二氧化钛镀膜玻璃表面防水
作者：叶超刘煜钱骅
来源：《科学与财富》2010年第02期
[摘要] 防水玻璃现实意义大,未来用途广泛,而二氧化钛越来越广泛地应用于不同类型的产业。将二氧化钛制成薄膜涂于玻璃表面,防水效果明显改善,吸水增加,但分布的水分子分布均匀,具有良好的防水效果。但实验只有在紫外光下,才能达到预期的效果。
[关键词] 二氧化钛玻璃防水提拉法
Titanium-plated Glass Surface Of The Waterproof Membrane
Liuyu Yechao Qianhua
(Central South University School of Civil Engineering Changsha 410075)
Abstract:The future using of a wide range of titanium dioxide and increasingly widely used in different types of industries.Will be made of titanium dioxide thin film applied to glass surfaces,the effect of improved water-proof,water-absorbent, but the distribution of distribution of water molecules, has a good waterproof effect.But the experiment is only visible under ultraviolet light in order to achieve the desired results.
Keywords:titanium dioxide,glass, waterproof hydrophilic,Czochralski method
一、实验设计
1.制作样品玻璃表面;
将75mL乙醇(分析醇)与1.5mL二次蒸馏水在搅拌下滴加硝酸(分析醇)调节PH=3~4,然后
将15mL钛酸正丁脂(分析醇)与25mL乙醇混合均匀后在强烈搅拌下滴加到前述溶液中,约1h滴完,继续搅拌20min,得透明溶胶。
采用浸渍提拉法,将5cm*5cm的玻璃片(无须清洗)以5cm/min的速度垂直提拉出液面。在
室温下无尘放置12h后,放入马福炉升温到600度灼烧60min,冷却后取出样品进行后续实验。
2.玻璃分组,将玻璃分为普通玻璃和镀有二氧化钛膜的样品玻璃,编号“一组”、“二组”,每组
有三块玻璃,编号为一组1、2、3和二组1、2、3。