2), calcium sulphate (CaSO4) and calcium silicate phases (3CaO.SiO2). The residue after leaching contains mainly kennedyite and rutile phases and free silica (SiO2) with traces of calcium silicate phase (CaO.SiO2). Removal of 80% calcium, 37% magnesium and 20% iron is achieved for sample treated at 800 o C for 60 min. Above this temperature the surface of the slag pellet becomes compact and retards the diffusion of the sulphating gas mixture into the pellet core and consequently the sulphation extent decreases. The upgraded slag contains about 72% TiO2. Acid leaching of this slag prior to sulphation roasting process is necessary to remove most of the iron in the ferrous state. This pre-leaching step enhances the break down of the slag structure and promotes its sulphation extent and helps removal of about 40% calcium, 20% magnesium and 40% iron. Synthetic rutile that has about 83% TiO2 can be
produced via process described in this work. Thermodynamic calculations give rational explanations of the obtained results and the suggested reactions.
Keywords: ilmenite, titanium slag; sulphation roasting; synthetic rutile
1. Introduction
In recent years there has been considerable research interest in utilizing ilmenite ore, the alternative abundant source for titanium, instead of the rare mineral, rutile. This is because of increasing demand for rutile to produce titanium tetrachloride (TiCl4) for use in titanium dioxide pigment and titanium metal production [1].
The feasibility of various processes for production of synthetic rutile from ilmenite could be classified into three main types, namely thermal reduction, selective chlorination and selective leaching. Thermal reduction is usually done either in an electric arc furnace (slagging process) or rotary kiln (nonslagging process) to form metallic iron and titanium oxide [2].
Several technologies today are using smelting technique to produce TiO2 slag and pig iron from ilmenite ore [3]. In this process, most of the Fe2O3 and FeO are reduced to metallic iron with a small amount of ferrous iron left in the slag to make it viscousless. A pseudobrookite phase, being the most suitable feed for the sulphate process, has been produced in the slag. If a rutile phase were produced, it would only be suitable for the chlorination process [4].
Many authors have proposed and reported different methods and techniques to treat titanium slag for producing a synthetic rutile [4-11]. Some of those techniques are practically applicable and some others are limited. A titaniferrous slag containing about 60-70% TiO2 was aged at high temperature of 1200o C for up to 72 hours in Ar atmosphere in presence of titanium pyrophosphate flux (2-15 % P2O5 equivalent), B2O3 and their binary mixtures [5-7]. This process converted the titanium bearing phases to discrete rutile crystals and a phosphate glass phase containing most of the associated impurities which dissolved further in mineral acid solution. Such as this technique is impractical since it needs long time period under Ar atmosphere at relatively high temperature and the use of expensive additives.
Calcined synthetic rutile containing 95-96 % TiO2 has been produced from low grade titanium slag containing 71-72 % TiO2 by soda ash roasting at temperature from 600 to 950 o C followed by two leaching stages in water and sulphuric acid. In this case the acid leaching is effectively only under drastic conditions [8]. Typical leaching temperature from 175 to 200 o C and pressure of 11.5 to 13.5 atm are necessary to break down the slag structure. Such leaching medium is a corrosive medium and it is impractical on industrial scale.
On the other hand, different sulphating agents including H2SO4, SO2/air mixture, SO3, (NH4)2SO4, NH4HSO4, Na2SO4, NaHSO4, Fe2(SO4)3, FeSO4, FeS2 and S have been used to treat either ilmenite ore or titanium slag [9-11]. Among them the treatment with SO2/air gas mixture or SO3 gas seems to be the most feasible one. This is because that of the treatment is carried out at a relatively moderate temperature range (600-1100 o C) at a relatively low flow rate (50-100 ml/min) and it is a gas/solid reaction which is easy to control. In addition the sulphation of high temperature oxides such as Ca and Mg can be achieved.
In a previous work that has been carried out by our group, a low-grade titanium slag (55-60% TiO2) has been produced through smelting of Egyptian (Abu-Ghalaga) low-grade ilmenite ore (33-37% TiO2) in a semi-pilot electric arc furnace [12]. X-ray diffraction analysis of this slag shows that it is composed mainly of armalcolite phase (a pseudobrookite phase). Accordingly, the proper upgrading method for this slag to produce synthetic rutile is the
sulphation process to form soluble gangue sulphates. This upgraded slag can be used efficiently as a suitable feedstock for chlorination process. Chlorination of contaminated slag at high temperatures without upgrading resulted in the formation of high boiling point liquid chlorides (CaCl 2 & MgCl 2). These chlorides accumulate as a liquid phase and form together with fine particles a paste, which consequently blocked the reactor system.
In the present work we investigate the sulphation roasting of a low-grade titanium slag. The sulphation extent of the harmful contaminants of the slag (Ca, Mg and Fe) to acid leachable forms is also explored. Various affecting parameters such as sulphation temperature, sulphation time and pellet sizes, on this process are also discussed. The upgraded products were examined physicochemically and mineralogically.
2. Materials and experimental methods
2.1 Materials
About 200 kg of titanium slag sample was obtained by electrothermal smelting of Egyptian ilmenite ore (Abu-Ghalaga, Eastern desert) in a semi-pilot scale three electrodes submerged electric arc furnace (0.4 MVA). The chemical analysis of a representative ground slag sample (-0.074 mm) is given in Table 1. Its microstructure is illustrated in Fig.1. Phase analysis of this sample shows that the slag composes mainly of tubular crystals (very light grey) of armalcolite phase (FeO.MgO.4TiO 2) which is a solid solution of ferrous pseudobrookite and magnesium titanate phases. In addition, rectangular crystals (light grey) of calcium titanates (4CaO.3TiO 2, CaO.TiO 2), dendritic structure (grey) of lower titanium oxides, matrix (dark grey) of calcium silicate (3CaO.SiO 2) and metallic iron (white) also existed, Fig. 2. The sulphating agent is SO 2/air gas mixture.
Table 1 Chemical composition of a representative ground titanium slag sample (-0.074 mm)
Component Wt. pct. TiO 2 (equivalent)*
55.07 Ti 2O 314.83 FeO 10.58 SiO 213.81 CaO 14.61 MgO 2.60 C 2.12 SO 20.32 V 2O 50.30 Others 0.59
* All titanium oxide formulae are calculated as TiO 2 (mainly TiO 2 + Ti 2O 3).
Fig.1 Microstructure of as-tapped titanium slag
Fig.2 XRD pattern of titanium slag
2.2 Sulphation system
Gaseous sulphation experiments were carried out in a home-built system. The schematic representation of this system is shown in Fig. 3. It consists of three main parts; (1) The SO2/air gas mixture generation unit, purification bubblers and flow meter. (2) The sulphation reactor is a silica tube of 2.8 cm internal diameter and 120 cm length that is inserted inside an electrically heated tube furnace with a maximum temperature of 1200 o C. The furnace temperature is measured by a Pt/Pt-10%Rh thermocouple and controlled by a temperature controller. The silica tube is sealed from both ends with rubber stoppers. The reaction gases are introduced from one end and out from the other end. Thermocouple is inserted from a hole in one of the tow stoppers and set at the heating zone of the furnace. (3) A series of absorbent bubblers containing water in which the exited gases are passed in and titrated against 0.1N sodium hydroxide solution to follow the change in SO2 gas concentration and to scrub the excess of it.
Fig.3 Schematic representation of sulphation roasting systém
2.3 Experimental procedure
About 0.5 kg of the ground slag sample (- 0.106 mm) is pelletized to a pellet size of approx. 0.6 cm. Water-molasses solution (10:1) is used as a binder. The pellets are then dried in an oven at 110 o C for 24 hours. The dried pellets are put into an alumina boat and inserted in the
hot zone of the sulphation reaction furnace. In order to sustain a thermal equilibrium of sample, the boat was kept in the furnace for 2 minutes. After that the sulphating gas mixture is introduced at a rate of 0.3 l/min into the furnace for different time periods (0-90 min) and at different temperatures (750-900 o C). At the end of the experiment, the sulphated sample is drawn outside the reactor and allowed to cool down to the room temperature. The cooled sample is weighed, ground and leached out in a three-neck water-fluxed bottle using dilute HCl solution (5 N, 1/10 solid/liquid, 95 o C bath temperature for 1 h) to determine the amount of soluble sulphates of the elements, calcium, magnesium and iron. The leaching conditions are adapted from a previous study work. The extent of removal for each element [X Me] is calculated as follows;
amount of the element present in the leachant liquor (L Me)
[X Me] = ----------------------------------------------------------------------
amount of the element in the original sample (O Me)
In some cases double stage leaching process is applied. In this case iron is leached out prior to sulphation roasting process. Some of calcium and magnesium contents are also dissolved in this stage.
The residue after leaching is then analyzed chemically to determine its grade with respect to TiO2 content. Some selected samples are examined by X-ray diffraction (PW 1370 Philips equipped with a wide range goniometer and iron filter) using Co-Kα radiation to detect the phases formed. Optical micrographs of the microstructure of these samples are taken with the aid of a metallurgical research microscope (Metallux II Leitz).
3. Results and discussion
3.1 Temperature of sulphation
The efficiency of removal of harmful contaminants (Ca, Mg, Fe) in the slag and Ti dissolution after sulphation-leaching process (removal extent [X Me]) is illustrated in Fig.4. It is clear that the conversion of these harmful contaminants to acid leachable forms is gradually increases as the sulphation temperature increases. The removal of 62 to ~ 78% of Ca and ~ 16 to 36% of Mg is achieved as the sulphation temperature increases from 750 to 800o C, respectively. This is followed by a decrease in the sulphation extent of Ca (~60%) and Mg (~15%) as the sulphation temperature increases to 950o C. On contrast to the behavior of calcium and magnesium, the removal extent of Fe decreases from 30 to 24% as the temperature increases from 750 to 950o C. It is worthy mentioning that removal of ~ 64% Fe is achieved by direct leaching without sulphation roasting. Also dissolution of small amount of Ti (~ 5%) is observed under the applied leaching condition in spite of the sulphation roasting condition.
The sulphated samples are investigated physically to compare their compression strengths as a function of sulphation temperature. The obtained results are represented in Fig.5. It is noticed that the compression strength of the sulphated pellets increased from 200 g/pellet to about 570 g/pellet as the sulphation temperature increases from 750 to 850 o C, respectively. At higher sulphation temperature than 850o C the compression strength did not show noticeable change (530 g/pellet) up to 950o C.
XRD patterns of the sulphated slag samples at 800o C and 950o C for 45 min are shown in Fig.6. The main lines in both samples are ascribed to kennedyite (Fe2O3. MgO.3TiO2) and rutile (TiO2) phases. Calcium sulphate (CaSO4) and calcium silicate phases (3CaO.SiO2) are also
detected. Free amorphous silica phase can not be detected by XRD analysis. However, its presence can be confirmed by infrared (IR) spectroscopic analysis. The main characteristic bands of cristoballite phase (SiO 2) are detected indicating the presence of the amorphous silica phase.
Sulphation Temperature,o C R e m o v a l e x t e n t , % %
Fig.4 Removal extent of harmful contaminants and dissolution of titanium with sulphation temperature
Sulphation temperature, o C C o m p r e s s i o n s t r e n g t h , g /p e l l e t Fig.5 Effect of sulphation temperature on compression strength of slag pellets
Fig.6 XRD patterns of sulphated slag samples at (a) 800 o C (b) 950 o C for 45 min
Microstructure of the sulphated slag samples at 800 o C and 950 o C are shown in Figs. 7a and b. It illustrated that the sulphated samples composed mainly of separated discrete grains, which attributed to kennedyite phase (light grey), distributed in a matrix of calcium sulphate (dark grey) and calcium silicate (deep dark grey) phases. Rutile grains are present as fine particles (grey) with round corners. The morphology of these grains indicated that the main features of the original slag structure did not alter upon sulphation. Also, the microstructure image showed that the formed CaSO4 phase (dark grey) adhered the existed rutile phase.
Fig.7 Microstructure of sulphated slag sample at (a) 800 o C (b) 950 o C
Phase analysis of the sulphated-leached slag samples is shown in Fig. 8. It shows the XRD patterns of the sulphated–leached slag samples of 800 and 950 o C sulphation temperature. The main lines in these patterns are ascribed to kennedyite and rutile phases. The other lines with lower intensities belong to calcium silicate phase. Whereas that characterized of CaSO4
phase disappeared.
Figs.9 a and b shows the microstructure of the residual grains of 800 and 950o C sulphation temperature samples after leaching. The figures reveal the presence of the kennedyite phase (light grey), rutile particles (grey) and silicate matrix (dark grey).
Fig.8 XRD patterns of sulphated-leached slag samples at (a) 800 o C (b) 950 o C
Fig.9 Microstructure of sulphated-leached slag samples at (a) 800 o C (b) 950 o C
3.2 Time of sulphation
The results of variation of sulphation time at the optimum sulphation temperature (800o C) are given in Fig.10. It is clear that the removal extent of calcium increases from 42 to 80% as the time of sulphation increases from 15 to 60 min, respectively. It does not show further change as the time of sulphation increased up to 90 min. Magnesium shows similar behavior whereas its sulphation extent increases from about 10 to 38% as the sulphation time increases from 15 to 60 min. Beyond that time (60 min) no significant change is observed up to 90 min time of sulphation. A sharp decrease in iron removal extent from ~ 37 to 20% is observed as the time of sulphation increases from 15 to 75 min. No meaningful decrease in its removal extent is noticed up to 90 min time of sulphation.
The chemical composition of the solid residue of the sulphated slag at 800 o C for 60 min after leaching is given in Table 2.
Table 2 Chemical composition of solid residue after leaching of the sulphated slag sample at 800 o C for 60 min Compound TiO2CaO MgO Fe2O3SiO2Others
Wt. pct 72.88 2.46 1.83 13.59 7.74 1.50
3.3 Effect of pre-leaching
From the above results it is observed that as the slag sample is subjected to the sulphation roasting process, iron is oxidized and become in a slightly acid soluble form (kennedyite phase). So, pre-leaching stage is carried out under the above- mentioned leaching condition to remove the ferrous iron. It is worthy mentioning that about 40% of Ca and 20% of Mg can be removed in this stage. Table 3 gives the chemical composition of the slag residue after sulphation-leaching process.
Table 3 Chemical composition of the residue of pre-leached titanium slag after sulphation-leaching process
Compound TiO 2
CaO MgO Fe 2O 3SiO 2Others Wt. pct 82.72 2.31 1.46 4.92 6.81 1.78
Time of sulphation, min.
R e m o v a l e x t e n t , % Fig.10 Removal extent of harmful contaminants and dissolution of titanium with sulphation time
Discussion
SO2/air mixture is introduced into the slag sample at elevated temperature, the
When
following simple reactions are expected to occur and lead to the dissociation of the slag
structure;
SO2 + 1/2O2 ? CaSO4 (1) CaO
+
MgO + SO2 + 1/2O2 ? MgSO4(2)
FeO + SO2 + 1/2O2? FeSO4 (3)
C + O2? CO2 (4) 2FeO
+
1/2O2 ? Fe2O3 (5) Fe2O3 + 3SO2 + 3/2O2 ? Fe2(SO4)3 (6)
From the results of investigation of the as-tapped slag, it is expected that the
sulphation process would be a complicated process rather a simple one. This is because of that
the main contaminant constituents (Ca, Mg, Fe) of the slag are distributed in different phases.
Some of these phases are stable and hard to break down whereas some others can be broken.
Based on X-ray diffraction analysis, metallographic investigation and thermodynamic
calculations, the following reactions are proposed to explain the sulphation roasting of this
titanium slag;
4CaO.3TiO2 + 3SO2 + 3/2O2 ? CaO.TiO2 + 3CaSO4 + 2TiO2(7)
?G 1100K = -118.57 kJ mol-1
CaO.TiO2 + SO2 + 1/2O2 ? CaSO4 + TiO2(8)
?G 1100K = -109.93 kJ mol-1
3CaO.SiO2 + 3SO2 + 3/2O2 ? 3CaSO4 + SiO2 (9)
?G 1100K = -171.29 kJ mol-1
2(FeO.MgO.4TiO2) + SO2 + O2 ? (Fe2O3.MgO.3TiO2) + MgSO4 + + 5TiO2 (10)
?G 1100K = -61.37 kJ mol-1
Ti2O3 + 1/2O2 ? 2TiO2 (11)
?G 1100K = -134.92 kJmol-1
It is clear from the above reactions (7-11) that all the slag components can be either
sulphated or oxidized during the sulphation roasting process, since their free energies are of
negative values (spontaneous reactions). Reaction (7 & 8) give rutile phase and calcium sulphate
phase at the grain boundaries of calcium titanates. Reaction (9) gives free silica and calcium
sulphate phase at the grain boundary of calcium silicate. The free silica is hard to attack by an
acid leaching process and it accumulates in the residue after leaching. Oxidation of armalcolite
phase (FeO.MgO.4TiO2) in reaction (10) to kennedyite phase (Fe2O3.MgO.3TiO2), which is hard
to leach, causes that Fe content in the slag is either increased or unchanged after leaching. Also,
oxidation of lower titanium oxides (reaction 11) is also supported by their disappearance after
the sulphation roasting process as confirmed by XRD analysis and microscopic investigation.
Hardeni N g of the pellets at higher sulphation temperatures and/or longer sulphation time might be due to semi-melting of these pellets and/or increase of the molar volumes of the products by approximately twice that of the reactants. Therefore, the size of the pores inside the pellets decreases. As a result, the diffusion of the reactant gases is retarded, the sulphation extent and consequently the removal extent decreases. These two reasons may cause pore closure inside the pellets, decrease its porosity, and indeed retard the diffusion of the sulphating gas mixture into the sample core. This effect can be occurred both at higher sulphation temperature (> 800o C) and at longer sulphation time (> 60 min). The proper pellet size used in this work is ~ 6 mm. Larger pellet size > 6 mm leads to lower sulphation extent. This is because the surface layer of the pellet becomes compact (non-porous) upon sulphation and indeed retards the diffusion of the sulphating gas mixture into the pellet core.
4. Conclusion
Low-grade titanium slag (~55% TiO2) which has a pseudobrookite structure (armalcolite phase) can be upgraded (~83% TiO2) efficiently by sulphation roasting and leaching processes. The optimum sulphation temperature for removal of the harmful contaminants (Ca, Mg and Fe) by subsequent leaching is 800 o C for 60 min. Above this temperature the slag pellets become hard and its porosity decrease. Accordingly, the diffusion of the sulphating gas mixture is retarded and the sulphation extent and consequently the removal extent decreases. Pre-leaching of iron prior to sulphation roasting process is carried out to enhance the break down of the armalcolite structure and minimize the possibility of kennedyite phase formation. The dissociation of the slag is accompanied with the liberation of SiO2 which contaminate the product. As a result, the percentage of TiO2 in the leached product reaching a limiting value governed by the SiO2 content in the slag. This silica can be removed by a subsequent preferential chlorination step. These results can be explained based on thermodynamic calculations.
Acknowledgements
The author would like to thank Prof. S. Z. El-Tawil and Prof. I. M. Morsi for helpful discussion.
Literature
[1]Ogasawara T., Veloso de Ara?jo R. V.: Hydrometallurgy, 56, 203, 2000
[2]Mackey T. S.: JOM, 4, 59, 1994
[3]Fouad O. A.: “Smelting of Egyptian ilmenite ore in electric arc furnace”, M. Sc. thesis,
Cairo University, 1995, Cairo, Egypt
[4]Toromanoff I., Habashi F.: Inter. J. Miner. Process., 15, 65, 1985
[5]Elger G. W., Stickney W. A..: Bur. Mines TPR 37, 1971
[6]Elger G. W., Kirby D. E.: US. Patent 3, 996, 332, 1976
[7]Laurance L. O., Sumner D. H., Hower J. Jr.: BuMines R. I. 7742, 1973
[8]Jarish B.: U. S. patent 4,038,363, 1977
[9]Lee C. T., Sohn H. Y.: Ind. Eng. Chem. Res., 28, 1802, 1989
[10]Chen Y., Marsh M., Williams J. S., Ninham B.: J. Alloys and Compounds, 245, 54, 1996
[11]Khairy E. M., Hussein M. K., El-Barawy K. A..: Proc. Symp. “Recent Development in
Non-ferrous Metals Technology”, 1968, Vol. III, 132, Jamsherdpur, India
[12]Fouad O. A., Morsi I. M., El-Barawy K. A., El-Tawil S. Z.: Proc. The Fifth
International Conference on Petroleum, Mining & Metallurgical Engineering, Feb., 1997, 378, Suez Canal University, Suez, Egypt.
从实践的角度探讨在日语教学中多媒体课件的应用 在今天中国的许多大学，为适应现代化，信息化的要求，建立了设备完善的适应多媒体教学的教室。许多学科的研究者及现场教员也积极致力于多媒体软件的开发和利用。在大学日语专业的教学工作中，教科书、磁带、粉笔为主流的传统教学方式差不多悄然向先进的教学手段而进展。 一、多媒体课件和精品课程的进展现状 然而，目前在专业日语教学中能够利用的教学软件并不多见。比如在中国大学日语的专业、第二外語用教科书常见的有《新编日语》（上海外语教育出版社）、《中日交流标准日本語》（初级、中级）（人民教育出版社）、《新编基础日语（初級、高級）》（上海译文出版社）、《大学日本语》（四川大学出版社）、《初级日语》《中级日语》（北京大学出版社）、《新世纪大学日语》（外语教学与研究出版社）、《综合日语》（北京大学出版社）、《新编日语教程》（华东理工大学出版社）《新编初级（中级）日本语》（吉林教育出版社）、《新大学日本语》（大连理工大学出版社）、《新大学日语》（高等教育出版社）、《现代日本语》（上海外语教育出版社）、《基础日语》（复旦大学出版社）等等。配套教材以录音磁带、教学参考、习题集为主。只有《中日交流標準日本語（初級上）》、《初級日语》、《新编日语教程》等少数教科书配备了多媒体DVD视听教材。 然而这些试听教材，有的内容为日语普及读物，并不适合专业外语课堂教学。比如《新版中日交流标准日本语（初级上）》，有的尽管DVD视听教材中有丰富的动画画面和语音练习。然而，课堂操作则花费时刻长，不利于教师重点指导，更加适合学生的课余练习。比如北京大学的《初级日语》等。在这种情形下，许多大学的日语专业致力于教材的自主开发。 其中，有些大学的还推出精品课程，取得了专门大成绩。比如天津外国语学院的《新编日语》多媒体精品课程为2007年被评为“国家级精品课”。目前已被南开大学外国语学院、成都理工大学日语系等全国40余所大学推广使用。
功率继电器结业报告 一、继电器的定义 继电器是一种电控制器件，当输入量的变化达到要求时，电气输出电路通断、开闭的一种电器。通常应用于自动化的控制电路中，它实际上是用小电流去控制大电流运作的一种“自动开关”。故在电路中起着自动调节、安全保护、转换电路等作用。如图1 二、继电器的构造和动作原理 无极机械继电器 a.无极继电器主要包括：线圈端子、电磁石、外壳、线圈、铁芯、衔铁、可动触点、固定端子、可动簧片、触点端子等。 b.无极继电器动作原理
继电器从①状态OFF状态，线圈通电，当电压上升到吸合电压时产生电磁感应，铁芯吸引衔铁达到②状态（NO）状态。，达到额定电压时，达到③状态，从而从开状态达到闭合状态。反过来说，当线圈电压减小时，触点从闭合慢慢断开。 有极继电器 a.有极继电器构造：如下图，主要有个永久磁铁，可以同过一定的脉冲电流后，继电器能够保磁， b.有极继电器动作原理
三、继电器作用 继电器是具有隔离功能的自动开关元件，广泛应用于遥控、遥测、通讯、自动控制、机电一体化及电力电子设备中，是最重要的控制元件之一。 继电器一般都有能反映一定输入变量（如电流、电压、功率、阻抗、频率、温度、压力、速度、光等）的感应机构（输入部分）；有能对被控电路实现“通”、“断”控制的执行机构（输出部分）；在继电器的输入部分和输出部分之间，还有对输入量进行耦合隔离，功能处理和对输出部分进行驱动的中间机构（驱动部分）。 作为控制元件，概括起来，继电器有如下几种作用： 1）扩大控制范围：例如，多触点继电器控制信号达到某一定值时，可以按触点组的不同形式，同时换接、开断、接通多路电路。 2）放大：例如，灵敏型继电器、中间继电器等，用一个很微小的控制量，可以控制很大功率的电路。 3）综合信号：例如，当多个控制信号按规定的形式输入多绕组继电器时，经过比较综合，达到预定的控制效果。 4）自动、遥控、监测：例如，自动装置上的继电器与其他电器一起，可以组成程序控制线路，从而实现自动化运行 四、继电器的分类 1.按动作机能可分为 机械式继电器（有触点）、半导体继电器（无触点）。 a.机械式继电器是利用电磁原理，利用电磁效应来控制触点的开闭，又分为单稳态、单线圈磁保持型继电器、双线圈磁保持型。单稳态是通过继电器线圈励磁变为ON，通过无励磁变为OFF。单线圈磁保持继电器通过在一个线圈中施加正负两极型信号，进行动作（置位）和复位。双线圈磁保持型继电器通过交互施加同一极性的脉冲进行动作复位。 b.半导体继电器是输出部分为半导体，不进行机械性的触点开闭，没有触点。分为
五年级上册成语解释及近义词反义词和造句大全 囫囵吞枣；【解释】：囫囵：整个儿。把枣整个咽下去，不加咀嚼，不辨味道。比喻对事物不加分析考虑。【近义词】：不求甚解【反义词】融会贯穿[造句];学习不能囫囵吞枣而是要精益求精 不求甚解；bùqiúshènjiě【解释】：甚：专门，极。只求明白个大概，不求完全了解。常指学习或研究不认真、不深入【近义词】：囫囵吞枣【反义词】：精益求精 造句；1；在学习上，我们要理解透彻，不能不求甚解 2；学习科学文化知识要刻苦钻研，深入领会，不能粗枝大叶，不求甚解。 千篇一律；【解释】：一千篇文章都一个样。指文章公式化。也比喻办事按一个格式，专门机械。 【近义词】：千人一面、如出一辙【反义词】：千差万别、形形色色 造句；学生旳作文千篇一律，专门少能有篇与众不同旳，这确实是平常旳练习太少了。 倾盆大雨；qīngpéndàyǔ【解释】：雨大得象盆里旳水直往下倒。形容雨大势急。 【近义词】：大雨如柱、大雨滂沱【反义词】：细雨霏霏牛毛细雨 造句；3月旳天说变就变，瞬间下了一场倾盆大雨。今天下了一场倾盆大雨。 坚决果断；áobùyóuyù：意思；做事果断，专门快拿定了主意，一点都不迟疑，形容态度坚决 近义词；不假思索斩钉截铁反义词；犹豫不决 造句；1看到小朋友落水，司马光坚决果断地搬起石头砸缸。2我坚决果断旳承诺了她旳要求。 饥肠辘辘jīchánglùlù【近义词】：饥不择食【反义词】：丰衣足食 造句；1我放学回家已是饥肠辘辘。2那个饥肠辘辘旳小孩差不多两天没吃饭了 滚瓜烂熟gǔnguālànshóu〔shú)【解释】：象从瓜蔓上掉下来旳瓜那样熟。形容读书或背书流利纯熟。【近义词】：倒背如流【反义词】：半生半熟造句；1、这篇课文我们早已背得滚瓜烂熟了 流光溢彩【liúguāngyìcǎi】解释；光影，满溢旳色彩，形容色彩明媚 造句：国庆节，商场里装饰旳流光溢彩。 津津有味；jīnjīnyǒuwèi解释：兴趣浓厚旳模样。指吃得专门有味道或谈得专门有兴趣。 【近义词】：兴致勃勃有滋有味【反义词】：索然无味、枯燥无味 造句；1今天旳晚餐真丰富，小明吃得津津有味。 天长日久；tiānchángrìjiǔ【解释】：时刻长，生活久。【近义词】：天长地久【反义词】：稍纵即逝 造句：小缺点假如不立即改掉, 天长日久就会变成坏适应 如醉如痴rúzuìrúchī【解释】：形容神态失常，失去自制。【近义词】：如梦如醉【反义词】：恍然大悟造句；这么美妙旳音乐，我听得如醉如痴。 浮想联翩【fúxiǎngliánpiān解释】：浮想：飘浮不定旳想象；联翩：鸟飞旳模样，比喻连续不断。指许许多多旳想象不断涌现出来。【近义词】：思绪万千 造句；1他旳话让人浮想联翩。2:这幅画饱含诗情，使人浮想联翩，神游画外，得到美旳享受。 悲欢离合bēihuānlíhé解释；欢乐、离散、聚会。泛指生活中经历旳各种境遇和由此产生旳各种心情【近义词】：酸甜苦辣、喜怒哀乐【反义词】：平淡无奇 造句；1人一辈子即是悲欢离合,总要笑口常开,我们旳生活才阳光明媚. 牵肠挂肚qiānchángguàdù【解释】：牵：拉。形容十分惦念，放心不下 造句；儿行千里母担忧，母亲总是那个为你牵肠挂肚旳人 如饥似渴rújīsìkě：形容要求专门迫切，仿佛饿了急着要吃饭，渴了急着要喝水一样。 造句；我如饥似渴地一口气读完这篇文章。他对知识旳如饥似渴旳态度造就了他今天旳成功。 不言而喻bùyánéryù【解释】：喻：了解，明白。不用说话就能明白。形容道理专门明显。 【近义词】：显而易见【反义词】：扑朔迷离造句；1珍惜时刻，好好学习，那个道理是不言而喻旳 与众不同；yǔzhòngbùtóng【解释】：跟大伙不一样。 〖近义词〗别出心裁〖反义词〗平淡无奇。造句； 1从他与众不同旳解题思路中，看出他专门聪慧。2他是个与众不同旳小孩
安然无恙：很平安，没有受到损失和伤害 - 造句：那次智利大地震，许多城市都毁灭了，但我叔父全家安然无恙，非常幸运。 - 拔苗助长：比喻违反事物的发展规律，急于求成，反而坏事 - 造句：“抢先教育”违背了儿童成长的客观规律，这种拔苗助长的办法结果必将造成对孩子身体和心灵的双重伤害。 - 跋山涉水：形容旅途的艰辛劳苦 - 造句：地质勘探队员不怕艰苦，跋山涉水，为祖国寻找地下的报藏。 - 百看不厌：对喜欢的人，事物等看多少遍都不厌倦。比喻非常喜欢。 -造句：到了节日里，各个景区摆设的花朵真是让人百看不厌。 - 班门弄斧：比喻在行家面前卖弄本领，不自量力 -造句：你在著名华文作家的面前卖弄华文,岂不是班门弄斧。
- 搬弄是非：把别人的话传来传去，有意挑拔，或在背后乱加议论，引起纠纷 - 造句：他们到处搬弄是非,传播流言、破坏组织内部的和谐。 - 变本加厉：指比原来更加发展。现指情况变得比本来更加严重 -造句;的坏习惯不但没有改正，反而变本加厉了. -变幻莫测：变化不可测度。变化很多，不能预料 -造句：草地的气候变幻莫测,一会儿烈日当空,一会儿大雨倾盆,忽而雨雪交加,忽而狂风怒吼。 - 别具匠心：指在技巧和艺术方面具有与众不同的巧妙构思- 造句：这篇小说让人看了回味无穷，作者确实是别巨匠心。 -不耻下问：指向地位比自己低、学识比自己少的人请教，也不感到羞耻（耻辱） -造句：学习，不仅要做到虚怀若谷，还要做到不耻下问。 -不可救药：比喻人或事物坏到无法挽救的地步 - 造句：他的问题很严重，已经不可救药。
- 不可思议：原有神秘奥妙的意思。现多指无法想象，难以理解 - 造句：我看这那座小山觉得不可思议。 -不期而遇：没有约定而遇见 -造句：高兴与悲伤总是不期而遇，或许这就是上帝再捉弄世俗吧！ -不屈不挠：形容顽强斗争,在敌人或困难面前不屈服,不低头那种不屈不挠的、要征服一切的心情 -造句：战士们不屈不挠的坚守在抗震第一线。 - 不速之客：指没有邀请而自己来的客人 - 造句：也不必说有时趁你不防钻进防盗铁门登堂入室的不速之客。 - 不屑置辩：认为不值得辩论 - 造句：孔乙己对那些嘲笑他的人显出不屑置辩的神情。 -不言而喻：形容道理很明显 -造句：你想他们这朋友之乐，尽可不言而喻了。
继电器的定义、分类、命名 一、继电器的定义 1、继电器的定义 继电器:当输入量(或激励量)满足某些规定的条件是能在一个或多个电器输出电路中产生跃变的一种器件 2、继电器的继电特性 继电器输出入量和输出量之间在整个变化过程中的相互关系成为继电器的继电特征或控制特征.用x表示输入回路量,y表示输出回路的输出量,如图1所示.当输出量x 连续变化到一定量xa时,输出量y发生跃变,有0增加到ya值,则是输入量继续增加,是输出保持不变.相反,当减少到xb是,y又突然由ya减少到0.xa被称为继电器的动作值,xb被称为继电器的释放值,ya即是继电器的负载. 二、继电器的分类 1、按继电器的工作原理或结构特征分类 （1）电磁继电器：利用输入电路内点路在电磁铁铁芯与衔铁间产生的吸力作用而工作的一种电气继电器。 直流电磁继电器：输入电路中的控制电流为直流的电磁继电器。 交流电磁继电器：输入电路中的控制电流为交流的电磁继电器。 磁保持继电器：利用永久磁铁或具有很高剩磁特性的铁芯，是电磁继电器的衔铁在其线圈断点后仍能保持在线圈通电时的位置上的继电器。 （2）固体继电器：指电子元件履行其功能而无机械运动构件的，输入和输出隔离的一种继电器。 （3）温度继电器：当外界温度达到给定值时而动作的继电器。 （4）舌簧继电器：利用密封在管内，具有触电簧片和衔铁磁路双重作用的舌簧的动作来开,闭或转换线路的继电器。 干簧继电器：舌簧管内的介质的介质为真空，空气或某种惰性气体，即具有干式触点的舌簧继电器。 湿簧继电器：舌簧片和触电均密封在管内，并通过管底水银槽中水银的毛细作用，而使水银膜湿润触点的舌簧继电器。 剩簧继电器：由剩簧管或有干簧关于一个或多个剩磁零件组成的自保持干簧继电器。 舌簧管：同理舌簧管有干簧管,湿簧管,剩簧管三种类型。 （5）时间继电器：当加上或除去输入信号时，输出部分需延时或限时到规定的时间才闭合或断开其被
悲惨的近义词反义词和造句 导读：悲惨的近义词 悲凉(注释:悲哀凄凉：～激越的琴声。) 悲惨的反义词 幸福(注释:个人由于理想的实现或接近而引起的一种内心满足。追求幸福是人们的普遍愿望，但剥削阶级把个人幸福看得高于一切，并把个人幸福建立在被剥削阶级的痛苦之上。无产阶级则把争取广大人民的幸福和实现全人类的解放看作最大的幸福。认为幸福不仅包括物质生活，也包括精神生活;个人幸福依赖集体幸福，集体幸福高于个人幸福;幸福不仅在于享受，而主要在于劳动和创造。) 悲惨造句 1.一个人要发现卓有成效的真理，需要千百个人在失败的探索和悲惨的错误中毁掉自己的生命。 2.贝多芬的童年尽管如是悲惨，他对这个时代和消磨这时代的地方，永远保持着一种温柔而凄凉的回忆。 3.卖火柴的小女孩在大年夜里冻死了，那情景十分悲惨。 4.他相信，他们每个人背后都有一个悲惨的故事。 5.在那次悲惨的经历之后，我深信自己绝对不是那种可以离家很远的人。 6.在人生的海洋上，最痛快的事是独断独航，但最悲惨的却是回头无岸。 7.人生是艰苦的。对不甘于平庸凡俗的人那是一场无日无夜的斗
争，往往是悲惨的、没有光华的、没有幸福的，在孤独与静寂中展开的斗争。……他们只能依靠自己，可是有时连最强的人都不免于在苦难中蹉跎。罗曼·罗兰 8.伟大的心胸，应该表现出这样的气概用笑脸来迎接悲惨的厄运，用百倍的勇气来应付开始的不幸。鲁迅人在逆境里比在在顺境里更能坚强不屈。遇厄运时比交好运时容易保全身心。 9.要抓紧时间赶快生活，因为一场莫名其妙的疾病，或者一个意外的悲惨事件，都会使生命中断。奥斯特洛夫斯基。 10.在我一生中最悲惨的一个时期，我曾经有过那类的想法：去年夏天在我回到这儿附近的地方时，这想法还缠着我;可是只有她自己的亲自说明才能使我再接受这可怕的想法。 11.他们说一个悲惨的故事是悲剧，但一千个这样的故事就只是一个统计了。 12.不要向诱惑屈服，而浪费时间去阅读别人悲惨的详细新闻。 13.那起悲惨的事件深深地铭刻在我的记忆中。 14.伟大的心胸，应该用笑脸来迎接悲惨的厄运，用百倍的勇气来应付一切的不幸。 15.一个人要发现卓有成效的真理，需要千百万个人在失败的探索和悲惨的错误中毁掉自己的生命。门捷列夫 16.生活需要爱，没有爱，那些受灾的人们生活将永远悲惨;生活需要爱，爱就像调味料，使生活这道菜充满滋味;生活需要爱，爱让生活永远充满光明。
常用成语造句大全及解释 导读：常用成语及造句大全： 【马到功成】形容事情顺利，一开始就取得胜利。 朋友要去参加考试我发自内心的祝她马到功成。 【安常守故】习惯于日常的平稳糊口，保保守的一套。指保守不知厘革。 他持久以来安常守故，缺乏锻炼，故而经不起挫折。 【挨门逐户】挨家挨户，一家也没有遗漏。 倾销员挨门逐户地倾销产物，可是并没有多少人愿意买 【破釜沉舟】比喻下决心悍然不顾地干到底。 只要咱们有破釜沉舟的决心，就能克服进修上的各类困难。 【大千世界】三昧，世界的千倍叫小千世界，小千世界的千倍叫中千世界，中千世界的千倍叫大千世界。后指广大无边的人世。 大千世界无奇不有，充满了抵牾。 【空手发迹】一切靠自己艰辛奋斗，创立了一番事业。 王董事长空手发迹，如今是王氏集团的总裁。 【卷土重来】卷土：人马奔跑时卷起的尘土。形容失败后组织力量，重图恢复。 这次角逐虽则表现不佳，但我决定明天卷土重来。 【晨钟暮鼓】古代梵宇中晨敲钟，暮伐鼓以报时，用以使人惊悟的言论。 每当我想坏事时，就会想起母亲对我的晨钟暮鼓的叮咛。
【力争上游】起劲争取长进求学做人都要力争上游，不要自满於近况 【投笔从戎】一小我私家抛弃文职而插手卫国的行列。 大伯父高中结业后投笔从戎，步入军校就读，负起保家卫国的责任。 【前车之鉴】比喻前人的失败，可以作为后人的借鉴。 有了这个前车之鉴，我下次出门一定会带雨具。 【金石为开】至诚可感动任何事物。 表哥相信精诚所至，金石为开，他的成意一定可以感动王小姐的。 【勤能补拙】指勤勉起劲能弥补天资上的不足。 勤能补拙，只要你多付出心思，一定有乐成的机会。 【揠苗助长】揠：拔起。把苗拔起，以助其生长。后用来比喻违反事物的发展规律，操之过急，反倒坏事。 对学生的教育既不能揠苗助长，也能任其自然。 【闻鸡起舞】听见鸡鸣就起身，比喻人发奋勇前进修，励精图治。 老爷爷在乡间修养，天天闻鸡起舞，打太极健身。 【哀鸿遍野】哀鸿：哀鸣的鸿雁。比喻饥寒交迫的灾民。比喻在天灾人祸中到处都是流离失所、呻吟呼号的饥民。 旧社会，每逢水灾战乱，人民就被迫四处逃亡，～，一片凄凉。 【联袂登台】同台演出 今晚的演出听说会有两位名角联袂登台献艺。 【使人咋舌】令人惊讶
新大学日语简明教程课文翻译 第21课 一、我的留学生活 我从去年12月开始学习日语。已经3个月了。每天大约学30个新单词。每天学15个左右的新汉字，但总记不住。假名已经基本记住了。 简单的会话还可以，但较难的还说不了。还不能用日语发表自己的意见。既不能很好地回答老师的提问，也看不懂日语的文章。短小、简单的信写得了，但长的信写不了。 来日本不久就迎来了新年。新年时，日本的少女们穿着美丽的和服，看上去就像新娘。非常冷的时候，还是有女孩子穿着裙子和袜子走在大街上。 我在日本的第一个新年过得很愉快，因此很开心。 现在学习忙，没什么时间玩，但周末常常运动，或骑车去公园玩。有时也邀朋友一起去。虽然我有国际驾照，但没钱，买不起车。没办法，需要的时候就向朋友借车。有几个朋友愿意借车给我。 二、一个房间变成三个 从前一直认为睡在褥子上的是日本人，美国人都睡床铺，可是听说近来纽约等大都市的年轻人不睡床铺，而是睡在褥子上，是不是突然讨厌起床铺了？ 日本人自古以来就睡在褥子上，那自有它的原因。人们都说日本人的房子小，从前，很少有人在自己的房间，一家人住在一个小房间里是常有的是，今天仍然有人过着这样的生活。 在仅有的一个房间哩，如果要摆下全家人的床铺，就不能在那里吃饭了。这一点，褥子很方便。早晨，不需要褥子的时候，可以收起来。在没有了褥子的房间放上桌子，当作饭厅吃早饭。来客人的话，就在那里喝茶；孩子放学回到家里，那房间就成了书房。而后，傍晚又成为饭厅。然后收起桌子，铺上褥子，又成为了全家人睡觉的地方。 如果是床铺的话，除了睡觉的房间，还需要吃饭的房间和书房等，但如果使用褥子，一个房间就可以有各种用途。 据说从前，在纽约等大都市的大学学习的学生也租得起很大的房间。但现在房租太贵，租不起了。只能住更便宜、更小的房间。因此，似乎开始使用睡觉时作床，白天折小能成为椅子的、方便的褥子。
初二上语文期末复习之成语运用专项训练 1.恍如隔世：恍惚如同相隔了一辈子。喻事物变化发展很快，变化很大。 例句：他曾因躲避战乱而隐居深山，和平后下山才发觉人间变化巨大，真是感觉恍如隔世。 2.轻描淡写：原意是绘画时用浅淡颜色轻轻描绘。形容说话或作文章时对重要的地方淡淡带过。也比喻做事不费力。 例句：医生未说实话，看他可怜，就用轻描淡写的话安慰他。 如此严重的问题，轻描淡写地说了说就算完了？ 3.与狼共舞：跟恶狼一起跳舞，比喻跟所谋求的对象有利害冲突,决不能成功。后多指跟恶人商量,要他牺牲自己的利 益,一定办不到。也说比喻与恶人在一起，随时都有危险，须特别谨慎。 例句：没有比与狼共舞更危险的事情。江山易改，本性难移。狼就是狼，无论外表装饰得如何漂亮，不管如何能言善辩，狼就是狼，早晚会露出凶残、狡猾的真面目。 4.林林总总：林林:树木聚集成片的样子;总总:全部汇集状。形容人或事物繁多。 例句：在林林总总的这类故事中，也有一个是说鲁班学习海龙王宫殿的建筑艺术。 5.不速之客：速:邀请。没有邀请而自己来的客人。指意想不到的客人。 例句：我们正在聚餐时来了一位不速之客。 多年不见的老朋友，突然出现在我的眼前，真是不速之客。 大会主席团作出决定，会议期间不准无故迟到，对那些不遵守大会纪律的不速之客要通报批评。（不是突然来到的人。语意不符） 6.责无旁贷：自己的责任，不能推卸给别人；贷，推卸。 例句：杨丽萍在接受媒体采访时说，保护洱海，她责无旁贷，同时她欢迎广大媒体、网友监督。 作为课题负责人，他责无旁贷地走向主席台。（用“当仁不让”更合适，语意不符） 7.如火如荼：像火那样红，像荼（茅草的白花）那样白。原比喻军容之盛，现用来形容旺盛、热烈或激烈。 例句：过了两年“五四运动”发生了。报纸上的如火如荼的记载唤醒了他的被忘却了的青春。 8.鳞次栉比：形容房屋密集，像鱼鳞和梳子的齿一样，一个挨着一个地排列着。 例句：鳞次栉比的摩天大楼在霍尔河畔奇迹般地崛起，让人以为自己仿佛到了纽约。 包头是一个倚山濒水的城市，向北是峰峦鳞次栉比的阴山，向南是波涛汹涌、曲折回环的黄河。（多用来形容房屋或船只等排列得很密很整齐。不能用来形容“山”。） 9.珠光宝气：闪耀着珍宝的光色。多形容妇女服饰华贵富丽。 例句：温德姆大堂的香氛过于浓烈，像一个珠光宝气、香水味四溢的贵妇人如影随行。 10.退避三舍：比喻对人让步，不与相争。 例句：可见二位仁兄的学问，不但本校众人所不能及，即使天下文才，也当退避三舍哩! 这个地头蛇，人见人怕，连警察见了他都要退避三舍。（“退避三舍”比喻对人让步，不与之相争；不是形容害怕、恐怖。） 11.司空见惯：看惯了的事情，并不觉得奇怪。 例句：这种种行为，在我们初来的东方人看来，多少存着好奇心和注意的态度，但在他们已司空见惯了。 我们都司空见惯了那种“违者罚款”的告示牌。（“司空见惯”的意思是形容经常看到不足为奇的事物。后面不能带宾语。） 12.月白风清：形容月夜的明朗幽静。 例句：这是一个月白风清的良宵，校园散步的人三三两两从我身边走过。 13.脍炙人口：本指美味人人都爱吃，现比喻好的诗文或事物人人都称赞。 例句：我国古典诗歌内蕴丰富，很能激发人们的联想和想象。“日出江花红胜火，春来江水绿如蓝”，吟咏这脍炙人口的诗句，谁不为春回大地后祖国母亲多姿多彩的面貌而自豪。 历史是一面脍炙人口的镜子，面对它，我会正衣冠，知兴替，明得失。（指美味人人爱吃。比喻好的诗文受到人们和称赞和传讼。不能修饰“镜子”） 14.鲁殿灵光：汉代鲁恭王建有灵光殿，屡经战乱而岿然独存。后用来称硕果仅存的人或事物。
继电器的主要分类？ 内容来源网络，由“深圳机械展（11万㎡，1100多家展商，超10万观众）”收集整理！ 更多cnc加工中心、车铣磨钻床、线切割、数控刀具工具、工业机器人、非标自动化、数字化无人工厂、精密测量、3D打印、激光切割、钣金冲压折弯、精密零件加工等展示，就在深圳机械展. 1．按继电器的工作原理或结构特征分类 1）电磁继电器：利用输入电路内电路在电磁铁铁芯与衔铁间产生的吸力作用而工作的一种电气继电器。 2）固体继电器：指电子元件履行其功能而无机械运动构件的，输入和输出隔离的一种继电器。 3）温度继电器：当外界温度达到给定值时而动作的继电器。 4）舌簧继电器：利用密封在管内，具有触电簧片和衔铁磁路双重作用的舌簧动作来开，闭或转换线路的继电器 5）时间继电器：当加上或除去输入信号时，输出部分需延时或限时到规定时间才闭合或断开其被控线路继电器。 6）高频继电器：用于切换高频，射频线路而具有最小损耗的继电器。 7）极化继电器：有极化磁场与控制电流通过控制线圈所产生的磁场综合作用而动作的继电器。继电器的动作方向取决于控制线圈中流过的的电流方向。 8）其他类型的继电器：如光继电器，声继电器，热继电器，仪表式继电器，霍尔效应继电器，差动继电器等。 2、按继电器的外形尺寸分类 1）微型继电器 2）超小型微型继电器 3）小型微型继电器 注：对于密封或封闭式继电器，外形尺寸为继电器本体三个相互垂直方向的最大尺寸，不包括安装件，引出端，压筋，压边，翻边和密封焊点的尺寸。 3、按继电器的负载分类
1）微功率继电器 2）弱功率继电器 3）中功率继电器 4）大功率继电器 4、按继电器的防护特征分类 1）密封继电器 2）封闭式继电器 3）敞开式继电器 5、按继电器按照动作原理可分类 1）电磁型 2）感应型 3）整流型 4）电子型 5）数字型等 6、按照反应的物理量可分类 1）电流继电器 2）电压继电器 3）功率方向继电器 4）阻抗继电器 5）频率继电器 6）气体（瓦斯）继电器 7、按照继电器在保护回路中所起的作用可分类1）启动继电器 2）量度继电器 3）时间继电器 4）中间继电器 5）信号继电器 6）出口继电器
习惯与礼仪 我是个漫画家，对旁人细微的动作、不起眼的举止等抱有好奇。所以，我在国外只要做错一点什么，立刻会比旁人更为敏锐地感觉到那个国家的人们对此作出的反应。 譬如我多次看到过，欧美人和中国人见到我们日本人吸溜吸溜地出声喝汤而面露厌恶之色。过去，日本人坐在塌塌米上，在一张低矮的食案上用餐，餐具离嘴较远。所以，养成了把碗端至嘴边吸食的习惯。喝羹匙里的东西也象吸似的，声声作响。这并非哪一方文化高或低，只是各国的习惯、礼仪不同而已。 日本人坐在椅子上围桌用餐是1960年之后的事情。当时，还没有礼仪规矩，甚至有人盘着腿吃饭。外国人看见此景大概会一脸厌恶吧。 韩国女性就座时，单腿翘起。我认为这种姿势很美，但习惯于双膝跪坐的日本女性大概不以为然，而韩国女性恐怕也不认为跪坐为好。 日本等多数亚洲国家，常有人习惯在路上蹲着。欧美人会联想起狗排便的姿势而一脸厌恶。 日本人常常把手放在小孩的头上说“好可爱啊！”，而大部分外国人会不愿意。 如果向回教国家的人们劝食猪肉和酒，或用左手握手、递东西，会不受欢迎的。当然，饭菜也用右手抓着吃。只有从公用大盘往自己的小盘里分食用的公勺是用左手拿。一旦搞错，用黏糊糊的右手去拿，
会遭人厌恶。 在欧美，对不受欢迎的客人不说“请脱下外套”，所以电视剧中的侦探哥隆波总是穿着外套。访问日本家庭时，要在门厅外脱掉外套后进屋。穿到屋里会不受欢迎的。 这些习惯只要了解就不会出问题，如果因为不知道而遭厌恶、憎恨，实在心里难受。 过去，我曾用色彩图画和简短的文字画了一本《关键时刻的礼仪》（新潮文库）。如今越发希望用各国语言翻译这本书。以便能对在日本的外国人有所帮助。同时希望有朝一日以漫画的形式画一本“世界各国的习惯与礼仪”。 练习答案 ５、 （１）止める並んでいる見ているなる着色した （２）拾った入っていた行ったしまった始まっていた
群芳吐艳：各种花草树木竞相开放出艳丽的花朵。比喻各种不同形式和风格的艺 术自由发展。也形容艺术界的繁荣景象。 什么花儿都争着开放.形容春意盎然的样子 造句—花展上的鲜花竞相开放，真是群芳吐艳，美不胜收啊！ 春天悄然而至，走到花园里，各种花群芳吐艳。 姹紫嫣红：姹：美丽。嫣：美好。形容各种花娇艳美丽 春天来了，处处姹紫嫣红，花儿们争先恐后的开放着。 满园的鲜花，争相怒放，一片姹紫嫣红、生机勃勃的景象，令人流连忘返。 郁郁葱葱的草丛中，一些姹紫嫣红的花朵煞是好看，大有百花争艳的气势。 落英缤纷：落英：落花。缤纷：繁多凌乱的样子。形容落花纷纷飘落的美丽情景。 这里山清水秀，落英缤纷，景色迷人。 傍晚的梅花林，斜阳西坠，落英缤纷，实在太美了。 鲜花盛开，花瓣纷纷飘落。形容春天的美好景色。也指花儿凋谢的暮春天气。 郁郁葱葱：形容草木苍翠茂盛的样子。也形容气势美好蓬勃。 山道两旁到处郁郁葱葱，风景美不胜收。 细雨滋润过后的草地绿意盎然郁郁葱葱。 那片树木葱葱郁郁的，十分茂盛。 夏日的池塘里,郁郁葱葱的荷叶映衬着亭亭玉立的荷花,真是一幅美丽的画卷啊! 那片树木葱葱郁郁的，十分茂盛。 喷薄欲出：喷薄：有力地向上涌的样子。形容水涌起或太阳初升时涌上地平线 的景象。 鸟儿唱着欢乐的歌，迎接着喷薄欲出的朝阳。 .我们来到了层峦叠翠郁郁葱葱的山腰.喷薄欲出的红日照耀着苍翠欲滴的古松。 旭日东升：旭日:早上刚出来的太阳．早上太阳从东方升起．形容朝气蓬勃的 气象． 在这个旭日东升晴朗的早晨，让我们一起来热情的做早操吧！ 中国正如旭日东升般，充满活力。 她们黑暗中挣扎和最后看到了旭日东升，破涕为笑，对未来充满希望。
继电器是什么? 继电器是一种电子控制器件，它具有控制系统(又称输入回路)和被控制系统(又称输出回路)。它实际上是用较小的电流去控制较大电流的一种“自动开关”。 继电器的分类： 1、按工作原理和结构特性可分为：电磁继电器、固体继电器、温度继电器、舌簧继电器、时间继电器、高频继电器、极化继电器、其他类型的继电器（有继电器，声继电器，热继电器，仪表式继电器，霍尔效应继电器，差动继电器等） 2、按动作原理可分为：电磁型、感应型、整流型、电子型、数字型等 3、按继电器的作用可分为：启动继电器、量度继电器、时间继电器、中间继电器、信号继电器、出口继电器 一、电磁继电器的工作原理和特性
电磁式继电器一般由铁芯、线圈、衔铁、触点簧片等组成的。只要在线圈两端加上一定的电压，线圈中就会流过一定的电流，从而产生电磁效应，衔铁就会在电磁力吸引的作用下克服返回弹簧的拉力吸向铁芯，从而带动衔铁的动触点与静触点(常开触点)吸合。当线圈断电后，电磁的吸力也随之消失，衔铁就会在弹簧的反作用力返回原来的位置，使动触点与原来的静触点(常闭触点)吸合。这样吸合、释放，从而达到了在电路中的导通、切断的目的。对于继电器的“常开、常闭”触点，可以这样来区分：继电器线圈未通电时处于断开状态的静触点，称为“常开触点”;处于接通状态的静触点称为“常闭触点”。 固态继电器的原理及结构 SSR按使用场合可以分成交流型和直流型两大类，它们分别在交流或直流电源上做负载的开关，不能混用。 下面以交流型的SSR为例来说明它的工作原理，图1是它的工作原理框图，图1中的部件①-④构成交流SSR的主体，从整体上看，SSR只有两个输入端(A和B)及两个输出端(C和D)，是一种四端器件。 图1 工作时只要在A、B上加上一定的控制信号，就可以控制C、D两端之间的“通”和“断”，实现“开关”的功能，其中耦合电路的功能是为A、B端输入的控
知己的近义词反义词及知己的造句 本文是关于知己的近义词反义词及知己的造句，感谢您的阅读！ 知己的近义词反义词及知己的造句知己 基本解释：顾名思义是了解、理解、赏识自己的人，如"知己知彼，百战不殆";更常指懂你自己的挚友或密友，它是一生难求的朋友，友情的最高境界。正所谓:"士为知己者死"。 1.谓了解、理解、赏识、懂自己。 2.彼此相知而情谊深切的人。 【知己近义词】 亲信，好友，密友，心腹，挚友，深交，相知，知交，知友，知心，知音，石友，老友，至友 【知己反义词】 仇人敌人陌路 【知己造句】 1、我们想要被人爱、想拥有知己、想历经欢乐、想要安全感。 2、朋友本应是我们的亲密知己和支持者，但对于大多数人来说，有一些朋友比起帮助我们，更多的却是阻碍。 3、那么，为什么你就认为，随着年龄的增长，比起女人来男人们的知己和丰富的人际关系更少，因此一般容易更孤独呢？ 4、他成了我的朋友、我的知己、我的顾问。 5、无论在我当州长还是总统的时候，布鲁斯都是我的密友、顾问和知己。他这样的朋友人人需要，也是所有总统必须拥有的。
6、波兰斯基有着一段声名卓著的电影生涯，也是几乎所有电影界重要人物们的挚友和同事，他们是知己，是亲密的伙伴。 7、搜索引擎变成了可以帮追我们的忏悔室，知己，信得过的朋友。 8、这样看来，奥巴马国家安全团队中最具影响力的当属盖茨了――但他却是共和党人，他不会就五角大楼以外问题发表看法或成为总统知己。 9、我们的关系在二十年前就已经和平的结束了，但在网上，我又一次成为了他精神层面上的评论家，拉拉队，以及红颜知己。 10、这位“知己”，作为拍摄者，站在距离电视屏幕几英尺的地方对比着自己年轻版的形象。 11、父亲与儿子相互被形容为对方的政治扩音筒、知己和后援。 12、这对夫妻几乎没有什么至交或知己依然在世，而他们在后纳粹时期的德国也不可能会说出实话的。 13、她把我当作知己，于是，我便将她和情人之间的争吵了解得一清二楚。 14、有一种友谊不低于爱情；关系不属于暖昧；倾诉一直推心置腹；结局总是难成眷属；这就是知己！ 15、把你的治疗师当做是可以分享一切心事的知己。 16、莉莉安对我敞开心胸，我成了她的知己。 17、据盖洛普民意调查显示，在那些自我认同的保守党人中，尽管布什仍维持72%支持率，但他在共和党领导层中似乎很少有几位知
成语大全解释及造句 本文是关于成语大全解释及造句，感谢您的阅读！ 首尾乖互：相互违违，先后自相矛盾。 你这人说话如许首尾乖互，叫我怎么信任你。 引颈受戮：戮：杀。伸长脖子等待被杀。指不作抵当而等死。 犯人知道自己罪责难逃，只有引颈受戮了。 衣不曳地：曳，拖动。时装不沾地，比喻非常繁忙。 这几天工作太多了，他都已经衣不曳地了。 水洁冰清：像冰水同样洁白清净。形容人品高洁或文笔雅致。 她是如许一个水洁冰清的人，怎么会和那一些坏人在一起。 如鲠在喉：鱼骨头卡在咽喉里。比喻生理有话没有说出来，非常难受。 我知道真象，但又不能说出来，真是如鲠在喉呀。 仰事俯畜：上要侍奉怙恃，下要养活妻儿。泛指维持一家生活。 父亲天天起早摊黑，仰事俯畜，非常辛苦。 为恶不悛：对峙作歹，不愿悔改。 这个报酬恶不悛，终究要受到法律的制裁。 无补于时：对事情没有什么益处。 此刻不努力学习，等未来悔怨了也无补于时了。 有脚书厨：戏称记闻精确、常识渊博的人。 他好学善思、常识博识，真是个有脚书厨呀 一字一珠：一个字就像一颗真珠。形容歌声婉转圆润。也比喻文
章优美、辞藻华美。 如许的文章真是一字一珠，看上几遍，还是回味无穷。 1、一拥而入：体育运动场的大门刚一打开，迷球的人们就一拥而入。 2。肝火冲冲：冲冲：感情冲动的样子。形容非常生气。《不知为何，他肝火冲冲地走进了教室。》 3。目不转睛：聚、会：堆积。形容注意力非常集中。《教室里同窗们都在目不转睛地听老师讲课。》 4。喃喃自语：自己和自己说话。《在路口经常可以看到一个老人，坐在那里喃喃自语。》 5。千钧一发：形容情况十分求助紧急。《就在要撞车的千钧一发的时候，司机紧迫刹住了汽车。》 6。精兵简政：简：使简化。《有些单位必需精兵简政，不断提高工作效率。》 7。五光十色：《一到夜晚，五光十色的灯把厦门装扮患上更加美丽。》 8。雨后春天的竹笋：形容新生物质大量涌现。《鼎新开放以来，工厂如雨后春天的竹笋般地不断涌现。》 9。满目琳琅：比喻面前出现了许多精美的物质。《那里展出的的工具满目琳琅，使我们的秋水应接没时间。》 10。顶天登时：形容形象非常高大，气概豪爽。《他至公无私，真是一个堂堂正正、顶天登时的男子汉。》
固态继电器的分类与工作原理 固态继电器(Solid State Relays,缩写SSR)是一种无触点电子开关，由分立元器件、膜固定电阻网络和芯片，采用混合工艺组装来实现控制回路(输入电路)与负载回路(输出电路)的电隔离及信号耦合，由固态器件实现负载的通断切换功能，内部无任何可动部件。尽管市场上的固态继电器型号规格繁多，但它们的工作原理基本上是相似的。主要由输入(控制)电路，驱动电路和输出(负载)电路三部分组成。 固态继电器的输入电路是为输入控制信号提供一个回路，使之成为固态继电器的触发信号源。固态继电器的输入电路多为直流输入，个别的为交流输入。直流输入电路又分为阻性输入和恒流输入。阻性输入电路的输入控制电流随输入电压呈线性的正向变化。恒流输入电路，在输入电压达到一定值时，电流不再随电压的升高而明显增大，这种继电器可适用于相当宽的输入电压范围。 固态继电器的驱动电路可以包括隔离耦合电路、功能电路和触发电路三部分。隔离耦合电路，目前多采用光电耦合器和高频变压器两种电路形式。常用的光电耦合器有光－三极管、光－双向可控硅、光－二极管阵列(光－伏)等。高频变压器耦合，是在一定的输入电压下，形成约10MHz的自激振荡，通过变压器磁芯将高频信号传递到变压器次级。功能电路可包括检波整流、过零、加速、保护、显示等各种功能电路。触发电路的作用是给输出器件提供触发信号。 固态继电器的输出电路是在触发信号的控制下，实现固态继电器的通断切换。输出电路主要由输出器件(芯片)和起瞬态抑制作用的吸收回路组成，有时还包括反馈电路。目前，各种固态继电器使用的输出器件主要有晶体三极管(Transistor)、单向可控硅(Thyristor或SCR)、双向可控硅(Triac)、MOS场效应管(MOSFET)、绝缘栅型双极晶体管(IGBT)等。 固态继电器原理固态继电器(Solidstate Relay, SSR)是一种由固态电子组件组成的新型无触点开关，利用电子组件（如开关三极管、双向可控硅等半导体组件）的开关特性，达到无触点、无火花、而能接通和断开电路的目的，因此又被称为“无触点开关”。相对于以往的“线圈—簧片触点式”继电器
成语解释加造句 【篇一：成语解释加造句】 82 、历历在目：指远方的景物看得清清楚楚,或过去的事情清清楚楚地重现在眼前. 例如：上海世博会虽然已经过去两三个月了,但参观世博会的情景仍然历历在目. 83 、力挽狂澜：比喻尽力挽回危险的局势. 在这次比赛中,我们队暂时落后,他力挽狂澜,终于战胜了所有对手,使我们队获得了冠军. 84 、理直气壮：理由充分,说话气势就壮. 例如：这件事上你没有错,你可以理直气壮地找小明理论理论. 85 、两全其美：指做一件事顾全到双方,使两方面都得到好处. 例如：我们一起把英语课文演一遍吧,这样我们既可以练英语,又可以轻松轻松,这不是两全其美吗? 86 、流离失所：流离：转徒离散.无处安身,到处流浪. 例如：在世界上许多战乱地区,人民流离失所. 87 、流连忘返：玩乐时留恋不愿离开.留恋得忘记了回去. 例如：桂林山水如此秀美,真令人流连忘返. 88 、络绎不绝：形容行人车马来来往往,接连不断. 例如：这个画展非常好看,参观的人络绎不绝. 89 、买椟还珠：椟：木匣；珠：珍珠.买下木匣,退还了珍珠.比喻没有眼力,取舍不当. 例如：如果我是你,我就不会买这些华而不实的东西,宁愿要几本书,因为我不喜欢买椟还珠. 90 、漫不经心：漫：随便.随随便便,不放在心上. 例如：做事可不能漫不经心,要认认真真,只有这样才能把事情做好.
91 、满载而归：装得满满地回来.形容收获很大. 例如：爷爷奶奶逛玩早市,满载而归,买了很多菜才回来. 92 、 茅塞顿开： 顿： 立刻； 茅塞： 喻人思路闭塞或不懂事. 比喻思想忽然开窍, 立刻明白了某个道理. 例如：老师一讲这个道理,我好像茅塞顿开,忽然明白了很多事情. 93 、诚心诚意：诚：真实的心意.真心诚意.形容十分真挚诚恳. 造句——在了解实情之后,她懊悔万分,诚心诚意地向孩子道歉. 94 、触景生情：受到眼前景物的触动,引起联想,产生某种感情.触：触动.造句——傍晚,看到天边的火烧云,使我触景生情,想起了许多往事! 95 、触类旁通：触类：接触某一方面的事物；旁通：相互贯通.掌握了某一事物的知识或规律,进而推 知同类事物的知识或规律. 造句——这让我掌握了一些生活的方法,能触类旁通地思索问题. 96 、唇亡齿寒：嘴唇没有了,牙齿就会感到寒冷.比喻关系密切,利害相关.造句——这两家公司有着多种业务关系,正所谓是唇亡齿寒. 97 、春华秋实：春天开花,秋天结果（多用于比喻） 造句——春华秋实,没有那浩荡的春风,又哪里会有这满野秋色和大好的收成呢? 98 、当之无愧：当：承当.无愧：毫无愧色.当得起某种称号或荣誉,无须感到惭愧. 造句——他搞了几项技术革新,被誉为革新大师,真是当之无愧! 99
继电器的作用及分类 继电器是一种电控制器件。它具有控制系统（又称输入回路）和被控 制系统（又称输出回路）之间的互动关系。通常应用于自动化的控制 电路中，它实际上是用小电流去控制大电流运作的一种“自动开关”。故在电路中起着自动调节、安全保护、转换电路等作用。 器件简介 当输入量（如电压、电流、温度等）达到规定值时，继电器被所 控制的输出电路导通或断开。 输入量可分为电气量（如电流、电压、频率、功率等）及非电气 量（如温度、压力、速度等）两大类。 继电器具有动作快、工作稳定、使用寿命长、体积小等优点。广 泛应用于电力保护、自动化、运动、遥控、测量和通信等装置中。 工作原理和特性 电磁继电器 电磁继电器一般由铁芯、线圈、衔铁、触点簧片等组成的。只要 在线圈两端加上一定的电压，线圈中就会流过一定的电流，从而产生电磁效应，衔铁就会在电磁力吸引的作用下克服返回弹簧的拉力吸向 铁芯，从而带动衔铁的动触点与静触点（常开触点）吸合。当线圈断
电后，电磁的吸力也随之消失，衔铁就会在弹簧的反作用力返回原来 的位置，使动触点与原来的静触点（常闭触点）释放。这样吸合、释放，从而达到了在电路中的导通、切断的目的。对于继电器的“常开、常闭”触点，可以这样来区分：继电器线圈未通电时处于断开状态的 静触点，称为“常开触点”；处于接通状态的静触点称为“常闭触点”。继电器一般有两股电路，为低压控制电路和高压工作电路。 固态继电器（SSR） 固态继电器是一种两个接线端为输入端，另两个接线端为输出端的四端器件，中间采用隔离器件实现输入输出的电隔离。 固态继电器按负载电源类型可分为交流型和直流型。按开关型式可分为常开型和常闭型。按隔离型式可分为混合型、变压器隔离型和光电隔离型，以光电隔离型为最多。 热敏干簧继电器 热敏干簧继电器是一种利用热敏磁性材料检测和控制温度的新 型热敏开关。它由感温磁环、恒磁环、干簧管、导热安装片、塑料衬 底及其他一些附件组成。热敏干簧继电器不用线圈励磁，而由恒磁环产生的磁力驱动开关动作。恒磁环能否向干簧管提供磁力是由感温磁 环的温控特性决定的。 磁簧继电器
仿照的近义词反义词和造句 仿照的近义词 【仿制解释】：仿造：～品 【模仿解释】：个体自觉或不自觉地重复他人的行为的过程。是社会学习的重要形式之一。尤其在儿童方面，儿童的动作、语言、技能以及行为习惯、品质等的形成和发展都离不开模仿。可分为无意识模仿和有意识模仿、外部模仿和内部模仿等多种类型。 仿照的反义词 【独创解释】：独特的创造：～精神ㄧ～一格。 仿照造句 一、老师让我们仿照黑板上的图画一幅画。 二、仿照下面的句式，以“只有”开头，写一结构与之相似的复句。 三、仿照例句的句子，在下面两句的横线上补写相应的内容。 四、仿照例句，以“记忆”或“友情”开头，另写一句话。 五、仿照下面两个例句，用恰当的词语完成句子，要求前后语意关联。 六、仿照开头两句句式，通过联想，在后面两句横线上填上相应的词语。 七、仿照所给例句，用下面的词展开联想，给它一个精彩的解释。 八、仿照例句，以“你”开头，另写一个句子。 九、仿照下列句式，续写两个句子，使之与前文组成意义相关的.句子。 十、我们也仿照八股文章的笔法来一个“八股”,以毒攻毒,就叫做八大罪状吧。
十一、仿照例句，任选一种事物，写一个句子。 十二、仿照下面一句话的句式和修辞，以“时间”开头，接着写一个句子。 十三、仿照例句，以“热爱”开头，另写一句子。 十四、仿照下面的比喻形式，另写一组句子。要求选择新的本体和喻体，意思完整。 十五、根据语镜，仿照划线句子，接写两句，构成语意连贯的一段话。 十六、仿照下面句式，续写两个句式相同的比喻句。 十七、自选话题，仿照下面句子的形式和修辞，写一组排比句。 十八、仿照下面一句话的句式，仍以“人生”开头，接着写一句话。 十九、仿照例句的格式和修辞特点续写两个句子，使之与例句构成一组排比句。 二十、仿照例句，另写一个句子，要求能恰当地表达自己的愿望。 二十一、仿照下面一句话的句式，接着写一句话，使之与前面的内容、句式相对应，修辞方法相同。 二十二、仿照下面一句话的句式和修辞，以“思考”开头，接着写一个句子。 二十三、仿照下面例句，从ABCD四个英文字母中选取一个，以”青春”为话题，展开想象和联想，写一段运用了比喻修辞格、意蕴丰富的话，要求不少于30字。 二十四、仿照下面例句，另写一个句子。 二十五、仿照例句，另写一个句子。 二十六、下面是毕业前夕的班会上，数学老师为同学们写的一句赠言，请你仿照它的特点，以语文老师的身份为同学们也写一句。